The Effect of Extrusion Processing Conditions and Polyisobutylene Concentration on the Properties of Polyethylene for Stretch and Cling Film Applications
Restricted accessResearch articleFirst published online October, 2002
The Effect of Extrusion Processing Conditions and Polyisobutylene Concentration on the Properties of Polyethylene for Stretch and Cling Film Applications
A range of LLDPE films with polyisobutylene (PIB) content from 2-8% was manufactured using a Killion blown film extrusion system and a cast film extrusion system. The films were aged at 25, 35 and 45 C for up to 28 days, to enable tack (cling) development. The results show that tack, in both blown and cast films, improved significantly with ageing at increased storage temperatures and at higher film blow up ratios. DSC analysis showed only a slight decrease in film crystallinity with increasing PIB concentration. The film tensile modulus, elongation and tear properties in both MD and TD were not significantly affected by an increase in PIB concentration.
1. Billham, M., Clarke, A.H., Garrett, G. and Murphy, W.R. (2001). Comparison of the Mechanical Performance of Extruded Blown and Cast Polyolefin Thin Film, In: 2001 ANTEC Proceedings, pp. 96-100.
2.
2. DeGroot, J.A., Doughty, A.T., Stewart, K.B. and Patel, R.M. (1994). Effect of Cast Film Fabrication Variables on Structure Development and Key Stretch Film Properties, Journal of Applied Polymer Science, 52: 365-376.
3.
3. Began, C.M., McNally, G.M. and Murphy, W.R. (1999). The Blending and Coextrusion of Metallocene Catalyzed Polyethylene in Blown Film Applications, In: 1999 ANTEC Proceedings, pp. 90-94.
4.
4. Sakhalkar, S.S. and Hirt, D.E. (1998). Surface Segregation of Erucamide in LLDPE Films: Thermodynamic Analysis and Experimental Verification, In: 1998 ANTEC Proceedings, pp. 2826-2831.
5.
5. Walters, K.B. and Hirt, D.E. (2001). Migration of Fluorinated Additives to HDPE Film Surfaces, In: 2001 ANTEC Proceedings, pp. 2644-2688.
6.
6. Lee, H. and Archer, L.A. (2001). Surface Modification of Polymer Via Surface-induced Migration of Copolymer Additives, In: 2001 ANTEC Proceedings, pp. 1472-1476.
7.
7. Novák, I. and Florián, S. (1997). Self-adhesive Stretching Polyethylene Foil, Materials Letters, 32: 235-239.
8.
8. Field, G.J., Micic, P. and Bhattacharya, S.N. (1999). Melt Strength and Film Bubble Instability of LLDPE/LDPE Blends, Polymer Int., 48: 461-466.
9.
9. Micic, P. and Bhattacharya, S.N. (2000). Rheology of LLDPE, LDPE and LLDPE/LDPE Blends and Its Relevance to the Film Blowing Process, Polymer Int., 49: 1580-1589.
10.
10. Michaels, A.S. and Bixler, H.J. (1961). Solubility of Gases in Polyethylene, Journal of Polymer Science, 50: 393-412.
11.
11. Michaels, A.S. and Parker, R.B. (1959). Journal of Polymer Science, 41: 33.
12.
12. Myers, A.W., Rogers, C.E., Stannett, V. and Szware, M. (1958). Tappi Journal, 41: 716.
13.
13. Drummond, K.M., Hopewell, J.L. and Shanks, R.A. (2000). Crystallization of Low-density Polyethylene and Linear Low-density Polyethylene-Rich Blends, Journal of Applied Polymer Science, 78: 1009-1016.
14.
14. Krishnaswamy, R.K. and Sukhadia, A.M. (2000). Orientation Characteristics of LLDPE Blown Films and Their Implications on Elmendorf Tear Performance, Polymer Journal, 41: 9205-9217.