Understanding Why Adhesion in Extrusion Coating Decreases With Diminishing Coating Thickness

Abstract

It is well known that in extrusion coating, the coating adhesion to the substrate decreases with decreasing thickness. The study on this phenomenon is divided into three parts. Part I explores the reduction in adhesion of LDPE to paper and other porous substrates. Several hypotheses are proposed for the origin of this decrease, including a reduction in oxidation time, faster cooling in the air gap, and more rapid quenching in the nip. A model of the molten polymer penetration into the substrate shows that the greatest effect is cooling in the nip; thinner coatings have less time to flow into the substrate interstices once the chill roll contact is made. The model results agree well with experimental adhesion data from the literature.

In Part II, adhesion to aluminum foil and other nonporous substrates is studied. Several hypotheses are proposed for why peel strength decreases in these structures, including a reduction in the air gap time, faster air gap cooling, more rapid nip quenching, and stress imposed during drawing. Modeling and experimental results show that cooling in the nip and imposed stress have the greatest impact.

In Part III, the peel test is analyzed to understand why the peel strength of better adhering adhesives are more sensitive to changes in coating thickness. The analysis shows that changes in the critical dimension of the deformation region at the peel front may be responsible.

Keywords

adhesion paperboard extrusion coating coating weight peel strength foil fracture mechanics.

Get full access to this article

View all access options for this article.

References

Goslin, J.P. and Sweeney, H.F. (1960). The Interaction of Processing Variables, Base Materials and Resins in Polyethylene Extrusion Coating, TAPPI Journal, 43(5): 434-447.

Guillotte, J.E. and McLaughlin Jr, T.F. (1962). Calculating the Adhesion of Polyethylene Coatings to Kraft Paper, TAPPI Journal, 45(3): 200-208.

Antonov, V. and Soutar, A. (1991). Foil Adhesion With Copolymers: Time in the Air Gap, TAPPI 1991 Polymers, Laminations & Coatings Conference Proceedings, TAPPI Press, Atlanta, 553.

Morris, B.A. and Suzuki, N. (2001). The Case against Oxidation as the Primary Factor for Bonding Acid Copolymers to Foil, Annual Technical Conference - Society of Plastics Engineers, 59(1): 25-35.

Morris, B.A. and Thai, H.T. (2004). Improving the Adhesion of LDPE to Aluminum Foil Through Blending, Annual Technical Conference - Society of Plastics Engineers, 62: 1101-1105.

Van Ness, R.T. (1968). Infrared Thermometry - A Useful Tool for the Coating Industry, TAPPI Journal, 51(12): 39A-46A.

Vlachopoulos, J. (1994). Melt Flow through Channels, In: Introduction to Polymer Processing, Chapter 2, 2nd edn, McMaster University, April.

Trouilhet, Y. and Morris, B.A. (1999). Prediction of Temperature Profiles Across Coating and Substrate in the Nip, TAPPI 1999 Polymers, Laminations and Coatings Conference, pp. 457-468.

Morris, B.A. (1998). The Influence of Stress on Peel Strength of Acid Copolymers to Foil, TAPPI 1998 Polymers, Laminations & Coatings Conference Proceedings, TAPPI Press, Atlanta, 1085-1094.

10.

Canning, K. , Bian, B. and Co, A. (1999). Film Casting of a Low Density Polyethylene Melt, Proceedings ANTEC 1999, Annual Technical Conference - Society of Plastics Engineers, 57: 386-390.

11.

Baird, D.G. and Collias, D.I. (1995). Postdie Processing, In: Polymer Processing, Principles and Design, Chapter 9, Butterworth-Heinemann , Boston, MA.

12.

Pearson, J.R.A. (1985). Film Stretching and Casting , In: Mechanics of Polymer Processing, Chapter 16, Elsevier Applied Science Publishers, London.

13.

Iyengar, V.R. and Co, A. (1993). Film Casting of a Modified Gieskus Fluid: A Steady State Analysis, J. Non-Newtonian Fluid Mech., 48(1): 1-20.

14.

Wu, S. (1982). Fracture of Adhesive Bond, Polymer Interface and Adhesion, Chapter 14, Marcel Dekker, Inc., New York.

15.

Kinloch, A.J. , Lau, C.C. and Williams, J.G. (1994). The Peeling of Flexible Laminates, International Journal of Fracture, 66(1): 45-70.

16.

Gent, A.N. and Hamed, G.R. (1977). Peel Mechanics for an Elastic-plastic Adherend , J. Applied Polymer Sci., 21(10): 2817-2831.

17.

Pascal, J. (2006). Ultraversatile Adhesives to Broaden the Possibilities of Extrusion Lamination, Proceedings 2006 TAPPI PLACE Conference, Cincinnati, OH.

18.

Kinloch, A.J. and Young, R.J. (1985). Fracture Behavior of Polymers, Elsevier Applied Science Publishers, London.