Properties of co-extruded nanoclay-filled aliphatic nylon (PA6)/linear low-density polyethylene and aromatic nylon (MXD6)/ linear low-density polyethylene multilayer films
Restricted accessResearch articleFirst published online January, 2015
Properties of co-extruded nanoclay-filled aliphatic nylon (PA6)/linear low-density polyethylene and aromatic nylon (MXD6)/ linear low-density polyethylene multilayer films
In this study, coextruded multilayer films with aliphatic (polyamide 6) and aromatic (poly (m-xylene adipamide)) nylons as well as their in-situ polymerized nanocomposites with 4 wt% nanoclay, as an oxygen barrier layer (core), and a linear low-density polyethylene, as a moisture barrier layer (skin), were produced and characterized. Five-layer films were prepared by cast coextrusion and rapidly cooled using an air knife. Dynamic rheological measurements showed that the selected materials can be coextruded with a minimum interfacial instability between the melt flows in the feed block. Type of crystals, crystallinity and thermal transitions of layers were investigated using differential scanning calorimetry and modulated differential scanning calorimetry. The mechanical, optical, oxygen and water vapor barrier properties of the coextruded multilayer films were measured and discussed. Although the crystallinity of the poly (m-xylene adipamide) layer in the multilayer films was lower compared to the polyamide 6 layer, the impermeability to oxygen and water vapor was much better for the former multilayer films. In addition, substituting the neat polyamide 6 and poly (m-xylene adipamide) by their nanocomposites improved the oxygen barrier of the multilayer films by more than 50%. The series resistance model was not able to predict the barrier properties of the multilayer films due to the difference in polymer behavior for the single layer and multilayer, and boundary adjacent layer effects. The coextruded polyamide linear low-density polyethylene multilayer films showed higher toughness, tear and flex crack resistance compared to the poly (m-xylene adipamide)/linear low-density polyethylene samples. The pristine poly (m-xylene adipamide)-based multilayer film showed a lower haze compared to the polyamide 6 films due to very little crystallinity in the former.
WagnerJR. Hand Book of Multilayer flexible packaging technology and applications for food, personal care and over-the counter pharmaceutical industries, Burlington, USA: Elsevier Inc, 2010.
2.
GanpuleHKKhomamiB. An investigation of interfacial instabilities in the superposed channel flow of viscoelastic fluids. J Non-Newtonian Fluid Mech1999; 81: 27–69.
3.
DooleyJHyunKSHughesK. An experimental study on the effect of polymer viscoelasticity on layer rearrangement in coextruded structures. Polym Eng Sci1998; 38: 1060–1071.
4.
KojimaYUsukiAKawasumiM. Mechanical properties of nylon 6-clay hybrid. J Mater Res1993; 8: 1185–1189.
5.
UsukiAKojimaYKawasumiM. Synthesis of nylon 6-clay hybrid. J Mater Res1993; 8: 1179–1184.
6.
OshinskiAJKeskkulaHPaulDR. Rubber toughening of polyamides with functionalized block copolymers: 1. Nylon-6. Polymer1992; 33: 268–283.
7.
KojimaYUsukiAKawasumiM. Synthesis of nylon 6-clay hybrid by montmorillonite intercalated with -caprolactam. J Polym Sci A Polym Chem1993; 31: 983–986.
ChoJWPaulDR. Nylon 6 nanocomposites by melt compounding. Polymer2001; 42: 1083–1094.
10.
DennisHRHunterDLChangD. Effect of melt processing conditions on the extent of exfoliation in organoclay-based nanocomposites. Polymer2001; 42: 9513–9522.
11.
PoissonCGuerengombaJLacrampeM-F. Mechanical, optical and barrier properties of PA6/nanoclay-based single- and multilayer blown films. Polym Polym Compos2008; 16: 349–358.
12.
HuYSMehtaSSchiraldiDA. Effect of water sorption on oxygen-barrier properties of aromatic polyamides. J Polym Sci Pol Phys2005; 43: 1365–1381.
13.
GavaraRHernandezRJ. The effect of water on the transport of oxygen through nylon6-films. J Polym Sci B Polym Phys1994; 32: 2375–2382.
14.
HuangCHWuJSHuangCC. Predicting the permeability and tensile behavior of high density polyethylene/tie/polyamide 6 three-layer films. Polym Int2004; 53: 2099–2106.
15.
SadeghiFAjjiA. Structure, mechanical and barrier properties of uniaxially stretched multilayer nylon/clay nanocomposite films. Int Polym Proc2012; 27: 565–573.
16.
Fereydoon M, Tabatabaei SH and Ajji A. Rheological, crystal structure, barrier, and mechanical properties of PA6 and MXD6 nanocomposite films. Polym Eng Sci 2013. Epub ahead of print 2013. DOI:10.1002/pen.23813.
17.
LagaronJMGimenezEGavaraR. Study of the influence of water sorption in pure components and binary blends of high barrier ethylene-vinyl alcohol copolymer and amorphous polyamide and nylon-containing ionomer. Polymer2001; 42: 9531–9540.
18.
AmmalaAPasSJLawrenceKA. Poly(m-xylene adipamide)-montmorillonite nanocomposites: Effect of organo-modifier structure on free volume and oxygen barrier properties. J Mater Chem2008; 18: 911–916.
Tomomichi KandaMoriA. Gas-barrier multi-layer structure Kanagawa, Japan: Mitsubishi Gas Chemical Company Inc., Tokyo (JP), 2007.
21.
Mueller C, Roger Kaas, Bertrand Fillon, et al. Thermoplastics film structures having improved barrier and mechanical properties. Patent 20020150729 A1, USA, 2002.
22.
ShibayamaMUenoyamaKOuraJI. Miscibility and crystalinity control of nylon-6 and poly(m-Xylene adipamide) blends. Polymer1995; 36: 4811–4816.
23.
TakedaYKeskkulaHPaulDR. Toughening of phase-homogenized mixtures of nylon-6 and poly(m-xylene adipamide) with a functionalized block copolymer. Polymer1992; 33: 3394–3407.
24.
TakedaYPaulDR. Phase homogenization of mixtures of poly(m-xylene adipamide) and nylon 6 by interchange reactions. Polymer1991; 32: 2771–2778.
25.
TakedaYPaulDR. The effect of physical interactions on melt-phase homogenized of mixtures of poly(M-Xylene Adipamide) with aliphatic polamides induced by interchange reactions. Polymer1992; 33: 3899–3907.
26.
TakedaYKeskkulaHPaulDR. Toughening of phase-homogenized mixtures of nylon-6 and poly (meta-xylene adipamide) with a functionalized block copolymer. Polymer1992; 33: 3394–3407.
27.
TakashigeMKanaiTYamadaT. Easy tear film of biaxially oriented PA 6/MXD 6 blend by double bubble tubular film process. Int Polym Proc2004; 19: 147–154.
28.
TakashigeMKanaiT. Easy tear multilayer film of biaxially oriented PA6/MXD6 by double bubble tubular film process. Int Polym Proc2005; 20: 100–104.
29.
DooleyJTungH. Coextrusion, encyclopedia of polymer science and technology, New York: John Wiley & Sons, Inc, 2002.
30.
DooleyJ. Viscoelastic flow effects in multilayer polymer coextrusion, Eindhoven, the Netherlands: Technische Universiteit Eindhoven, 2002.
HanCD. A study of bicomponent coextrusion of molten polymers. J Appl Polym Sci1973; 17: 1289–1303.
35.
HanCDShettyR. Studies on multilayer film coextrusion II. Interfacial instability in flat film coextrusion. Polym Eng Sci1978; 18: 180–186.
36.
Lamnawar K, Zhang H and Maazouz A. Coextrusion of Multilayer Structures, Interfacial Phenomena. Encyclopedia of Polymer Science and Technology. John Wiley & Sons, Inc, 2013. DOI: 10.1002/0471440264.pst584.
37.
LamnawarKMaazouzA. Role of the interphase in the flow stability of reactive coextruded multilayer polymers. Polym Eng Sci2009; 49: 727–739.
38.
SchrenkWJBradleyNLAlfreyT. Interfacial flow instability in multilayer coextrusion. Polym Eng Sci1978; 18: 620–623.
39.
DooleyJHyunKSHughesK. An experimental study on the effect of polymer viscoelasticity on layer rearrangement in coextruded structures. Polym Eng Sci1998; 38: 1060–1071.
40.
HengFMitsoulisE. Numerical simulation of wire-coating coextrusion. Int Polym Process1989; 4: 44–56.
41.
AyyerRKLeonovAI. Comparative rheological studies of polyamide-6 and its low loaded nanocomposite based on layered silicates. Rheol Acta2004; 43: 283–292.
42.
DoudouBDargentEGrenetJ. Crystallization and melting behaviour of poly(m-xylene adipamide). J Therm Anal Calorim2006; 85: 409–415.
43.
PicardEVermogenAGérardJF. Barrier properties of nylon 6-montmorillonite nanocomposite membranes prepared by melt blending: Influence of the clay content and dispersion state: Consequences on modelling. J Membr Sci2007; 292: 133–144.
44.
HongHZhangZChungTCM. Synthesis of new 1-decene-based LLDPE resins and comparison with the corresponding 1-octene- and 1-hexene-based LLDPE resins. J Polym Sci A Polym Chem2007; 45: 639–649.
45.
DooleyJRudolphL. Viscous and elastic effects in polymer coextrusion. J Plast Film Sheet2003; 19: 111–122.
46.
LamnawarKBousminaMMaazouzA. 2D Encapsulation in multiphase polymers: Role of viscoelastic, geometrical and interfacial properties. Macromolecules2011; 45: 441–454.
47.
WaliaPSGuptaRKKiangCT. Influence of interchange reactions on the crystallization and melting behavior of nylon 6,6 blended with other nylons. Polym Eng Sci1999; 39: 2431–2444.
LeeKMHanCD. Rheology of organoclay nanocomposites: effects of polymer matrix/organoclay compatibility and the gallery distance of organoclay. Macromolecules2003; 36: 7165–7178.
50.
LertwimolnunWVergnesB. Influence of compatibilizer and processing conditions on the dispersion of nanoclay in a polypropylene matrix. Polymer2005; 46: 3462–3471.
51.
KhomamiBRanjbaranMM. Experimental studies of interfacial instabilities in multilayer pressure-driven flow of polymeric melts. Rheol Acta1997; 36: 345–366.
52.
WilsonGMKhomamiB. An experimental investigation of interfacial instabilities in multilayer flow of viscoelastic fluids. Part II. Elastic and nonlinear effects in incompatible polymer systems. J Rheol1993; 37: 315–339.
53.
MaitiPOkamotoM. Crystallization controlled by silicate surfaces in nylon 6-clay nanocomposites. Macromol Mater Eng2003; 288: 440–445.
54.
MiriVElkounSPeurtonF. Crystallization kinetics and crystal structure of nylon6-clay nanocomposites: Combined effects of thermomechanical history, clay content, and cooling conditions. Macromolecules2008; 41: 9234–9244.
55.
FornesTDYoonPJKeskkulaH. Nylon 6 nanocomposites: The effect of matrix molecular weight. Polymer2001; 42: 09929–09940.
56.
BafnaABeaucageGMirabellaF. 3D Hierarchical orientation in polymer–clay nanocomposite films. Polymer2003; 44: 1103–1115.
57.
UsukiAHasegawaNKadouraH. Three-dimensional observation of structure and morphology in nylon-6/clay nanocomposite. Nano Lett2001; 1: 271–272.
58.
YalcinBErgungorZKonishiY. Molecular origins of toughening mechanism in uniaxially stretched nylon 6 films with clay nanoparticles. Polymer2008; 49: 1635–1650.
59.
FornesTDPaulDR. Crystallization behavior of nylon 6 nanocomposites. Polymer2003; 44: 3945–3961.
60.
SeifSCakmakM. Stress - optical behavior of poly(m-xylylenediamine adipamide) (nylon MXD6): Influence of molecular weight. Polymer2010; 51: 3762–3773.
61.
Sallem-IdrissiNMiriVElkounS. Trichroic infrared analysis of the strain-induced structural changes in the PA6 layer of PA6/PE multilayer films under biaxial drawing. Polymer2009; 50: 5812–5823.
62.
YalcinBCakmakM. Superstructural hierarchy developed in coupled high shear/high thermal gradient conditions of injection molding in nylon 6 nanocomposites. Polymer2004; 45: 2691–2710.
63.
WilfongDLKnightGW. Crystallization mechanisms for LLDPE and its fractions. J Polym Sci Pol Phys1990; 28: 861–870.
MaCCMKuoCTKuanHC. Effects of swelling agents on the crystallization behavior and mechanical properties of polyamide 6/clay nanocomposites. J Appl Polym Sci2003; 88: 1686–1693.
66.
HommingaDSGoderisBMathotVBF. Crystallization behavior of polymer/montmorillonite nanocomposites. Part III. Polyamide-6/montmorillonite nanocomposites, influence of matrix molecular weight, and of montmorillonite type and concentration. Polymer2006; 47: 1630–1639.
67.
LiuXWuQ. Phase transition in nylon 6/clay nanocomposites on annealing. Polymer2002; 43: 1933–1936.
68.
WatanabeSSanoNNodaI. Surface Melting and Lamella Rearrangement Process in Linear Low Density Polyethylene. J Phys Chem B2009; 113: 3385–3394.
69.
JonesKJKinshottIReadingM. The origin and interpretation of the signals of MTDSC. Thermochim Acta1997; 304–305: 187–199.
70.
ShishanWDingjunJXiaodongO. The structure and properties of PA6/MMT nanocomposites prepared by melt compounding. Polym Eng Sci2004; 44: 2070–2074.
TabatabaeiSHCarreauPJAjjiA. Microporous membranes obtained from PP/HDPE multilayer films by stretching. J Membr Sci2009; 345: 148–159.
73.
Krizan TD, Coburn JC and Blatz PS. Structure of amorphous polyamides. In: Koros WJ (ed.). Barrier polymers and structures. Washington, DC: American Chemical Society, 1990, pp.111–125.
ThellenCSchirmerSRattoJA. Co-extrusion of multilayer poly(m-xylylene adipimide) nanocomposite films for high oxygen barrier packaging applications. J Membr Sci2009; 340: 45–51.
76.
TabatabaeiSHCarreauPJAjjiA. Effect of processing on the crystalline orientation, morphology, and mechanical properties of polypropylene cast films and microporous membrane formation. Polymer2009; 50: 4228–4240.
77.
GhasemiHCarreauPJKamalMR. Properties of PET/clay nanocomposite films. Polym Eng Sci2012; 52: 420–430.
78.
LinYHiltnerABaerE. Nanolayer enhancement of biaxially oriented polypropylene film for increased gas barrier. Polymer2010; 51: 5807–5814.
79.
ShahRKKrishnaswamyRKTakahashiS. Blown films of nanocomposites prepared from low density polyethylene and a sodium ionomer of poly(ethylene-co-methacrylic acid). Polymer2006; 47: 6187–2201.
80.
Fereydoon M, Tabatabaei SH and Ajji A. X-ray and trichroic infrared orientation analyses of uniaxially stretched PA6 and MXD6 nanoclay composite films. Macromolecules 2014; 47: 2384–2395.
81.
CotterellBChiaJYHHbaiebK. Fracture mechanisms and fracture toughness in semicrystalline polymer nanocomposites. Eng Fract Mech2007; 74: 1054–1078.
82.
HuYSPrattipatiVHiltnerA. Improving transparency of stretched PET/MXD6 blends by modifying PET with isophthalate. Polymer2005; 46: 5202–5210.