Corrosion Testing of some Austenitic Stainless Steels and of Inconel Alloy at 25°c in Acidic Chloride Solutions

The corrosion of austenitic stainless steels types AISI 304, 310 and 316, and of Inconel alloy, was studied at 25°c, in 5% NaCl solution at an initial pH value of 2·5, and in 5% FeCl³ at pH 1·2. The resistance of the alloys in both corrosive environments was in the order: 310 > 316 > 304 > Inconel. Pre-treatment of the specimens with bubbling chlorine gas increased the subsequent corrosion rates of the alloys. Intermittent bubbling of gas mixtures such as Cl₂, N₂, and/or H₂S, increased the corrosion rate of Inconel alloy when Cl₂ was present, but decreased the corrosion rate when H₂ was present. Heat treatment of austenitic stainless steels increased the subsequent corrosion rates, whereas 16% pre-straining of annealed specimens slightly reduced the rates. Addition of trisodium phosphate to the corrosive solution reduced the corrosion rates and pitting tendency for all three types of austenitic stainless steel.