Control of corrosion in oil and gas production tubing

Abstract

Controlling corrosion in production tubing is essential for maintaining production and for preventing loss of well control. Materials for use downhole have to meet criteria for corrosion resistance and also mechanical requirements. The potential corrosion rate can be estimated and the risks of sulphide stress corrosion cracking assessed on the basis of the anticipated environmental conditions and flow regime. Material options for tubing can then be considered on the basis of published corrosion test data and also field experience. Candidate materials may be tested under the precise field conditions expected in order to ensure that overconservative choices are not made. Corrosion inhibitors, coated carbon steel, and fibre reinforced plastic tubing have temperature, flow regime, and mechanical limitations. Specific corrosion resistant alloys (CRAs) have environmental limitations with respect to temperature, hydrogen sulphide, and chloride content. Details of field experience with all of these material options are given. There exists a large amount of experience with CRAs for downhole applications. Correctly selected CRAs have a good track record of service, even for hostile, H₂ S containing conditions. There are a few limited examples of CRA clad tubing. This product may be one that needs re-evaluation as it offers potential for economic use of costly but effective CRAs.

Get full access to this article

View all access options for this article.

References

Kermani

M. B.

and SMITH

L. M.

(eds.): ‘CO2 corrosion control in oil and gas production — design considerations’, EFC Publication No. 23; 1997, London, The Institute of Materials.

Kermani

M. B.

et al.: Proc. Conf. Corrosion ‘91, Cincinnati, OH, USA, March 1991, NACE, Paper 21.

‘Guidelines on materials requirements for carbon and low alloy steels for H2 S-containing environments in oil and gas production’, EFC PublicationNo. 16; 1995, London, The Institute of Materials.

Bonis

and CROLET

J.-L.

: Corros. Sci., 1987, 27, 1059–1070.

Houghton

C. J.

and WESTERMARK

R. V.

: J. Pet. Technol., Jan. 1983, 239.

Huntoon

G. G.

and ALKIRE

J. D.

: ‘Design and performance properties of oilfield fibreglass tubulars’, SPE 19728, Society of Petroleum Engineers, San Antonio, TX, 1989.

Smith

L. M.

: ‘Engineering with clad steel’, NiDI Technical Series No. 10064, Nickel Development Institute, Birmingham, 1996.

Yoshida

, MATSUI

, ATSUTA

, TOMA

, and HASEGAWA

: Proc. Offshore Technology Conf., Houston, TX, USA, May 1982, Paper 4200.

Colwell

J. A.

, MARTIN

C. J.

, and MACK

R. D.

: Corrosion, 1989, 45, (5), 429.

10.

Mater. Petform., 1990, 29, (2), 60–63.

11.

Kane

R. D.

, ABAYARATHNA

, NAKAMURA

, and MASAMURA

: Proc. Conf. Corrosion ‘95, Houston, TX, USA, April 1995, NACE, Paper 68.

12.

Ikeda

et al.: Proc. Conf. Corrosion ‘83, Anaheim, CA, USA, April 1983, NACE, Paper 4.

13.

Klein

et al.: Proc. Conf. Corrosion ‘90, Las Vegas, NV, USA, April 1990, NACE, Paper 52.

14.

Craig

B. D.

: ‘Selection guidelines for corrosion resistant alloys in the oil and gas industry’, NiDI Technical Series No. 10073, Nickel Development Institute, Birmingham, 1995.

15.

Nairn

: Proc. 4th Meeting of the EFC Working Party on Corrosion in the Oil and Gas Industry, Barcelona, Spain, July 1993.

16.

Sisak

W. J.

: Proc. Conf. Corrosion ‘91, Cincinnati, OH, USA, March 1991, NACE, Paper 12.

17.

Ueda

et al.: Proc. Conf. Corrosion ‘92, Nashville, TN, USA, April—May 1992, NACE, Paper 55.

18.

Hashizume

: Proc. Conf. Corrosion ‘92, Nashville, TN, USA, April—May 1992, NACE, Paper 54.

19.

‘NKK material selection guide for OCTG’, Fig. A6;1992, Tokyo, NKK Corp.

20.

Francis

and BYRNE

: Proc. Conf. Corrosion ‘94, Baltimore, MD, February—March 1994, NACE, Paper 64.

21.

Gooch

and GUNN

: ‘Alloy materials for sour environments — a critical review’, Report TWI GSP 5607/1/92, TWI, Cambridge, 1992.

22.

Barteri

et al.: Proc. Conf. Corrosion ‘86, Houston, TX, USA, March 1986, NACE, Paper 157.

23.

Francis

: Proc. Conf. Duplex ‘94, Glasgow, UK, November 1994, TWI, Keynote Paper KIV.

24.

Smith

L. M.

and C. De WAARD: Ind. Corros., Dec. 1989—Jan. 1990, 14–18.

25.

Kolts

: Corrosion ‘86, Houston, TX, USA, March 1986, NACE, Paper 323.

26.

Craig

B. D.

: Mater. Petform., 1991, 30, (12), 51–56.

27.

R GAVESON et al.: Proc. Conf. Corrosion ‘87, San Francisco, CA, USA, March 1987, NACE, Paper 286.

28.

Badrak

R. R

: Proc. Conf. Corrosion ‘92, Nashville, TN, USA, April—May 1992, NACE, Paper 62.

29.

Martin

C. J.

: Proc. Conf. Corrosion ‘94, Baltimore, MD, USA, February—March 1994, NACE, Paper 70.

30.

Schutz

R. W.

: Proc. Conf. Corrosion ‘92, Nashville, TN, USA, April—May 1992, NACE, Paper 51.

31.

Kitayama

et al.: Proc. Conf. Corrosion ‘92, Nashville, TN, USA, April—May 1992, NACE, Paper 52.

32.

‘Corrosion resistant alloys for oil and gas production: guidance on general requirements and test methods for H25 service’, EFC Publication No. 17; 1996, London, The Institute of Materials.

33.

Craig

B. D.

: Mater. Petform., 1986, 25, (6), 48.