Fine oxide reduced copper powders of about 10 μm mean grain size are irregular in particle shape and high in oxygen content, which poses a difficulty in achieving good properties from injection moulding. Injection moulding was possible when a multicomponent binder with a large fraction of the backbone polymer was used. Injection moulded parts could be sintered to a density of about 95% theoretical, if reduction of the residual oxides in the powder was effectively carried out prior to closure of pores during sintering. Under such a condition, the injection moulded parts could attain an electrical conductivity higher than 80% of pure copper. July 2004.
TummalaR. R.: ‘Fundamentals of microsystems packaging’, 214; 2001, New York, NY, McGraw-Hill Company Inc.
2.
ZaghlolA., LEONARDW. and CULHAMR.: ‘Proceedings of IEEE applied power electronics conference and exposition-APEC’, Vol. 2, 1037–1042; 2003, Piscataway, NJ, Institute of Electrical and Electronics Engineers Inc.
3.
ShropshireB. H., KLATTK., LINS. T. and CHANT. Y.: mt. J. Powder Metal!., 2003, 39, 47–50.
4.
LimT. W. and HayashiK.: J. Jpn Soc. Powder Powder Metal!., 1993, 40, 373–378.
5.
LimT. W. and HayashiK.: J. Jpn Soc. Powder Powder Metal!., 1991, 138, 114–120.
6.
SweetJ. F., DOMBROSKIM. J AND LAWLEYA.: INT. J. POWDER METALL., 1992, L28, 41–51.
7.
SweetJ. F., DOMBROSKIM. J. and LAWLEYA.: ‘Advances in powder metallurgy’ (ed.PeaseL. F.III and SansoucyR. J.), Vol. 4, 87–102; 1991, Princeton, NJ, MPIF.
8.
BraselG. M. and ALLENJ. K.: ‘Advances in powder metallurgy and particulate materials’, (ed.KckotchR. A. and WebbR.), Vol. 3, 18.65-18.76; 1997, Princeton, NJ, MPIF.
9.
HensK. F., LEED., LINS. T. and GERMANR. M., in ‘Advances in powder metallurgy’, (ed.AndreottiE. R. and McGeehanP. J.), 283–298; 1990, Princeton, NJ, MPIF.
10.
BelangerB., SANSCHAGRINB. and EISAB.: J. Thermoplas. Comp. Mater., 1997, 10, 532–542.
11.
LinS. T.: Ph.D. Thesis, Rensselaer Polytechnic Institute, 19, 1991, Troy, NY.
12.
OnoK., KANEKOY. and KANKAWAY.: J. Jpn Soc. Powder Powder Metal!., 1994, 41, 227–231.
13.
GermanR. M.: ‘Sintering theory and practice’, 110; 1996, New York, NY, John Wiley and Sons, Inc.
14.
WadaN., KANKAWAY. and KANEKOY.: J. Jpn Soc. Powder Powder Metal!., 1997, 44, 604–611.
15.
UraokaH., KANEKOY., IWASAKIH., KANKAWAY. and SAITOHK.: J. Jpn Soc. Powder Powder Metal!., 1990, 37, 187–190.