Effect of tempering on nitrided and deformed austenitic stainless steel

Abstract

The effect of tempering on nitrided austenitic stainless steel AISI 316 has been studied. Nitrided specimens (with 0.4 wt-%N) were tempered for short times at temperatures up to 900°C and the results show a small effect on the microstructures and mechanical properties. The strength is consistent with a Hall–Petch relationship dependent on nitrogen content in solution. The effect of tempering has also been studied on cold and hot deformed nitrided specimens. In these cases, tempering had a range of different effects on the microstructures and mechanical properties. Specimens that are tempered before cold rolling showed a continuous decrease in strength as the tempering temperature increased, while specimens cold rolled and then tempered had a maximum strength at 550°C. Specimens with 0.4 wt-%N subjected to tempering followed by hot deformation also showed a maximum strength at similar tempering temperatures. The nature of these changes has been analysed and mechanisms have been proposed that relate microstructural effects and properties.

Get full access to this article

View all access options for this article.

References

SOUSSAN

, DEGALLAIX

, and FOCT

: Proc. 2nd Int. Conf. on ‘High nitrogen steels’, (ed. Stein

and Witulski

), Dusseldorf, Germany, 1990, 67.

UGGOWITZER

P. J.

and M. HARZENMOSER: Proc. 1st Int. Conf. on ‘High nitrogen steels’, (ed. Foct

and Hendry

), 174; 1989, London, Institute of Metals.

UGGOWITZER

P. J.

and SPEIDEL

M. O.

: Proc. Int. Conf. on ‘Stainless steels’, 762; 1991, Tokyo, Iron and Steel Institute of Japan.

PICKERING

F. B.

: Proc. 1st Int. Conf. on ‘High nitrogen steels’, (ed. Foct

and Hendry

); 10; 1989, London, The Institute of Metals.

FOCT

: Proc. 2nd Int. Conf. on ‘High nitrogen steels’, (ed. Stein

and Witulski

), Dusseldorf, Germany, 1990, Stahleisen.

ESKAFI

M. A. H.

PhD

thesis, University of Strathclyde, Glasgow, UK, 1998.

BAHRAMI

PhD

thesis, University of Strathclyde, Glasgow, UK, 1993.

HANSEN

and D. KUHLMANN WILSDORF: Mater. Scl Eng., 1986, 81, 141.

MONTEIRO

S. N.

and KESTENBACH

H. J.

: Metall Trans. A, 1975, 6A, 938.

10.

JACKSON

P. J.

: Scr. Metall., 1983, 17, 199.

11.

KESTENBACH

H. J.

, DA SILVEIRA

T. LUIZ

, and MONTEIRO

S. N.

: Metall. Trans. A, 1976, 7A, 155.

12.

NORSTROM

L. A.

: Met. Sci., 1977, 11, 208.

13.

DEGALLAIX

, FOCT

, and HENDRY

: Met. Scl Technol, 1986, 2, 946.

14.

IRVINE

K. J.

, LLEWELLYN

D. T.

, and PICKERING

F. B.

: J. Iron Steel Inst., 1961, 199, 153.

15.

BRANDIS

and W. HEIMANN: Proc. Conf. on ‘Stainless steels’, 97; 1985, London, The Institute of Metals.

16.

PICKERING

F. B.

: ‘Physical metallurgy and the design of steels'; 1978, Barking, Applied Science.

17.

MENZEL

, STEIN

, and DAHLMANN

: Proc. 1st Int. Conf. on ‘High nitrogen steels’, (ed. Foct

and Hendry

), 147; 1989, London, Institute of Metals.

18.

SCHRAMM

R. E.

and REED

R. P.

: Met. Trans. A, 1975, 6A, 1345.