Numerical simulation of quenching of large sized blocks of 718 steel used for plastic dies

Abstract

The 718 steel used for plastic dies is required to be prehardened to 29 – 35HRC. For large sized blocks, it is relatively difficult to additionally guarantee uniform hardness with the greatest hardness difference of 3HRC and without any quenching cracks after heat treatment. In this paper, the transient temperature field and microstructure transformation during the quenching process of large sized blocks of 718 steel have been simulated numerically. Based on the simulation and experimental results, an appropriate quenching process, that is, direct air cooled quenching after austenitising at higher temperatures such as 880 – 930°C, was recommended in order to reach hardness uniformity and avoid quenching cracks.

Keywords

QUENCHING NUMERICAL SIMULATION HARDNESS 718 STEEL USED FOR PLASTIC DIE FINITE ELEMENT METHOD (FEM)

Get full access to this article

View all access options for this article.

References

INOUE

and JANAKA

: J. Soc. Mater. Sci. Japan, 1973, 22, 218–223.

DENIS

and ARCHAMBAULT

: Proc. 3rd Int. Conf. on ‘Quenching and control of distortion’, Prague, Czech Republic, March 1999, 263–266.

BUCHMAYR

and J. S. KIRICALDY: J. Heat Treatment, 1990, 8, 127–136.

PAN

J. S.

, HU

M. J.

, TIAN

and RUAN

: Heating Technol, 1998, 1, 1–4.

CHEN

: Adv. Mater. Process., 1997, 152, 44w–44y.

Z. Y.

: ‘The principle of phase transformation’, 1st edn; 1988, Beijing, China, Science Press.

RETI

, FRIED

and FELDE

: Proc. 3rd Int. Conf. 011 ‘Quenching and control of distortion’, Prague, Czech Republic, March 1999, 157–172.

PHAM

T. T.

and E. B. HAWBOLT: Metall Mater. Trans. A, 1995, 26A, 1993–1999.

FERNANDES

F. M. B.

, DENIS

and SIMON

: Mater. Sci. Technol, 1985, 1, 838–844.

10.

LIU

, WU

Z. J.

, WU

J. Z.

and ZHANG

: ‘The numerical simulation on heat treatment process’, 1st edn, 119–158; 1996, Beijing, China, Science Press.

11.

ZXU

Z. C.

and Z. Y. XU: Trans. Metal Heat Treatment, 1988,9, (2), 45.

12.

BAKER

A. J.

, MANHARDT

P. D.

and ORZECHOWSKI

J. A.

: Proc. 2nd Int. Conf. on ‘Quenching and control of distortion’, ASM International, Materials Park, OH, 1996, 283–296.

13.

PAN

J. S.

and M. J. HU: Heat Treatment Metals, 1998, 12, 26— 31.

14.

WOODARD

P. R.

, CHANDRASEICAR

and YANG

H. T. Y.

: Metall Mater. Transform. B, 1999, 30B, 815–822.

15.

YAO

: ‘The application of computer simulation on the quenching of large-sized mould blocks and bearing steel’, 28; 2003, Dissertation, Shanghai Jiao Tong University.

16.

HAMOUDA

A. M. S.

, SULAIMAN

and C. K. LAU: J. Mater. Process. Technol, 2001, 119, 354 — 360.

17.

HOUGARDY

H. P.

and YAMAZAKI

: Steel Res., 1986, 57, 466–471.

18.

AGARWAL

P. K.

and J. K. BRIMACOMBE: Metall Trans. B, 1981, 12B, 121–133.

19.

JOHNSON

A. W.

and R. F. MEHL: Trans. AIME, 1939, 135, 416–458.

20.

KOISTINEN

D. F.

and R. E. MARBURGER: Acta Metall., 1959, 7, 50 — 60.