Analysis of factors affecting type IV cracking in welded joints of high chromium ferritic heat resistant steels

Abstract

In the present work, creep tests on single pass welded joints were carried out to investigate the factors affecting the deterioration of the creep strength of weldments of high Cr heat resistant steels. In creep tests at a temperature of 923 K and stresses of 90 and 120 MPa, creep fracture occurred in the fine grained heat affected zone (FGHAZ) and was identified as type IV cracking. It was found that a peak temperature between Ac₁ and Ac₃ in the FGHAZ caused the observed creep property deterioration. The factors identified as leading to the deterioration are a fine grain structure, low hardness, and large precipitates. Further investigations confirmed the influence of the fine grain structure as a critical factor decreasing the creep rupture time. The hardness difference between the FGHAZ and the base metal is insignificant, especially at 923 K. However, SEM investigations revealed that many large precipitates are distributed on the boundaries of the martensite laths and prior austenite grain boundaries. It is considered that the large precipitates also have a significant influence on the creep strength deterioration.

Get full access to this article

View all access options for this article.

References

Bhadeshia

H. K. D. H.

: ISIJ Int., 2001, 41, (6), 626–640.

Cerjak

, Hofer

and Schaffernak

: ISIJ Int., 1999, 39, (9), 874–888.

Masuyama

: ISIJ Int., 2001, 41, (6), 612–625.

Cerjak

and Letofsky

: Sci. Technol. Weld. Joining, 1996, 1, (1), 36–42.

Bhadeshia

H. K. D. H.

: Proc. Int. Workshop on ‘Innovative structural materials for infrastructure in 21st century’, Tsukuba, Japan, January 2000, National Research Institute for Metals, 89–108.

Lalam

S. H.

, Bhadeshia

H. K. D. H.

and Maokay

D. J. O.

: Sci. Technol. Weld. Joining, 2000, 5, (3), 135–160.

Kozesohnik

, Polt

, Breet

and Buohmayr

: Sci. Technol. Weld. Joining, 2002, 7, (2), 65–68.

Kozesohnik

, Warbiohler

, Letofsky-Papst

, Breet

and Buohmayr

: Sci. Technol. Weld. Joining, 2002, 7, (2), 69–76.

Morimoto

, Ohkita

and Sakurai

: J. Jpn Weld. Soc., 1997, 15, (4), 664–673.

10.

Laha

, Ohandravathi

K. S.

, Rao

K. B. S.

, Mannan

S. L.

and Sastry

D. H.

: Metall. Mater. Trans. A, 2001, 32A, 115–123.

11.

Matsui

, Tabuohi

, Watanabe

, Kubo

, Kinugawa

and Abe

: ISIJ Int. Suppl., 2001, 41, 126–130.

12.

Sourmail

: Mater. Sci. Technol., 2001, 17, (1), 1–14.

13.

Morimoto

, Tanaka

, Ohkita

and Fuji

: J. Jpn Weld. Soc., 1998, 16, (4), 512–521.

14.

Ogata

: J. Soc. Mater. Sci. Jpn, 1998, 47, (3), 253–259.

15.

Shinozaki

, Li

D. J.

, Kuroki

, Harada

and Ohishi

: Proc. 7th Int. Welding Symp., Kobe, Japan, November 2001, Japan Welding Society, 743–748.

16.

Takaki

and Tuszaki

: in ‘Microstructure of materials’, 2nd edn, 134–135; 2001, Tokyo, Asakura Press.

17.

Prader

, Cerjak

and David

S. A.

: Proc. 4th Int. Conf. on ‘Trends in welding research’, Gatlinburg, TN, USA, June 1995, ASM International, 247–252.

18.

Cerjak

and Letofsky

: Proc. 7th Int. Welding Symp., Kobe, Japan, November 2001, Japan Welding Society, 731–736.

19.

Cerjak

, Hofer

and Schaffernak

: Proc. 5th Workshop on ‘The ultra-steel’, Tsukuba, Japan, January 2001, National Research Institute for Metals, 158–163.

20.

Cui

, Kim

I. S.

, Kang

O. Y.

and Miyahara

: ISIJ Int., 2001, 41, (4), 368–371.

21.

Yutaka

, Okamoto

and Tokunaga

: Tetsu-to-Hagane, 1995, 81, (5), 59–64.

22.

Goods

S. H.

and Brown

L. M.

: Acta Mater., 1979, 27, 1–15.