Influence of process parameters on microstructural evolution and mechanical properties in friction stirred Al-2024 (T3) alloy

Abstract

Commercial Al-2024 (T3) alloy was friction stir welded at various heat index (HI) values using bead on plate approach. Quantitative analysis using electron microscopy and differential scanning calorimetry (DSC) revealed a complex variation in the precipitation evolution of Guinier-Preston-Bagaryatskii (GPB) zone and Al₂CuMg (S phase) precipitates in nugget and heat affected zone (HAZ). Differential scanning calorimetry data also suggested formation energy of GPB zone equal to −236 J g⁻¹. Tensile properties attained a maximum for HI values close to 3·94 in the nugget region, which was attributed to corresponding minimisation of the volume fraction of coarse S phase to the profit of GPB zone. The precipitation of fine S phase precipitates resulted in higher tensile properties in HAZ as compared to those in nugget for all HI values. Experimental data were used to determine major strengthening mechanisms by using constitutive relationships.

Keywords

FRICTION STIR WELDING ALUMINIUM ALLOYS DIFFERENTIAL SCANNING CALORIMETRY PRECIPITATION EVOLUTION TENSILE STRENGTH

Get full access to this article

View all access options for this article.

References

Thomas

W. M.

: International Patent App. No. PCT/GB92/02203 and GB PatentApp. No. 9125978·8, 1991,US PatentNo. 5460317.

Nicolas

and Deschamps

: Acta Mater., 2003, 51, 6077.

Arbegast

W. J.

: Proc. Hot Deformation of Aluminum Alloys III. San Diego, CA, USA, March, 2003, TMS, 313.

Arbegast

W. J.

: ‘Technology gaps that stand in the place of taking Stir Friction to a standard’, Proc. SAE Friction Stir Weld. Symp., Albuquerque, NM, USA, June 2004, SAE.

Dixit

, Mishra

R. S.

, Lederich

R. J.

and Talwar

: Sci. Technol. Weld. Join., 2007, 12, (4), 334.

Genevois

, Deschamps

, Denquin

and Doisneau-cottignies

: Acta Mater., 2005, 53, 2447.

Jones

M. J.

, Heurtier

, Desrayaud

, Montheillet

, Allehaux

and Driver

J. H.

: Scr. Mater., 2005, 52, 693.

Ehrström

J. C.

, Bigot

, Cervi

and Gerard

: Mater. Sci. Forum, 2003, 426–432, 2941.

Lockwood

W. D.

, Tomaz

and Reynolds

A. P.

: Mater. Sci. Eng. A, 2002, A323, 348.

10.

Karlsen

, Frigaard

, Hjelen

, Grong

and Norum

: Mater. Sci. Forum, 2003, 426–432, 2861.

11.

Heurtier

, Jones

M. J.

, Desrayaud

, Driver

J. H.

and Montheillet

: Mater. Sci. Forum, 2003, 426–432, 2927.

12.

Starink

M. J.

, Wang

S. C.

and Sinclair

: Proc. Friction Stir Welding and Processing III, San Francisco, CA, USA, February 2005, TMS, 233.

13.

Sharma

S. R.

: ‘Microstructure modification for improved mechanical properties in 356 Al using friction stir processing’, PhD thesis, University of Missouri Rolla, MI, USA, 2005.

14.

Starink

M. J.

: Int. Mater. Rev., 2004, 49, 191.

15.

Reich

, Ringer

S. P.

and Hono

: Phil. Mag. Lett., 1999, 79, (9), 639.

16.

Wang

S. C.

, Starink

M. J.

and Gao

: Scr. Mater., 2006, 54, 287.

17.

Buhler

, Fries

S. G.

and Spencer

P. J.

: J. Phase Equilibr., 1998, 19, (4), 317.

18.

Perlitz

and Westgren

: Ark. Chem. Miner. Geol. B, 1943, 16B, 13.

19.

Wolverton

: Acta Mater., 2001, 49, 3129.

20.

Sato

Y. S.

, Urata

and Kokawa

: Metall. Mater. Trans. A, 2002, 33A, (3), 625.

21.

Rhodes

C. G.

, Mahoney

M. W.

, Bingel

W. H.

and Calabrese

Scr. Mater., 2003, 48, 1451.

22.

Sato

Y. S.

and Kokawa

: Metall. Mater. Trans. A, 2001, 32A, 3033.

23.

Starink

M. J.

, Wang

, Sinclair

and Gregson

P. J.

: Acta Mater., 1999, 47, (14), 3841.

24.

Deschamps

and Brechet

: Acta Mater., 1999, 47, (1), 293.

25.

Silcock

M. J.

: J. Inst. Met., 1960, 89, 203.

26.

Notin

, Dirand

, Bouaziz

and Hertz

J. C. R.

: Acad. Sci. Paris, 1986, 63, 302.