Keyhole stability in disc laser welding of AZ31B and AZ61A magnesium alloys and weld metal properties

Abstract

To confirm the process potential and limitations of laser welding of magnesium alloys, a newly developed disc laser of 16 kW in maximum power was used to weld thin plates of AZ31B and AZ61A alloys. Melting characteristics and weld metal properties were studied under different process parameters. The very high power density of the applied beam caused the keyhole and the molten pool to be unstable. Underfill was the main welding defect limiting the process window and its formation was closely related to the keyhole instability. A process diagram indicating areas of sound and defected welds could be constructed. Sound welded joints could be obtained for AZ31B alloy with similar mechanical properties as that of the base material. The brittle intermetallics network present along the grain boundaries in AZ61A weld metals required a higher energy input to alleviate its detrimental effect on the mechanical properties of the welded joints.

Keywords

MAGNESIUM ALLOYS LASER WELDING KEYHOLE WELDING DEFECTS UNDERFILL

Get full access to this article

View all access options for this article.

References

Kainer

K. U.

: ‘Magnesium alloys and technology’, 1–23; 2003, Weinheim, Wiley-VCH.

Mordike

B. L

and Ebert

: ‘Magnesium Properties-applications-potential’, Mater. Sci. Eng. A, 2001, A302, 37–45.

Steen

W. M.

: ‘Laser material processing’, 3rd edn, 108–144; 2003, London, Springer.

Kannatey-Asibu

, ‘Principles of laser materials processing’, 502–567; 2009, Hoboken, NJ, John Wiley & Sons, Inc.

Jankiewicz

and Kopczyiiski

: ‘Diode-pumped solid-state lasers’, Opto-Electron. Rev., 2001, 9, (1), 19–33.

Morris

and Mann

: ‘Disk laser enables application advancement’, Proc. 23rd Int. Cong. on ‘Applications of lasers and electro-optics’, Jacksonville, FL, USA, October 2004, Laser Institute of America, Paper 305.

Hügel

: ‘New solid-state lasers and their application potentials’, Opt. Laser Eng., 2000, 34, 213–229.

Katayama

: in ‘New developments in advanced welding’, (ed. N. Ahmed), 158–197; 2005, Cambridge, Woodhead Publishing.

Cao

, Jahazi

, Immarigeon

J. P.

and Wallace

: ‘A review of laser welding techniques for magnesium alloys’, J. Mater. Process. Technol., 2006, 171, 188–204.

10.

Matsunawa

: ‘Problems and solutions in deep penetration laser welding’, Sci. Technol. Weld. Join., 2001, 6, (6), 351–354.

11.

Kawahito

, Mizutani

and Katayama

: ‘High quality welding of stainless steel with 10 kW high power fibre laser’, Sci. Technol. Weld. Join., 2009, 14, (4), 288–294.

12.

Beretta

and Previtali

: ‘Estimate of maximum pore size in keyhole laser welding of carbon steel’, Sci. Technol. Weld. Join., 2009, 14, (2), 106–116.

13.

Ribic

, Rai

and DebRoy

: ‘Numerical simulation of heat transfer and fluid flow in GTA/laser hybrid welding’, Sci. Technol. Weld. Join., 2008, 13, (8), 683–693.

14.

Sanders

P. G.

, Keske

J. S.

, Leong

K. H.

and Kornecki

: ‘High power Nd:YAG and CO2 laser welding of magnesium’, J. Laser Appl., 1999, 11, (2), 96–103.

15.

Quan

Y. J.

, Chen

Z. H.

, Gong

X. S.

and Yu

Z. H.

: ‘Effects ofheat input on microstructure and tensile properties of laser welded magnesium alloy AZ31’, Mater. Charact., 2008, 59, (10), 1491–1497.

16.

Wang

H. Y.

and Li

Z. J.

: ‘Investigation of laser beam welding process of AZ61 magnesium-based alloy’, Acta. Metall. Sin. (Engl. Lett.), 2006, 19, (4), 287–294.

17.

Coelho

R. S.

, Kostka

, Pinto

, Riekehr

, Kocak

and Pyzalla

A. R.

: ‘Microstructure and mechanical properties of magnesium alloy AZ31B laser beam welds’, Mat. Sci. Eng. A, 2008, A485, 20–30.

18.

Gao

, Zeng

X. Y.

, Tan

and Feng

J. C.

: ‘Study of laser MIG hybrid welded AZ31 magnesium alloy’, Sci. Technol. Weld. Join., 2009, 14, (4), 274–281.

19.

Sun

, Pan

and Wei

: ‘Comparative evaluation of tungsten inert gas and laser welding of AZ31 magnesium alloy’, Sci. Technol. Join., 2002, 7, (6), 343–351.

20.

‘Standard test methods for tension testing of metallic materials’, E8-00b, ASTM International West Conshohocken, PA, USA, 2003.

21.

Katayama

and Kawahito

: ‘Interpretation of laser weld penetration and welding phenomena’, Chin. J. Lasers, 2009, 36, (12), 3160–3166.

22.

Kawahito

, Matsumoto

, Abe

and Katayama

: Q. J. Jpn Weld. Soc., 2009, 27, (3), 183–188.

23.

Pastor

, Zhao

, Martukanitz

R. P.

and DebRoy

: ‘Porosity, underfill and magnesium loss during continuous wave Nd:YAG laser welding of thin plates of aluminum alloys 5182 and 5754’, Weld. J., 1999, 78, 207s–216s.

24.

ISO

International Standard

13919–2, ‘Welding-electron and laser beam welded joints-guidance on quality levels for imperfections-part 2: aluminium and its weldable alloys’; 2001, Geneva, International organization for standardization.