Influence of HAZ cracks on fatigue resistance of resistance spot welded joints made of advanced high strength steels

Abstract

A method is reported with which heat affected zone (HAZ) cracks in a specific region of spot welded joints, made of advanced high strength steels, could be realised. The influence of HAZ cracks on the fatigue behaviour, which is the focus of the contribution, was studied by evaluating the stiffness characteristics as a function of the number of cycles N in comparison with crack-free specimens, i.e. by analysing HAZ and fatigue cracks on the specimen surface and the surface of fatigue fractures containing beach marks. It was found that the fatigue cracks are not initiated at the HAZ cracks. The number of cycles to failure N_f is not significantly reduced for specimens with HAZ cracks. Overall, the examinations did not reveal any influence of HAZ cracks on the fatigue strength of resistance spot welded joints.

Keywords

Spot welding HAZ crack Discontinuities Fatigue Advanced high strength steels AHSS

Get full access to this article

View all access options for this article.

References

Franz

: Application of ultra high strength steel in the automotive processing chain’, Steels Cars Trucks, 2008, 2, 354–357.

Osburg

, Patberg

, Grüneklee

, Flöth

, Große-Gehling

, Hinz

, Mebus

: ‘New steel body – Sicherer und wirtschaflicher Karosserieleichtbau mit Stahl’, Automob. Z. ATZ, 2004, 106, (3), 190.

Wesling

, Rekesdrees

, Keitel

, Winkler

, Schreiber

: ‘Investigations into the resistance spot welding of newly developed sheets made of higher-strength and super-high-strength steels’, Weld. Cut., 2004, 3, 168–173.

Sierlinger

, Szinyur

, Ritsche

: ‘Schweißeignung und Gebrauchseigenschaften von punktgeschweißten hochfesten Multiphasenstählen’, Eurojoin, 2004, 5, V10.

Fritzsche

, Laurenz

: ‘Widerstandspunktschweißen kaltgewalzter Mehrphasenstähle – DVS 2935-2’, DVS-Sondertagung Widerstandspunktschweißen, 2007, 20, 33–40.

Weber

, Göklü

: ‘Resistance spot welding of uncoated and zinc coated advanced high-strength steels (AHSS) – weldability and process reliability-influence of welding parameters’, Weld. World, 2006, 50, (3/4), 3–12.

Maggi

, Murgia

: ‘Introduction to the metallurgic characteristics of advanced high-strength steels for automobile applications’, Weld. Int., 2008, 22, (9), 610–618.

Bertsch

, Ruther

: ‘Adaptive weld control as innovative production technology in volume production’, Steels Cars Trucks, 2008, 2, 350–354.

Hofmann

, Becker

, Göklü

, Richter

, Thomas

: ‘X-IP 1000: properties of an austenitic super high strength high manganese steel – status and outlook’, Steels Cars Trucks, 2008, 2, 34–42.

10.

Hsu

, Lee

, Hsieh

, Weng

: ‘Fracture analysis on spot weld nugget of advanced high strength steels’, Proc. Baosteel Biennial Academic Conf., Shanghai, China, September 2008, Vol. 3, D38–D42.

11.

Hahn

, Flüggen

: ‘Einfluss zyklischer Belastung auf das Tragverhalten von Widerstandspunktschweißverbindungen vor dem Hintergrund der Auslegung crashrelevanter Bauteile’, DVS-Sondertagung Widerstandspunktschweißen, 2010, 21, 180–191.

12.

Ritsche

, Sierlinger

: ‘Einfluss von Imperfektionen auf die Gebrauchseigenschaften von punktgeschweißten Mehrphasenstählen’, DVS-Sondertagung Widerstandspunktschweißen, 2007, 20, 40–46.

13.

‘Resistance spot welding – destructive tests of welds – method for the fatigue testing of spot welded joints’, DIN EN ISO 14324, ISO, Geneva, Switzerland, 2003.

14.

Hahn

, Flüggen

: ‘Untersuchung der Beeinflussung des Festigkeitsverhaltens von Widerstandspunktschweißverbindungen durch betriebsbedingte Belastungen’, Schweißen Schneid., 2010, 62, (4), 194–197.

15.

Gaul

, Weber

, Rethmeier

: ‘Evaluation of fatigue crack propagation in spot welded joints by stiffness measurements’, Int. J. Fatigue, 2011, 33, (5), 740–745.</othinfo>

16.

Gaul

, Weber

, Brauser

, Rethmeier

: ‘Method to obtain weld discontinuities in spot welded joints made of advanced high strength steels’, SC-Auto-38-10, IIW, Roissy Charles de Gaulle Cedex, France, 2010, 1–12.

17.

Fischer

, Gruhle

, Günter

, Preß

, Simon

: ‘Simulation of crack propagation in spot welds subject to cyclic loading’, Weld. Cut., 1994, 46, (1), 12–16.