Full penetration 15 kW Yb fibre laser butt welding of thick AlMg3 (AW 5754) plates was performed in PA position. A contactless inductive electromagnetic weld pool support system was used to prevent gravity dropout of the melt. The welding speed needed to achieve 20 mm penetration was ∼0·5 m min−1. An ac power supply of ∼244 W at 460 Hz was necessary to completely suppress gravity dropout of the melt and eliminate sagging of the weld pool root side surface. The oscillating magnetic field can suppress the Marangoni convection in the lower part of the weld pool. The system was also successfully used in the full penetration welding of 30 mm thick AlMg3 plates.
SetoN, KatayamaS, MatsunawaA: ‘Porosity formation mechanism and suppression procedure in laser welding of aluminium alloys’, Weld. Int., 2001, 15, (3), 191–202.
3.
VerhaegheG: ‘Low porosity laser welding of 12·7 mm thickness aerospace aluminium’, Proc. INALCO 2007, Osaka, Japan, October 2007, JAA and JLWA, 143–150.
4.
RethmeierM, GookS, LammersM, GumenyukA: ‘Laser-hybrid welding of thick plates up to 32 mm using a 20 kW fibre laser’, J. Jpn Weld. Soc., 2009, 27, (2), 74s–79s.
5.
MillsKC: ‘Recommended values of thermophysical properties for selected commercial alloys’; 2002, Cambridge, Woodhead Publishing Ltd.
6.
KeeneBJ: ‘Review of data for the surface tension of pure metals’, Int. Mater. Rev., 1993, 38, 157–192.
7.
AvilovVV, BergerP, AmbrosyG: ‘Electromagnetic melt support system for overhead position laser and electron beam welding of thick metal plates’, Proc. 5th Int. Symp. on ‘Electromagnetic processing of materials’, Sendai, Japan, October 2006, ISIJ, Vol. 2, 237–241.
8.
AvilovVV, MoldovanR, BergerP, GrafT, MockD: ‘Electromagnetic weld pool control by CO2 and YAG disk laser welding of thick stainless steel plates’, Proc. 6th Int. Conf. on ‘Electromagnetic processing of materials’, Dresden, Germany, October 2009, Forschungszenzrum Dresden-Rossendorf, 644–647.
9.
JonesLP, AubertP, AvilovV, CosteF, DaennerW, JokinenT, NightingaleKR, WykesM: ‘Towards advanced welding methods for the ITER vacuum vessel sectors’, Fusion Eng. Des., 2003, 69, 215–220.
10.
AvilovVV, MoldovanR, BergerP, GrafT: ‘Electromagnetic weld pool control systems for laser beam welding of thick metal plates’, Proc. Int. Workshop on ‘Thermal forming and welding distortion’, Bremen, Germany, April 2008, BIAS Verlag, 413–420.
11.
LandauLD, LifshitzEM: in‘Electrodynamics of continuous media’, Vol. 8, ‘Course of theoretical physics’;1984, Oxford, Pergamon.
BachmannM, AvilovV, GumenyukA, RethmeierM: ‘CFD simulation of the liquid metal flow in high power laser welding of aluminum with electromagnetic weld pool support’, Proc. 2nd Int. Conf. on ‘Fluid mechanics and heat and mass transfer’, Corfu, Greece, July 2011, WSEAS, 179–184.