The friction stir welding (FSW) tools for high temperature materials are required to have high performance at elevated temperatures. The purposes of this study are to strengthen iridium with an excellent oxidation resistance at elevated temperatures and to develop an FSW tool for high temperature materials. As a result, it was clarified that Ir based alloys are strengthened by the addition of elements with a larger atomic radius than that of Ir, and Zr was the most effective element in this study. Ir–10Re–1Zr has excellent mechanical properties and oxidation resistance at elevated temperatures. The FSW tool made from this alloy was hardly worn even if the SUS 304 stainless steel was friction stir welded.
OzekcinA, JinHW, KooJY, BangaruNV, AyerR: ‘A microstructural study of friction stir welding joints of carbon steels’, Int. J. Offshore Polar Eng., 2004, 14, (4), 284–288.
6.
UejiR, FujiiH, CuiL, NishiokaA, KunishigeK, NogiK: ‘Friction stir welding of ultrafine grained plain low-carbon steel formed by the martensite process’, Mater. Sci. Eng. A, 2006, A423, 324–330.
7.
FujiiH, CuiL, TsujiN, MaedaM, NakataK, NogiK: ‘Friction stir welding of carbon steel’, Mater. Sci. Eng. A, 2006, A429, 50–57.
8.
CuiL, FujiiH, TsujiN, NogiK: ‘Friction stir welding of a high carbon steel’, Scr. Mater., 2007, 56, 637–640.
9.
CuiL, FujiiH, TsujiN, NakataK, NogiK, IkedaR, MatsushitaM: ‘Transformation in stir zone of friction stir welded carbon steels with different carbon contents’, ISIJ Int., 2007, 47, (2), 299–306.
10.
SatoYS, YamanoiH, KokawaH, FuruharaT: ‘Microstructural evolution of ultrahigh carbon steel during friction stir welding’, Scr. Mater., 2007, 57, 557–560.
ParkSHC, SatoYS, KokawaH, OkamotoK, HiranoS, InagakiM: ‘Rapid formation of the sigma phase in 304 stainless steel during friction stir welding’, Scr. Mater., 2003, 49, 1175–1180.
14.
ParkSHC, SatoYS, KokawaH, OkamotoK, HiranoS, InagakiM: ‘Microstructural characterization of stir zone containing residual ferrite in friction stir welded 304 austenitic stainless steel’, Sci. Technol. Weld. Join., 2005, 10, (5), 550–556.
15.
ZhuXK, ChaoYJ: ‘Numerical simulation of transient temperature and residual stresses in friction stir welding of 304L stainless steel’, J. Mater. Process. Technol., 2004, 146, 263–272.
16.
SatoYS, NelsonTW, SterlingCJ, SteelRJ, PatterssonC.-O: ‘Microstructure and mechanical properties of friction stir welded SAF 2507 super duplex stainless steel’, Mater. Sci. Eng. A, 2005, A397, 376–384.
17.
SaeidT, Abdollah-zadehA, AssadiH, GhainiFMlek: ‘Effect of friction stir welding speed on the microstructure and mechanical properties of a duplex stainless steel’, Mater. Sci. Eng. A, 2008, A496, 262–268.
18.
SatoYS, HarayamaN, KokawaH, InoueH, TadokoroY, TsugeS: ‘Evaluation of microstructure and properties in friction stir welded superaustenitic stainless steel’, Sci. Technol. Weld. Join., 2009, 14, (3), 202–209.
LakshminarayananAK, BalasubramanianV: ‘An assessment of microstructure, hardness, tensile and impact strength of friction stir welded ferritic stainless steel joints’, Mater. Des., 2010, 31, 4592–4600.
21.
SteelRJ, RowlandR, AllenC, NelsonTW, SorensenC, PetersonJ, PackerSM: ‘Friction stir welding of high melting metals and applications and development of tool’, Proc. Forum on ‘Friction stir welding’, Tokyo, Japan, April 2010, Sanpo publication,12–19.
22.
ParkSHC, SatoYS, KokawaH, OkamotoK, HiranoS, InagakiM: ‘Boride formation induced by pcBN tool wear in friction-stir-welded stainless steels’, Metall. Mater. Trans. A: Phys. Metall. Mater. Sci., 2009, 40A, (3), 625–636.
23.
ThompsonB, BabuSS: ‘Tool degradation characterization in the friction stir welding of hard metals’, Weld. J., 2010, 89, 256s–261s.
24.
ChoiDH, LeeCY, AhnBW, ChoiJH, YeonYM, SongK, ParkHS, KimYJ, YooCD, JungSB: ’Frictional wear evaluation of WC–Co alloy tool in friction stir spot welding of low carbon steel plates’, Int. J. Refract. Met. Hard Mater., 2009, 27, 931–936.
ReedBD, SchneiderSJ: ‘Testing of wrought iridium/chemical vapor deposition rhenium rocket’, NASA Technical Memorandum 107452, NASA, Washington, DC, USA, 1997.
29.
BiaglowBDReedJA, SchneiderSJ: ‘Iridium-coated rhenium radiation-cooled rockets’, NASA Technical Memorandum 107453, NASA, Washington, DC, USA, 1997.
30.
MiyazawaT, IwamotoY, MarukoT, FujiiH: ‘Development of Ir based tool for friction stir welding of high temperature materials’, Sci. Technol. Weld. Join., 2011, 28, (2), 188–192.
31.
KittelC: ‘Atomic radius’, in‘Introduction to solid state physics’, 6th edn, (trans. R. Uno et al.), 82; 1988, Tokyo, Maruzen.
OkadaA, YamamotoY, YodaR: ‘Hot-hardness and indentation creep characteristics of pure metals’, Tetsu-to-Hagane, 1987, 73, (9), 1186–1192.
34.
‘Hot-rolled stainless steel plate, sheet and strip’, JIS G 4304, JSA, Tokyo, Japan, 2005.
35.
MoteffJ, BhargaveRK, McClluoughWL: ‘Correlation of the hot-hardness with the tensile strength of 304 stainless steel to temperatures of 1200°C’, Metall. Trans. A, 1975, 6A, 1101–1104.
36.
KimYG, FujiiH, TsumuraT, KomazakiT, NakataK: ‘Three defect types in friction stir welding of aluminum die casting alloy’, Mater. Sci. Eng. A, 2006, A415, 250–254.
37.
OosterkampA, OosterkampLD, NordeideA: ‘“Kissing bond” phenomena in solid-state welds of aluminum alloys’, Weld. J., 2004, 83, 225s–231s.
38.
‘NIRM creep data sheet’, no. 32A, NIMS, Tsukuba, Japan, 1995.