Microscale evaluation of mechanical properties of friction stir welded A6061 aluminium alloy/304 stainless steel dissimilar lap joint

Microscale evaluation of the mechanical properties of a friction stir welded A6061/SUS 304 grooved lap joint was performed using a microtensile test and transmission electron microscopy. The microtensile test revealed that ∼62% of the area along which the rotating tool passed the specimen was regarded as the bonded region and that the joint was fractured at the A6061 matrix owing to the formation of very thin interfacial reaction layers. Equiaxed aluminium grains were observed at the interface of the specimen after it was fractured, indicating that the interface deformed only slightly during the microtensile test. It should be noted that although the maximum tensile strength of the joint was approximately the same as that of the base alloy, the proof stress of the joint decreased with the dissolution of the β″ phase in the A6061 aluminium alloy.