This study was aimed at evaluating the static shear strength and fatigue properties of the newly developed refilled friction stir spot welded AA 6061-T6 joints. The keyhole, the process disadvantage of conventional friction stir spot welding, was refilled successfully, using an additional filler plate, with specially designed tools. Two different tool profiles, namely, convex and concave, were used for the refilling process. Sound and defect free joints were obtained by the refilling process. Joints refilled with convex tools showed better static shear strength than those with the concave ones. The variation of microhardness in different regions of the weld was analysed. Fatigue tests were conducted on the lap shear specimens at a stress ratio of R = 0·1. The optical micrographs of the welds after fatigue failure in both the conventional and refilled processes were examined to study the fatigue crack propagation and failure modes.
AgarwalH., GokhaleA. M., GrahamS. and HorstemeyerM. F.:‘Void growth in 6061-aluminum alloy under triaxial stress state’, Mater. Sci. Eng. A, 2003, A341, 35–42.
2.
AmbrizR. R., MesmacqueG., RuizA., AmroucheA., LopezV. H. and BenseddiqN.:‘Fatigue crack growth under a constant amplitude loading of Al-6061-T6 welds obtained by modified indirect electric arc technique’, Sci. Technol. Weld. Join., 2010, 15, 514–521.
3.
BriskhamP., BlundellN., HanL., HewittR. and YoungK.:‘Comparison of self-pierce riveting, resistance spot welding and spot friction joining for aluminium automotive sheet’, SAE Technical Paper 2006-01-0774, 2006.
4.
ThomasW. M., NicholasE. D., NeedhamJ. C., MurchM. G., Temple-SmithP. and DawesC. J.:‘Friction stir welding’, International Patent Application no. PCT/GB92/02203 and Great Britain Patent Application no. 9125978·8, 1991.
5.
DawesC. J. and ThomasW. M.:‘Friction stir process welds aluminum alloys’, Weld. J., 1996, 75, 41–45.
ZhangZ., YangX., ZhangJ., ZhouG., XuX. and ZouB.:‘Effect of welding parameters on microstructure and mechanical properties of friction stir spot welded 5052 aluminum alloy’, Mater. Des., 2011, 32, 4461–4470.
8.
SunY. F., FujiiH., TakakiN. and OkitsuY.:‘Microstructure and mechanical properties of mild steel joints prepared by a flat friction stir spot welding technique’, Mater. Des., 2012, 37, 384–392.
9.
KhanM. I., KuntzM. L., SuP., GerlichA., NorthT. H. and ZhouY.:‘Resistance and friction stir spot welding of DP600: a comparative study’, Sci. Technol. Weld. Join., 2007, 12, 175–182.
10.
SunY. F., FujiiH., TakakiN. and OkitsuY.:‘Novel spot friction stir welding of 6061 and 5052 Al alloys’, Sci. Technol. Weld. Join., 2011, 15, 605–612.
11.
LathabaiS., PainterM. J., CantinG. M. D. and TyagiV. K.:‘Friction spot joining of an extruded Al–Mg–Si alloy’, Scr. Mater., 2006, 55, 899–902.
12.
GerlichA., YamamotoM. and NorthT. H.:‘Strain rates and grain growth in Al 5754 and Al 6061 friction stir spot welds’, Metall. Mater. Trans. A, 2007, 38A, 1291–1302.
13.
IwashitaT.:‘Method and apparatus for joining’, US Patent no. 6601751 B2, 2003.
14.
ShenZ., YangX., ZhangZ., CuiL. and LiT.:‘Microstructure and failure mechanisms of refill friction stir spot welded 7075-T6 aluminum alloy joints’, Mater. Des., 2013, 44, 476–486.
15.
UematsuY., TokajiK., TozakiY., KuritaT. and MurataS.:‘Effect of re-filling probe hole on tensile failure and fatigue behavior of friction stir spot welded joints in Al–Mg–Si alloy’, Int. J. Fatigue, 2008, 30, 1956–1966.
16.
ShenZ., YangX., YangS., ZhangZ. and YinY.:‘Microstructure and Mechanical properties of friction spot welded 6061-T4 aluminum alloy’, Mater. Des., 2014, 54, 766–778.
17.
ZhouL., LiuD., NakataK., TsumuraT., FujiiH., IkeuchiK., MichishitaY., MichishitaY., FujiyaY. and MorimotoM.:‘New technique of self-refilling friction stir welding to repair keyhole’, Sci. Technol. Weld. Join., 2012, 17, 649–655.
18.
ShillingC. and Dos SantosJ.:‘Method and Device for Joining at Least Two Adjoining Work Pieces by Friction Welding’, US patent no. 0179682, 2002.
19.
TierM. D., RosendoT. S., dosSantosJ. F., HuberN., MazzaferroJ. A., MazzaferroC. P. and StrohaeckerT. R.:‘The influence of refill FSSW parameters on the microstructure and shear strength of 5042 aluminium welds’, J. Mater. Process. Technol., 2013, 213, 997–1005.
20.
FoxS. L.:‘Refill friction stir spot weld repair of a fatigue crack. Research experience for undergraduates’; 2010, Rapid City, SD, South Dakota School of Mines and Technology.
21.
ChowdhuryS. H., ChenD. L., BholeS. D., CaoX. and WanjaraP.:‘Lap shear strength and fatigue life of friction stir spot welded AZ31magnesium and 5754 aluminum alloys’, Mater. Sci. Eng. A, 2012, A556, 500–509.
22.
LinP.-C., SuZ.-M., HeR.-Y. and LinZ.-L.:‘Failure modes and fatigue life estimations of spot friction welds in cross-tension specimens of aluminum 6061-T6 sheets’, Int. J. Fatigue, 2012, 38, 25–35.
23.
TranV.-X., PanJ. and PanT.:‘Fatigue behavior of aluminum 5754-O and 6111-T4 spot friction welds in lap-shear specimens’, Int. J. Fatigue, 2008, 30, 2175–2190.
24.
HassanifardS., MohammadpourM. and RashidH. A.:‘A novel method for improving fatigue life of friction stir spot welded joints using localized plasticity’, Mater. Des., 2014, 53, 962–971.
25.
HuangY. X., HanB., LvS. X., FengJ. C., LiuH. J., LengJ. S. and LiY.:‘Interface behaviours and mechanical properties of filling friction stir weld joining AA 2219’, Sci. Technol. Weld. Join., 2012, 17, 225–230.
26.
HuangY. X., HanB., TianY., LiuH. J., LvS. X., FengJ. C., LengJ. S. and LiY.:‘New technique of filling friction stir welding’, Sci. Technol. Weld. Join., 2011, 16, 497–501.
27.
MuthukumaranS.:‘An improved friction forming process and a friction forming machine with a tool and fixture’, Indian Patent Application no. 137/KOL/06 (filed on 16 February 2006), Patent No. 242420 (granted on 27 August 2010).
28.
John PrakashS. and MuthukumaranS.:‘Refilling probe hole of friction spot joints by friction forming’, Mater. Manuf. Processes, 2011, 26, 1539–1545.
29.
Specimens dimensions and procedure for shear testing resistance spot and embossed projection welded joints’, JIS Z 3136, Japanese Standards Association, Tokyo, Japan, 1999.
30.
RosendoT., ParraB., TierM. A. D., da SilvaA. A. M., dos SantosJ. F. and StrohaeckerT. R.:‘Mechanical and microstructural investigation of friction spot welded AA6181-T4 aluminium alloy’, Mater. Des., 2011, 32, 1094–1100.
31.
FujimotoM., KogaS., AbeN., SatoY. S. and KokawaH.:‘Microstructural analysis of stir zone of Al alloy produced by friction stir spot welding’, Sci. Technol. Weld. Join., 2008, 13, 663–670.
32.
WangD.-A. and LeeS.-C.:‘Microstructures and failure mechanisms of friction stir spot welds of aluminum 6061-T6 sheets’, J. Mater. Process. Technol., 2007, 186, 291–297.
33.
MurrL. E., LiuG. and McClureJ. C.:‘A TEM study of precipitation and related microstructures in friction-stir-welded 6061 aluminum’, J. Mater. Sci., 1998, 33, 1243–1251.