Solidification cracking susceptibilities of high Mn steel welds were evaluated in the present study. A longitudinal Varestraint technique was utilised to assess the solidification cracking behaviours of the fusion zone. High Mn steel welds were more susceptible to solidification cracking than 304 and 202 austenitic stainless steel welds, however, they were less susceptible than 310S austenitic stainless steel welds. Extensive segregations of Mn and C took place at the dendritic and grain boundaries in the weld metal, and accordingly contributed to the increase of the hot cracking susceptibility of high Mn steel by the enlargement of solidification temperature range. Further, continuous γ-(Fe,Mn)3C eutectic phases formed at 1090°C along the grain boundary primarily resulted in the increase of solidification cracking sensitivity in high Mn steel.
ChoiHC, HaTK, ShinHC and ChangYW: ‘The formation kinetics of deformation twin and deformation induced ϵ-martensite in an austenite Fe-C-Mn steel’, Scr. Mater., 1999, 40, 1171–1177.
2.
BrackeL, KestensL and PenningJ: ‘Direct observation of the twinning mechanism in an austenitic Fe-Mn-C steel’, Scr. Mater., 2009, 61, 220–222.
3.
ParkKT, KimGS, KimSK, LeeSW, HwangSW and LeeCS: ‘On the Transitions of deformation modes of fully austenitic steels at room temperature’, Met. Mater. Int., 2010, 16, 1–6.
4.
DumayA, ChateauJP, AllainS, MigotS and BouazizO: ‘Influence of addition elements on the stacking-fault energy and mechanical properties of an austenitic Fe–Mn–C steel’, Mater. Sci. Eng.A, 2008, A483–A484, 184–187.
5.
AllainS, ChateauJP, BouazizO, MigotS and GueltonN: ‘Correlations between the calculated stacking fault energy and the plasticity mechanisms in Fe–Mn–C alloys’, Mater. Sci. Eng. A, 2004, A387–A389, 158–162.
6.
KimJK, LeeSJ and De CoomanBC: ‘Effect of Al on the stacking fault energy of Fe–18Mn–0·6C twinning-induced plasticity’, Scr. Mater., 2044, 65, 363–366.
7.
GrässelO, KrügerL, FrommeyerG and MeyerLW: ‘High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development – properties – application’, Int. J. Plast., 2000, 16, 1391–1409.
8.
FrommeyerG, BrűxU and NeumannP: ‘Supra-ductile and high-strength manganese-TRIP/TWIP steels for high energy absorption purposes’, ISIJ Int., 2003, 43, 438–446.
9.
HuaD, Zheng-YouT, WeiL, MeiW and DanS: ‘Microstructures and Mechanical Properties of Fe-Mn-(A1 Si) TRIP/TWIP Steels’, J. Iron Steel Res., 2006, 13, 66–70.
10.
ParkKT, JinKG, HanSH, HwangSW, ChoiKY and LeeCS: ‘Stacking fault energy and plastic deformation of fully austenitic high manganese steels: Effect of Al addition’, Mater. Sci. Eng. A, 2010, A527, 3651–3661.
11.
MujicaL, WeberS, PintoH, ThomyC and VollertsenF: ‘Microstructure and mechanical properties of laser-welded joints of TWIP and TRIP steels’, Mater. Sci. Eng. A, 2010, A527, 2071–2078.
12.
MendezJ, GhoreshyM, MachayWBF, SmithTJN, SmithRW: ‘Weldability of austenitic manganese steel’, J. Mater. Process Technol., 2004, 153–154, 596–602.
13.
KeilD, ZinkeM and PriesH: ‘Investigations on hot cracking of novel high manganese TWIP-steels’, in‘Hot Cracking Phenomena in Welds III’, (ed. LippoldJ C et al.), 209–233; 2011, Berlin/Heidelberg, Springer.
14.
RajinikanthV, MukherjeeK, Ghosh ChowdhuryS, SchiebahnA and BleckW: ‘Mechanical property and microstructure of resistance spot welded twinning induced plasticity-dual phase steels joint’, Sci. Tchnol. Weld. Join., 2013, 18, 485–491.
15.
HamadaAS and KarjalainenLP: ‘Hot ductility behavior of high-Mn TWIP steels’, Mater. Sci. Eng. A, 2011, A528, 1819–1827.
16.
SahaDC, ChoY and ParkY.-D: ‘Metallographic and fracture characteristics of resistance spot welded TWIP steels’, Sci. Tchnol. Weld. Join., 2013, 18, 711–720.
17.
CrossCE: ‘On the origin of weld solidification cracking’, in‘Hot cracking phenomena in welds’, (ed. BölinghausT et al.), 3–18; 2010, Berlin/Heidelberg, Springer.
18.
LippoldJC: ‘Recent developments in weldability test’, in‘Hot cracking phenomena in welds’, (ed. BölinghausT et al.), 271–290; 2010, Berlin/Heidelberg, Springer.
19.
ArataY, MatsudaF and SaruwatariS: ‘Varestraint test and solidification crack susceptibility in weld metal of austenitic stainless steels’, Trans. JWRI, 1974, 3, 79–88.
20.
LundinCD, LeeCH and MenonR: ‘Hot ductility and weldability of free machining austenitic stainless steel’, Weld. J., 1988, 67, 119–130.
21.
AnkaraA and AriHB: ‘Determination of hot crack susceptibility in various kinds of steels’, Mater. Design, 1996, 17, 261–265.
22.
ShankarV, GillTPS, MannanSL and SundaresanS: ‘Solidification cracking in austenitic stainless steel welds’, Sadhana, 2003, 28, 359–382.
23.
HullFC: ‘Effect of delta ferrite on the hot cracking of stainless steel’, Weld. J, 1967, 46, 399–409.
24.
ZhenmingX, GaofeiL, QingfengG and QichuanJ: ‘TiC as heterogeneous nuclei of the (Fe, Mn)3C and austenite intergrowth eutectic in austenite steel matrix wear resistant composite’, Mater. Res. Bull., 2004, 39, 457–463.
25.
BarbagalloS, LaukliHI, LohneO and CerriE: ‘Divorced eutectic in a HPDC magnesium–aluminum alloy’, J. Alloy. Compd, 2004, 378, 226–232.