Double pulse laser welding is investigated to reduce hot cracking in 6082 aluminium alloy welds. Therefore, Nd:YAG and diode laser pulses are superimposed and synchronised with a specific delay. The diode laser heats the parent metal and weld metal during weld spot solidification to compensate for solidification shrinkage and thermal contraction. The results of conventional pulsed laser welding prove that hot cracking is strongly dependent on the pulse peak power of the Nd:YAG laser, which constrains the crack free penetration depth. Adding the diode laser pulse at a defined time during weld spot solidification eliminated hot cracking. The double pulse welding method allowed the butt welding of 0·5 mm thick 6082 aluminium alloys without the formation of hot cracking.
SteenWM: ‘Laser material processing’, 3rd edn, 169–172; 2003, New York, Springer-Verlag.
2.
CieslakMJ and FuerschbachPW: ‘On the weldability, composition, and hardness of pulsed and continuous Nd:YAG laser welds in aluminum alloys 6061, 5456 and 5086’, Metall. Mater. Trans. B, 1988, 19B, 319–329.
3.
ZhangJ, WeckmanDC and ZhouY: ‘Effects of temporal pulse shaping on cracking susceptibility of 6061-T6 aluminum Nd:YAG laser welds’, Weld. J., 2008, 87, 18– 30.
4.
MichaudEJ, KerrHW and WeckmanDC: ‘Temporal pulse shaping and solidification cracking in laser welded Al–Cu alloys’, Proc. 4th Int. Conf. on ‘Trends in welding research’, Gatlinburg, TN, USA, June 1995, ASM International, 1–6.
5.
DworakJ: ‘The effect of laser beam pulse shape on the process of pulsed laser welding’, Weld. Int., 2014, 28, (7).
6.
MatsunawaA, MizutaniM and KatayamaS: ‘Mathematical modeling of fusion and solidification in laser welding and evaluation of hot cracking’, Trans. Jpn Weld. Res. Inst., 1996, 25, (2), 161–169.
7.
KatayamaS, MizutaniM and MatsunawaA: ‘Modelling of melting and solidification during laser spot welding’, Sci. Technol. Weld. Joining, 1997, 2, (1), 2–9.
8.
BergmannJP, BieleninM, StambkeM, FeustelT, WitzendorffPv and HermsdorfJ: ‘Effects of diode laser superposition on pulsed laser welding of aluminum’, Physics Procedia, 2013, 41, 180–189.
9.
SheikhiM, Malek GhainiF and AssadiH: ‘Solidification crack initiation and propagation in pulsed laser welding of wrought heat treatable aluminium alloy’, Sci. Technol. Weld. Joining, 2014, 19, (3), 250–255.
10.
LiuJ, RaoZ, LiaoS and WangP.-C: ‘Modeling of transport phenomena and solidification cracking in laser spot bead-on-plate welding of AA6063-T6 alloy. Part II—simulation results and experimental validation’, Int. J. Adv. Manuf. Technol., 2014.
11.
Ren-peiL, Zu-jueD and Yong-mingP: ‘Solidification crack susceptibility of aluminum weld metals’, Trans. Nonferrous Met. Soc. China, 2006, 16, 110–116.
12.
ArataY, MatsudaF, NakataK and ShinozakiK: ‘Solidification crack susceptibility of aluminum alloy weld metals (Report 2): effect of straining rate on cracking threshold in weld metal during solidification’, Trans. Jpn Weld. Res. Inst., 1977, 6, (1), 91–104.
13.
PloshikhinV, ZochH.-W, KarkhinVA, MakhutinM and PeschHJ: ‘Numerical optimisation of the temperature field for the prevention of solidification cracking during laser beam welding using the multi-beam technique’, Proc. Int. Conf. ‘Materials Week 2002’, Munich, Germany, 2002, Deutsche Gesellschaft für Materialkunde.
14.
PloshikhinV, PrihodovskyA and IlinA: ‘Experimental investigation of the hot cracking mechanism in welds on the microscopic scale’, Front. Mater. Sci., 2011, 5, (2), 135–145.
15.
BrennerB and GoebelG: ‘Avoiding hot cracking by induction based change of thermal strains during laser welding’, Proc. Int. Cong. on ‘Applications of lasers and electro optics’, Scottsdale, AZ, USA, 2006, Laser Institute of America, Paper 105.
16.
ProkhorovN: ‘The technological strength of metals while crystallizing during welding’, Weld. Prod., 1962, 9, (4), 1–8.
17.
NakashibaS, OkamotoY, SakagawaT, MiuraK, OkadaA and UnoY: ‘Welding characteristics of aluminum alloy by pulsed Nd:Yag laser with pre- and post-irradiation of superposed continuous diode laser’, Proc. Int. Cong. on ‘Applications of lasers and electro optics’, Orlando, FL, USA, 2011, Laser Institute of America,23–27.
18.
DavisJR: ‘ASM specialty handbook: aluminum and aluminum alloys’, 1st edn, 378; 1993, Materials Park, ASM International.
19.
TottenGE and MacKenzieDS: ‘Handbook of aluminum’, 1st edn., Vol. 1, 56; 2003, New York, Marcel Dekker.
20.
DrezetM, LimaMS.-F, WagniereJD, RappazM and KurzW: ‘Crack-free aluminium alloy welds using a twin laser process’, in Proc. Int. Inst. Weld. Conf. (ed. P. Mayr, G. Posch and H. Cerjak), Graz, Austria, 2008, International Institute of Welding,87–94.