This study examined the effects of alloying elements, which are normally used to modify the composition of advanced high strength steels, on the expulsion phenomenon during resistance spot welding as well as the effects of alloying elements on the expulsion limit current (ELC). An equation for the ELC prediction was derived from the correlation between the ELC and alloying element: ELC (kA) = 9.85–0.74Si–0.67Al–0.28C–0.20Mn–0.18Cr. The coefficient of determination between the calculated and measured values was sufficiently high (R2 = 0.94). The extent of the effects of the alloying elements on the ELC was in the order of Si, Al, C, Mn and Cr. From the correlations among the ELC and resistivity R, the coefficient of thermal expansion α and yield strength (YS1200°C), the ELC was calculated to be ELC (kA) = 9.3 − 0.057R − 0.035α+0.22YS1200°C, and the coefficient of determination was sufficiently high (R2 = 0.96).
PouranvariM., AbediA., MarashiP. and GoodarziM.: ‘Effect of expulsion on peak load and energy absorption of low carbon steel resistance spot welds’, Sci. Technol. Weld. Join., 2008, 3, 40–41.
2.
MaC., BholeS. D., ChenD. L., LeeA., BiroE. and BoudreauG.: ‘Expulsion monitoring in spot welded advanced high strength automotive steels’, Sci. Technol. Weld. Join., 2006, 11, 480–487. doi: 10.1179/174329306X120895
3.
HwangI. S., KangM. J. and KimD. Ch.: ‘Expulsion reduction in resistance spot welding by controlling of welding current waveform’, Procedia Eng., 2011, 10, 2775–2781. doi: 10.1016/j.proeng.2011.04.461
4.
ShenJ., ZhangY. S. and LaiX. M.: ‘Influence of initial gap on weld expulsion in resistance spot welding of dual phase steel’, Sci. Technol. Weld. Join., 2010, 15, 386–392. doi: 10.1179/136217110X12693513264213
5.
ZhangY., ShenJ. and LaiX.: ‘Influence of electrode force on weld expulsion in resistance spot welding of dual phase steel with initial gap using simulation and experimental method’, ISIJ Int., 2012, 52, 494–497.
6.
ChoiH. D., ParkY. D., SonDo. M., KimS. J. and MoonM. B.: ‘High-rate tensile properties of Si-reduced TRIP sheet steels’, Met. Mater. Int., 2010, 16, 28–32.
7.
HanamuraT., TorizukaS., SunaharaA., ImagumbaiM. and TakechiH.: ‘Excellent total mechanical-properties – balance of 5% Mn, 30000 MPa% steel’, ISIJ Int., 2011, 51, 685–687. doi: 10.2355/isijinternational.51.685
8.
ZhangH., HuS. J. and SenkaraJ.: ‘A statistical analysis of expulsion limits in resistance spot welding’, J. Manuf. Sci. Eng., 2000, 122, 501–510. doi: 10.1115/1.1285873
9.
‘Resistance welding – weldability. Part 1: assessment of weldability for resistance spot, seam and projection welding of metallic materials’, ISO 18278-1:2004, ISO, Geneva, Switzerland2004.
10.
MiuraM., NakayaM. and MukaiY.: ‘Cold-rolled, 980MPa grade steel-sheets with excellent elongation and stretch-flangeability’, Kobelco Technol. Rev., 2008, 28, 8–12.
11.
JungG. S., LeeK. Y., LeeJ. B., BhadeshiaH. K. D. H. and SuhD. W.: ‘Spot weldability of TRIP assisted steels with high carbon and aluminium contents’, Sci. Technol. Weld. Join., 2012, 17, 92–98. doi: 10.1179/1362171811Y.0000000081
12.
NayakS. S., Baltazar HernandezV. H., OkitaY. and ZhouY.: ‘Microstructure–hardness relationship in the fusion zone of TRIP steel welds’, Mater. Sci. Eng. A, 2012, A551, 73–81. doi: 10.1016/j.msea.2012.04.096
13.
PouranvariM. and MarashiS. P. H.: ‘Critical review of automotive steels spot welding: process, structure and properties’, Sci. Technol. Weld. Join., 2013, 18, 369–371. doi: 10.1179/1362171813Y.0000000120
14.
SenkaraJ., ZhangH. and HuS. J.: ‘Expulsion prediction in resistance spot welding’, Weld. J., 2004, 83, 123–132.
15.
‘Standard test method for sheet resistance uniformity evaluation by in-line four-point probe with the dual-configuration procedure’, F1529, ASTM, West Conshohocken, PA, USA1997.
16.
‘Metals handbook’, 8th edn, Vol. 1, ‘Properties and selection of metals’,; 1997, Materials Park, OH, USA, ASM International.
17.
ChoiD. Y. and KimY. G.: ‘Trend of joining technology for automotive sheet steels.’, J. KWJS, 2009, 27, 125–130.
18.
GuoZ., SaundersN., MiodownikA. P. and SchilleJ. P.: ‘Introduction of materials modelling into processing simulation – towards true virtual design and simulation’, Int. J. Met. Eng., 2013, 2, 198–202.
19.
SaundersN., GuoZ., LiX., MiodownikA. P. and SchilleJ. Ph.: ‘Using JMatPro to model materials properties and behavior’, JOM, 2003, 12, 60–63. doi: 10.1007/s11837-003-0013-2
20.
PolakovaI. and KubinaT.: ‘Flow stress determination methods for numerical modelling’, Proc. 22nd Int. Conf. on ‘Metallurgy and materials’. Brno, Czech Republic, 15–17 May 2013, TANGER, Ltd.
21.
GuoZ., SaundersN., SchilleJ. P. and MiodownikA. P.: ‘Material properties for process simulation’, Mater. Sci. Eng. A, 2009, A499, 11–12.
22.
GuoZ., SaundersN., MiodownikA. P. and SchilleJ. Ph.: ‘Modelling of materials properties and behaviour critical to casting simulation’, Mater. Sci. Eng. A, 2005, A413–A414, 465–469. doi: 10.1016/j.msea.2005.09.036
23.
GuoZ., SaundersN., MiodownikP. and SchilleJ. P.: ‘Modeling material properties of lead-free solder alloys.’, J. Electron. Mater., 2008, 37, 23–31. doi: 10.1007/s11664-007-0218-1
24.
HatamiaS., MalakizadiaA., NyborgaL. and WallinD.: ‘Critical aspects of sinter-hardening of prealloyed Cr–Mo steel’, J. Mater. Process. Technol., 2010, 210, 1180–1189. doi: 10.1016/j.jmatprotec.2010.03.002
25.
FeulvarchE., RobinV. and BergheauJ. M.: ‘Resistance spot welding simulation: a general finite element formulation of electrothermal contact conditions’, J. Mater. Process. Technol., 2004, 153–154, 436–441. doi: 10.1016/j.jmatprotec.2004.04.096