Fatigue crack growth behaviour of 4130X steel in H 2 S environment

Abstract

Fatigue crack growth rates of 4130X steel used for compressed natural gas vessels were investigated in this paper. Considering the operating conditions, corrosion fatigue tests at a low frequency of 0·0067 Hz, in H₂S saturated, H₂S unsaturated and air environments were conducted on modified wedge opening load specimens by using a home made low cycle fatigue test system. Curve fitting was applied to the fatigue test data of da/dN–ΔK according to Paris formula. A correlation study between fracture surface and stress intensity factor range was conducted and K values for three stages in different environments were characterised quantitatively. The results show that da/dN in H₂S environment is more than 20 times faster than in an air environment. When the H₂S concentration reaches a certain range, the increase of da/dN becomes slower than that of the H₂S concentration. da/dN differs by 2·4 times while the concentration differs by 11 times. The corrosive environment accelerates the fatigue failure.

Keywords

H2S CORROSION FATIGUE CRACK GROWTH RATE ALLOWABLE CRACK SIZE FATIGUE FRACTURE

Get full access to this article

View all access options for this article.

References

Sadananda

and Vasudevan

A. K.

: Int. J. Fatigue 2003 25 899–914.

Xue

H. J.

and Lu

G. Z.

: J. Meek Strength (China) 2001 23, (1), 35–37.

D. M.

, and Zhou

C. Y.

: Pres. Ves. (China) 2003 20 (8) 1–3 52.

Wang

M. X.

and Zheng

X. L.

: J. Aeronaut. (China) 1993 14, (3), 188–189.

Zhao

J. P.

and Y:

C.Y.

Pres. Ves. (China) 1999 16 (6) 1–4 57.

Tsay

L. W.

Liu

Y. C.

Young

M. C.

and Lin

D.-Y.

: Mater. Sci. Eng. A 2004 374 204–210.

Dong

Y. J.

Zhang

Y. L.

and Wang

: Measur. Technol., 2004 6 37–38.

‘The test method of metal fatigue crack growth rate’, Chinese Standard GB6398–86 1986.

‘Natural gas’, Chinese Standard GB17820–1999 1999.

10.

‘Sulphide stress cracking resistant metallic materials for oilfield equipment, NACE MR0175–03 2003.

11.

‘Laboratory testing of metals for resistance to specific forms of environmental cracking in H 2S environments NACE TM0177-05 2005.

12.

‘Guidelines on materials requirements for carbon and low alloy steels for H 2S-containing environments in oil and gas production’ EFC Publications No.16 reprinted with Corrections 1998.

13.

Saxena

and Hudak

S. J.

JR : J. Test. Evaluat., 1975, 3, (6), 455–468.

14.

Shih

T. T.

and G:

W.G.

‘ Environment-sensitive fracture: evaluation and comparison of test methods’325–340; 1984

Philadelphia

PA, ASTM.

15.

‘ASME boiler and pressure vessel code’, Section XI, Appendix A, 2001 Article A- 3000 371–389.

16.

Blackburn

P. R.

and Rana

M. D.

: Pres. Ves. Technol., 1986 108, (2), 234–240.

17.

Fabis

T. R.

Liaw

P. K.

and D:

J.D.

‘ Environment-sensitive fracture: evaluation and comparison of test methods’470–483; 1984

Philadelphia

PA, ASTM.

18.

Barsom

J. M.

: Nall Assoc. Corros. Eng., 1972 424–436.

19.

Stewart

A. T.

: Proc. mechanisms of environment sensitive cracking of materials Guildford, UK, April 1977

University of Survey

400–411.