The aim of the present study is to determine the role of tin on the corrosion behaviour of bronzes. For this purpose, different nuances of single phase α-Cu(Sn) are immersed in a 10–2 mol L–1 deaerated sulphate solution, buffered at pH 6·8. Then, the chemical–physical and electrochemical characterisation of an artificial patina, thin layer of corrosion products electrochemically formed at the surface of a 7 wt-% tin bronze are performed. First of all, the synthesised species are cathodically reduced. The successive steps of the potential–time curves, characteristic of the electrochemical reactions occurring at the electrode surface, are successfully calibrated with reference oxides. In order to complete the previous results, X-ray photoelectron spectroscopy (XPS) depth profiles are carried out by abrading progressively the oxidised surface. The deconvoluted XPS and Auger electron spectroscopy (AES) spectra speak in favour of an ‘alloy/SnO2/Cu2O’ layered structure similar to that reported in the literature. Analyses carried out on the oxidised samples by transmission electron microscopy (TEM) confirm this pattern.
HeL.ZhaoQ. R. and GaoM.: ‘ Characterization of corroded bronze Ding from the Yin Ruins of China’Corros. Sci200749, (6), 2534–2546.
2.
IngoG. M.de CaroT.RiccucciC. and KhosroffS.: ‘ Uncommon corrosion phenomena of archaeological bronze alloys’Appl. Phys. A200683A, (4), 581–588.
3.
WadsakM.ConstantinidesI.VittiglioG.AdriaensA.JanssensK.SchreinerM.AdamsF. C.BrunellaP. and WuttmannM: ‘Multianalytical study of patina formed on arch-aeological metal objects from Bliesbruck-Reinheim’Mikrochim. Acta2000133159–164.
4.
CicileoG. P.CrespoM. A. and MB. Rosales: ‘Comparative study of patinas formed on statuary alloys by means of electrochemical and surface analysis techniques’Corros. 200446, (4), 929–953.
5.
ChiavariC.RahmouniK.TakenoutiH.JoiretS.VermautP. and RobbiolaL.: ‘ Composition and electrochemical properties of natural patinas of outdoor bronze monuments’Electrochim. Acta200752, (27), 7760–7769.
TylecoteR. F.: ‘The effect of soil conditions on the long-term corrosion of buried tin—bronzes and copper’, J. Archaeolog. 19796, (4), 345–368.
8.
OttoH.: ‘Ober röntgenographisch nachweisbare Bestandteile in Patinaschichten’Naturwissenschaften196148, (21), 661–664.
9.
ConstantinidesI.AdriaensA. and AdamsF.: ‘ Surface characterization of artificial corrosion layers on copper alloy reference materials’Appl Surf Sci., 2002189, (1-2), 90–101.
10.
BernardiE.ChiavariC.MartiniC. and MorselliL.: ‘ The atmospheric corrosion of quaternary bronzes: an evaluation of the dissolution rate of the alloying elements’Appl. Phys. A, 200892A, (1), 83–89.
11.
RobbiolaL.BlenginoJ. M. and FiaudC.: ‘ Morphology and mechanisms of formation of natural patinas on archaeological Cu—Sn alloys’Corros. Sci199840, (12), 2083–2111.
12.
PiccardoP.MilleB. and RobbiolaL: ‘ Tin and copper oxides in corroded archaeological bronzes’, in ‘Corrosion of metallic heritage artefacts — investigation, conservation and prediction for long-term behaviour’, (ed. DillmannP..), 239–262; 2007CambridgeWoodhead Publishing.
13.
Debiemme-ChouvyC.AmmelootF. and SutterE. M. M.: ‘ X-ray photoemission investigation of the corrosion film formed on a polished Cu-135n alloy in aerated NaC1 solution’Appl Surf Sci2001174, (1), 55–61.
14.
RobbiolaL.TranT. T. M.DubotP.MajerusO. and RahmouniK.: ‘ Characterisation of anodic layers on Cu-10Sn bronze (RDE) in aerated NaC1 solution’Corros. Sci., 200850, (8), 2205–2215.
15.
SidotE.SouissiN.BousselmiL.TrikiE. and RobbiolaL.: ‘ Study of the corrosion behaviour of Cu-10Sn bronze in aerated Na2504 aqueous solution’, Corros. ScL200648, (8), 2241–2257.
16.
MullerJ.: ‘Etude électrochimique et caractérisation des produits de corrosion formés A. la surface des bronzes Cu—Sn en milieu sulfate’PhD thesisUniversité Paris Est, Thiais, France2010.
17.
SeahM. P.SmithG. C., and AnthonyM. T.: ‘AES-energy calibration of electron spectrometers. 1. An absolute, traceable energy calibration and the provision of atomic reference line energies’Surf Interf Anal199015, (5), 293–308.
18.
SeahM. P.HolbournM. W.OrtegaC. and DaviesJ.A.: ‘ An intercomparison of tantalum pentoxide reference studies’Nucl. Instrum. Methods Phys. Res. Sect. B198830B, (2), 128–139.
19.
AteyaB. G.FritzJ. D. and W:H. W.‘Kinetics of dealloying of a copper-5 atomic percent gold alloy’J. Electrochem. Soc., 1997144, (8), 2606–2613.
20.
LaikB.GessierF.MercierF.TrocellierP.ChausseA. and MessinaR.: ‘ Influence of lithium salts on the behaviour of a petroleum coke in organic carbonate solutions’, Electrochim. Acta199844, (10), 1667–1676.
21.
LaikB.PoizotP. and TarasconJ.M.: ‘ The electrochemical quartz crystal microbalance as a means for studying the reactivity of Cu2O toward lithium’J. Electrochem. Soc., 2002149, (3), A251—A255.
22.
BasileF.BergnerJ.BombartC.RondotB.Le GuevelP. and LorangG: ‘Electrochemical and analytical (XPS and AES) study of passive layers formed on Fe—Ni alloys in borate solutions’Proc. 8th European Conf. on ‘Applications of surface and interface analysis’Seville, Spain, Philippe Dillmann October 1999154–157.
23.
BouttemyM.: ‘Etude des mécanismes de formation et de croissance des films passifs formés sur les alliages Fe—Ni et Fe—Cr’PhD thesisUniversité Paris Sud — Paris XI Paris, Paris, France2006.
24.
KellerP. and H:H. H. ‘ XPS-studies on the formation of passive layers on Sn and CuSn alloys in 0.1 m KOH’Z. Phys. Chem., 2005219, (11), 1481–1488.
25.
MathisF.: ‘Croissance et propriétés des couches d'oxydation et des patines A. la surface d'alliages cuivreux d'intérêt archéologique ou artistique’PhD thesis, Université d'Orsay (Paris 11)Paris, France2005.
26.
LeyssensK.AdriaensA.DegrignyC. and PantosE: ‘Evaluation of corrosion potential measurements, as a means to monitor the storage and stabilization process of archaeological copper-based artifacts’Anal. Chem., 2006782794–2801.