The corrosion study of the pipeline steel is extremely important for the safety of CO2 pipeline. The present work studied the effect of temperature on the corrosion behaviour of X70 steel in high pressure CO2/SO2/O2/H2O mixtures. Weight loss method was utilised to measure the corrosion rate. Environmental scanning electron microscopy and focused ion beam technology were employed to observe the morphology of product scales. X-ray diffraction was used to analyse the composition of product scales. The porosity of product scales was measured, and the exhaust gas was detected by gas chromatography. Results showed that the corrosion rate increased with the increasing temperature and then started to decline with temperature with the peak corrosion rate at 348 K. Results also showed that there was hydrogen that existed in the exhausted gas, indicating that the hydrogen evolution reaction was contained in the corrosion cathodic process.
ForbesSMVermaPCurryTEFriedmannSJWadeSM: ‘Guidelines for CO2 capture, transport and storage’; 2008Washington, DCWorld Resources Institute.
2.
DooleyJJDahowskiRTDavidsonCL: ‘Comparing existing pipeline networks with the potential scale of future U.S. CO2 pipeline networks’, Energy Proc.20091(1)1595–1602.
3.
ChoiYSNesicSYoungD: ‘Effect of impurities on the corrosion behavior of CO2 transmission pipeline steel in supercritical CO2–water environments’, Environ. Sci. Technol.201044(23)9233–9238.
4.
DugstadAMorlandBClausenS: ‘Corrosion of transport pipelines for CO2 – effect of water ingress’, Energy Proc.201143063–3070.
5.
XiangYWangZXuCZhouCLiZNiW: ‘Impact of SO2 concentration on the corrosion rate of X70 steel and iron in water-saturated supercritical CO2 mixed with SO2’, J. Supercrit. Fluids201158(2)286–294.
6.
XiangYWangZYangXNiWLiZ: ‘Corrosion behavior of X70 steel in the supercritical CO2 mixed with SO2 and saturated water’Proc. 21st Int. Offshore and Polar Engineering Conf., Maui, HI, USA, June 2011, ISOPE,350–354.
7.
XiangYWangZLiZNiW: ‘The impact of corrosion product scales on the corrosion rates of X70 steel in supercritical CO2 with SO2 and H2O impurities’Proc. World Cong. on ‘Engineering and technology (CET)’Shanghai, China October 2011IEEE498–504.
8.
XiangYWangZYangXLiZNiW: ‘The upper limit of moisture content for supercritical CO2 pipeline transport’, J. Supercrit. Fluids20126714–21.
9.
NesicSLeeKLJ: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films – Part 3: film growth model’, Corrosion200359(7)616–628.
10.
NesicSNordsveenMNyborgRStangelandA: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films – Part 2: a numerical experiment’, Corrosion200359(6)489–497.
11.
NesicSPostlethwaiteJOlsenS: ‘An electrochemical model for prediction of corrosion of mild steel in aqueous carbon dioxide solutions’, Corrosion199652(4)280–294.
12.
NesicSWangSCaiJXiaoY: ‘Integrated CO2 corrosion – multiphase flow model’Proc. SPE Int. Symp. on ‘Oilfield corrosion’, Aberdeen, UK, May 2004, Society of Petroleum Engineers, Paper 87555.
13.
NordsveenMNesicSNyborgRStangelandA: ‘A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films – Part 1: theory and verification’, Corrosion200359(5)443–456.
14.
SongFM: ‘A comprehensive model for predicting CO2 corrosion rate in oil and gas production and transportation systems’, Electrochim. Acta201055(3)689–700.
15.
VitseFNesicSGunaltunYde TorrebenDLDuchet-SuchauxP: ‘Mechanistic model for the prediction of top-of-the-line corrosion risk’, Corrosion200359(12)1075–1084.
16.
de WaardCMilliamsDE: ‘Carbonic acid corrosion of steel’, Corrosion197531(5)177–182.
17.
YinZFFengYRZhaoWZBaiZQLinGF: ‘Effect of temperature on CO2 corrosion of carbon steel’, Surf. Interface Anal.200941(6)517–523.
18.
KladkaewNIdemRTontiwachwuthikulPSaiwanC: ‘Corrosion behavior of carbon steel in the monoethanolamine–H2O–CO2–O2–SO2 system’, Ind. Eng. Chem. Res.200948(19)8913–8919.
19.
NainarMVeawabA: ‘Corrosion in CO2 capture process using blended monoethanolamine and piperazine’, Ind. Eng. Chem. Res.200948(20)9299–9306.
20.
CuiZDWuSLZhuSLYangXJ: ‘Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2’, Appl. Surf. Sci.2006252(6)2368–2374.
21.
‘Standard practice for preparing, cleaning, and evaluating corrosion test specimens’G1-03ASTMWest Conshohocken, PA, USA2003.
22.
‘Standard practice for laboratory immersion corrosion testing of metals’G31ASTMWest Conshohocken, PA, USA1994.
23.
SpycherNPruessKEnnis-KingJ: ‘CO2–H2O mixtures in the geological sequestration of CO2. I. Assessment and calculation of mutual solubilities from 12 to 100 degrees C and up to 600 bar’, Geochim. Cosmochim. Acta200367(16)3015–3031.
24.
AustegardASolbraaEde KoeijerGMolnvikMJ: ‘Thermodynamic models for calculating mutual solubilities in H2O–CO2–CH4 mixtures’, Chem. Eng. Res. Des.200684(A9)781–794.
25.
MunkejordSTJakobsenJPAustegardAMolnvikMJ: ‘Thermo- and fluid-dynamical modeling of two-phase multi-component carbon dioxide mixtures’, Greenhouse Gas Control Technol.20091(1)1649–1656.
26.
MunkejordSTJakobsenJPAustegardAMolnvikMJ: ‘Thermo- and fluid-dynamical modelling of two-phase multi-component carbon dioxide mixtures’, Int. J. Greenhouse Gas Control20104(4)589–596.
27.
WeiYJiQ: ‘Velocity profile and gas bubble size distribution in an agitated vessel – a cold model study on the particle size and its distribution in gas–liquid dispersion polymerization processes’, Chem. React. Eng. Technol.19862(2)14–24.
28.
NesicS: ‘Key issues related to modelling of internal corrosion of oil and gas pipelines – a review’, Corros. Sci.200749(12)4308–4338.
29.
AgudeloACMarcoJFGancedoJrPerez-AlcazarGA: ‘Fe–Mn–Al–C alloys: a study of their corrosion behaviour in SO2 environments’, Hyperfine Interact.2002139(1-4)141–152.
30.
LideDr: ‘CRC handbook of chemistry and physics: a ready-reference book of chemical and physical data’; 2008Boca Raton, FLCRC Press.
31.
KertesAS: ‘Solubility data series’in ‘Sulfites, selenites and tellurites’, (ed. MassonM R, ed); 1987OxfordPergamon252–255.
32.
YuQHuangYLZhengC: ‘Hydrogen permeation and corrosion behaviour of high strength steel 35CrMo under cyclic wet–dry conditions’, Corros. Eng. Sci. Technol.200843(3)241–247.
33.
ZhengCBHuangYLYuQHuoCY: ‘Effect of H2S on stress corrosion cracking and hydrogen permeation behaviour of X56 grade steel in atmospheric environment’, Corros. Eng. Sci. Technol.200944(2)96–100.
34.
AllamIMArlowJSSaricimenH: ‘Initial stages of atmospheric corrosion of steel in the Arabian Gulf’, Corros. Sci.199132(4)417–432.
35.
ZhaoBLiYZhuoYTongHZhangXChenC: ‘Mass transfer and kinetics study on the sulfite forced oxidation with manganese ion catalyst’, Korean J. Chem. Eng.200724(3)471–476.
36.
BäckströmHLJ: ‘The chain-reaction theory of negative ctalysis’, J. Am. Chem. Soc.192749(6)1460–1472.
37.
MoayedMHNewmanRC: ‘Deterioration in critical pitting temperature of 904L stainless steel by addition of sulfate ions’, Corros. Sci.2006483513–3530.