Mostly known to improve the high temperature oxidation resistance of superalloys, hafnium may also form carbides. Several per cents of Hf allow developing a dense carbide network to mechanically strengthen alloys. Here, the high temperature oxidation behaviour of three HfC containing cobalt alloys was characterised at all steps of a thermogravimetry test: heating, isothermal stage and cooling, compared with two Co–Cr–C model alloys. The five alloys were heated in synthetic air, maintained at 1200°C during 50 h and then cooled. The mass gains were plotted versus time or according to (m×dm/dt = Kp–m×Kv) to specify the isothermal kinetic constants, or versus temperature to determine how oxidation acts during heating and oxide spallation occurs during cooling. Compared to the ternary alloys, the oxidation of the HfC reinforced alloys starts earlier but leads to lower mass gains during heating, the isothermal oxidation is faster and oxide spallation occurs later.
SimsC. T. and HagelW. C.: ‘The superalloys’; 1972New YorkJohn Wiley & Sons.
2.
SimsC. T.StoloffN. S. and HagelW. C.: ‘Superalloy II – high temperature materials for aerospace and industrial power’; 1987New YorkJohn Wiley.
3.
BerthodP.MichonS.ArandaL.MathieuS. and GachonJ. C.: ‘Experimental and thermodynamic study of the microstructure evolution in cobalt-base superalloys at high temperature’Calphad200327353–359.
4.
DonachieM. J. and DonachieS. J.: ‘Superalloys – a technical guide’2nd edn; 2002Materials Park, OHASM International.
5.
BerthodP.HeilC. and ArandaL.: ‘Influence of the morphologic evolution of the eutectic carbides at high temperature on the thermal expansion behaviour of refractory cast alloys’J. Alloys Compds2010504243–250.
6.
BerthodP.MichonS.ArandaL. and SteinmetzP.: ‘Consequences of the high temperature microstructure evolution on the tensile properties at high temperature of a cobalt-based superalloys reinforced by tantalum carbides’Proc. No. 0702 ‘Matériaux 2006’, Fédéation Française des Matériaux, Dijon, France, November 2006.
7.
BerthodP.ArandaL. and HeilC.: ‘Effect of a preliminary aging treatment on the oxidation kinetic at high temperature for a cobalt-based alloy strengthened by tantalum carbides’Open Corros. J.20092150–156.
8.
BerthodP.: ‘High temperature properties of several chromium-containing Co-based alloys reinforced by different types of MC carbides (M = Ta, Nb, Hf and/or Zr)’J. Alloys Compds2009481746–754.
9.
KofstadP.: ‘High temperature corrosion’; 1988LondonElsevier Applied Science.
10.
YoungD. J.: ‘High temperature oxidation and corrosion of metals’; 2008AmsterdamElsevier.
11.
LeeW. S. and KimG. M.: ‘The effect of Hf, Y and Zr additions on the oxidation behaviour of Ni-based Inconel 601 at high temperature’Han'guk Pusik Hakhoechi199524124–133.
12.
MaragoudakisN.TsipasD. and Eggonopoulos-PapadopoulosV.: ‘The role of reactive elements on scale adherence in high-temperature oxidation behaviour of metals and alloys’Rom. J. Phys.200449245–250.
13.
IshiiK.KohnoM.IshikawaS. and SatohS.: ‘Effect of Ti, Zr and Hf on high-temperature oxidation resistance of Fe–20Cr–5Al–0·1La alloy foils’Mater. Trans. JIM199839, 1040-1045.
14.
AmanoT.OzawaT.KudoK.MatsumotoN.SakaiN. and IsobeH.: ‘High-temperature oxidation of heat-resistant iron alloy containing small amounts of S and Y or Hf for 1800ks at 1373 K’J. Adv. Sci.20011364–65.
15.
ChunmeiX.GuoJ. and YangF.: ‘High-temperature oxidation behaviour of NiAl–28Cr–5Mo–1Hf alloy’Jinshu Xuebao200137857–860.
16.
WangZ.ZhouL.GuoJ.LiangY. and HuZ.: ‘High temperature oxidation behaviour of directional solidification NiAl–28Cr–5·94Mo–0·05Hf–0·01Ho eutectic alloy’Cailiao Yanjiu Xuebao201024585–591.
17.
GuoH.SunL.LiH. and GongS.: ‘High temperature oxidation behaviour of hafnium modified NiAl bond coat in EB-PVD thermal barrier coating system’Thin Solid Films2008516, 5732-5735.
18.
SongP.LuJ.ZhangD.LuJ. and LiD.: ‘Effect of La and Hf dopant on the high temperature oxidation of CoNiCrAl alloys’Jinshu Xuebao201147655–662.
19.
BerthodP.: ‘Kinetics of high temperature oxidation and chromia volatilization for a binary Ni–Cr alloy’Oxid. Met.200564235–252.
20.
BerthodP.: ‘Thermogravimetric study of oxide spallation for chromium-rich cast cobalt-based and iron based alloys oxidized at high temperature’Open Corros. J.2009261–70.
21.
BerthodP.: ‘Oxidation start detection on heating parts of thermogravimetry curves for high temperature alloys based on nickel, cobalt or iron’Open Corros. J.201141–8.
22.
BerthodP.: ‘Influence of the base element and of the carbides’ density on the high temperature oxidation of M–30Cr–xC alloys (M = Co, Ni, Fe). Part I: Parabolic and Cr2O3-volatilization kinetic constants’, Ann. Chim. Sci. Mater.200833225–245.
23.
BerthodP.BernardJ. L. and LiébautC.: ‘Cobalt–chromium alloy for spinner cups in manufacture of mineral wool from silicate glass’International Patent WO20010904292001.