Comparison of ASME K IR curve and dynamic master curve in determining ductile–brittle transition temperature of A48P2 steel

The ductile–brittle transition temperature (DBTT) of grade A48P2 steel is characterised based on the American Society of Mechanical Engineers (ASME) fracture toughness K _IR curve and dynamic master curve approaches. The indexing parameter for the K _IR curve, reference temperature RT_NDT, is determined from drop weight and Charpy tests to be −45°C. The dynamic master curve is constructed following ASTM standard E1921 guidelines; however, instead of precracked tests, the dynamic fracture toughness K _Jd is determined from Charpy V notch tests using a modified Schindler's procedure. A Weibull plot is constructed using the K _Jd data, and it is found that the points comply reasonably with the forced fit line of slope 4. The reference temperature for constructing the dynamic master curve, termed T^dy,Sch₀, thus determined is −56°C. The ASME K _IR curve is shown to be conservative compared with the dynamic master curve constructed using T^dy,Sch₀.