Partially melted zone in Al–Mg–Si alloy gas tungsten arc welds: Effect of techniques and prior thermal temper

Abstract

Influence of prior thermal temper and welding techniques on microstructure changes in the partially melted zone (PMZ) of AA6061 alloy gas tungsten arc (GTA) welds was investigated. Welds of AA6061 in naturally aged (T4) and artificially aged (T6) thermal tempers were made by continuous current (CC) and pulsed current (PC) techniques of GTA welding. Optical, scanning electron microscopy and microhardness testing were carried out to study the PMZ in welds. Susceptibility to liquation was high in the T6 temper as compared to the T4 temper and was attributed to a greater amount of silicon rich eutectic at the grain boundaries of PMZ. The PC technique was found to improve the resistance to susceptibility to liquation in the PMZ of AA6061 alloy GTA welds and was due to the possible reduction in the peak temperature.

Keywords

PARTIALLY MELTED ZONE PRIOR THERMAL TEMPER LIQUATION AL ALLOY GTA WELDS

Get full access to this article

View all access options for this article.

References

Kou

: ‘Welding metallurgy’, 2nd edn; 2003, New York, Wiley.

Allen

C. M.

, O'Reilly

K. A. Q.

, Cantor

and Evans

P. V.

: Frog. Mater. Sei.,1998, 43,89–170.

Mondolfo

L. F.

: ‘Aluminium alloys: structure and properties’; 1976, London, Butterworths.

Starke

E. A.

Jr : in ‘Contemporary research and applications, 35; 1989, New York, Academic Press.

Huang

and Kou

: Weld. 1, 2000, 79, 113s-120s.

Huang

and Kou

: Weld. 1, 2002, 81, 211s-222s.

Huang

and Kou

: Weld. J., 2001, 80, 46s–53s.

Huang

and Kou

: Weld. J., 2001, 80, 9s–17s.

Garland

J. G.

: Met. Constr. Br. Weld. J., 1987, 6, 121–127.

10.

Reddy

G. M.

: J. Mater. Sci., 1997, 32, 4117–4124.

11.

Yamamoto

: Weld Int., 1993,7, 456–467.

12.

Janaki Ram

G. D.

: Pract. Metall., 2000, 37, 276–284.

13.

Madhusudana Reddy

: ‘Welding of Al-Li alloys’, PhD thesis, Indian Institute of Technology (Madras), 1998, 323–328.

14.

Arthur

J. B.

: Weld J., 1955, 34, 558s–569s.

15.

Collins

F. R.

: Weld. J., 1962, 41, 337s–345s.

16.

Schillinger

D. E.

, Betz

I. G.

, Hussey

F. W.

and Markus

: Weld. J., 1963, 42, 269–275.

17.

Fish

R. E.

and Shira

C. S.

: Weld. J., 1966, 45, 490–496.

18.

Dudas

J. H.

and Collins

F. R.

: Weld J., 1966, 45, 241s–249s.

19.

Metzger

G. E.

: Weld J., 1967, 46, 457s–469s.

20.

Steenbergen

J. E.

and Thorton

H. R.

: Weld. J., 1970, 49, 61s–68s.

21.

Gittos

N. F.

and Scott

M. H.

: Weld J., 1981, 60, 95s–103s.

22.

Katoh

and Kerr

H. W.

: Weld J., 1987, 66, 360s–368s.

23.

Kerr

H. W.

and Katoh

: Weld J., 1987, 66, 251s–259s.

24.

Miyazaki

, Nishio

, Katoh

, Mukae

and Kerr

H. W.

: Weld. J., 1990, 69, 362s–371s.

25.

Koteswara

S. R.

rao, Reddy

G. M.

, Kamaraj

and Prasad Rao

: Proc. National Aerospace Manufacturing Seminar, NAMS, Trivandrum, India, June 2003.

26.

Ravi Vishnu

: Weld. World., 1995, 35, 214–223.

27.

Darward

R. C.

: Metall. Trans., 1973, 4, 508.

28.

Guitterez

L. A.

, Neye

and Zschech

: Weld 1, 1996, 75,115s-121s.

29.

Graberg

, Bratland

D. H.

, O. Grong and O. Reiso: Mater. Set Forum, 2002, 396–402, 1329-1334.

30.

Miao

W. F.

and Laughlin

D. E.

: Metall. Mater. Trans. A, 2000, 31A, 361–369.

31.

Caylon

and Buffat

P. A.

: Acta Mater., 2000, 48, 2639–2653.

32.

Wolverton

: Acta Mater., 2001, 49, 3129–3142.

33.

Malin

: Weld J., 1995, 74, 305.

34.

Kou

and Le

: Weld J., 1985, 64, 51–55.