Synthesis and some properties of Ti 3 SiC 2 by hot pressing of Ti,Si and C powders Part 2 – Mechanical and other properties of Ti 3 SiC 2

Some properties of the remarkable Ti₃SiC₂ based ceramic synthesised by hot pressing of elemental Ti, Si, and C powders have been investigated. Its flexural strength by using three point bending tests and fracture toughness by using single edge notched beam tests were measured at room temperature to be in the range 310–427 MPa and about 7·MPa m^1/2, respectively. This material is a relative ‘soft’ ceramic with a low hardness of 4 GPa. Ti₃SiC₂ is similar to the soft metals and is a damage tolerant material that is able to contain the extent of microdamage. An oxidation test has been performed in the temperature range 1000–1400°C in air for 20 h. The oxidation resistance below 1100°C was good. Two oxidized layers were formed, the outer layer consisting of pure rutile-type TiO₂, and the inner layer a mixture of SiO₂ and TiO₂. The average coefficient of thermal expansion (CTE) of Ti₃SiC₂ was measured to be 9·29 × 10⁻⁶ K⁻¹ in the temperature range 25–1400°C. The thermal shock resistance of Ti₃SiC₂ was evaluated by quenching the samples from 800°C, 1200°C, and 1400°C, respectively. The retained flexural strength drops dramatically at quenching temperature, but shows a slight increase after quenching from 1400°C compared with quenching from 800°C and 1200°C.