Although a transition from transgranular to intergranular fracture occurs and the tempered bainite microstructure evolves during creep exposure, new relationships allow rationalisation and extrapolation of the multibatch creep data sets reported for 1Cr–1Mo–0·25V steel. Specifically, analyses of results from tests lasting only up to 5000 h accurately predict the minimum creep rates, the times to various strains and the creep lives for stress–temperature conditions causing failure in 100 000 h and more. Validation of this new methodology would therefore offer the prospect of cost effective acquisition of long term creep design data.
YagiK.: in ‘Creep and fracture in high temperature components-design and life assessment issues’, (ed.ShibliI. A.et al), 31-45; 2005, London, DEStech Publ. Inc.
2.
EnnisP. J.: in ‘Creep and fracture in high temperature components-design and life assessment issues’, (ed.ShibliI. A.et al), 279-287; 2005, London, DEStech Publ. Inc.
3.
BrearJ. M.: in ‘Creep and fracture in high temperature components-design and life assessment issues’, (ed.ShibliI. A.et al), 394-405; 2005, London, DEStech Publ. Inc.
4.
BendickW. and GabrelJ.: in ‘Creep and fracture in high temperature components - design and life assessment issues’, (ed.ShibliI. A. et al), 406-418; 2005, London, DEStech Publ. Inc.
5.
MasuyamaF.: in ‘Creep and fracture in high temperature components-design and life assessment issues’, (ed.ShibliI. A.et al), 983-996; 2005, London, DEStech Publ. Inc.
6.
KimuraK.: in ‘Creep and fracture in high temperature components-design and life assessment issues’, (ed.ShibliI. A.et al), 1009-1022; 2005, London, DEStech Publ. Inc.
7.
MercklingG.: in ‘Creep and fracture in high temperature components - design and life assessment issues’, (ed.ShibliI. A.et al), 3-11; 2005, London, DEStech Publ. Inc.
8.
HoldsworthS. R., AskinsM., BakerA., GariboldiE., HolmstromS., KlenkA., RingelM., MercklingG., SandstromR., SchwienheerM. and SpigarelliS.: in ‘Creep and fracture in high temperature components - design and life assessment issues’, (ed.ShibliI. A. et al), 380-393; 2005, London, DEStech Publ. Inc.
9.
CipollaL. and GabrelJ.: in ‘Super-high strength steels’; 2005, Rome, Associazione Italia di Metallurgia, on CD-ROM.
10.
Di GianfrancescoA., CipollaL., CirilliF., CuminoG. and CaminadaS.: in ‘Super-high strength steels’; 2005, Rome, Associazione Italia di Metallurgia, on CD-ROM.
11.
EvansR. W., ParkerJ. D. and WilshireB.: in ‘Recent advances in creep and fracture of engineering materials and structures’, 135-184; 1982, Swansea, Pineridge Press.
12.
EvansR. W. and WilshireB.: ‘Creep of metals and alloys’, 1985, London, The Institute of Metals.
13.
EvansR. W. and WilshireB.: ‘Introduction to creep’; 1993, London, The Institute of Materials.
14.
EvansR. W.: Proc. Roy. Soc. A, 2000, 456A, 835–868
15.
EvansR. W. and WilshireB.: in ‘Unified constitutive laws of plastic deformation’ (ed.KrauszA. S. and KrauszK.), 107-152; 1996, London, Academic Press.
16.
WilshireB. and BattenboughA. J.: Mater. Sci. Eng. A, 2007, A443, 156–166.
17.
WilshireB., BurtH. and LaveryN.: Mater. Sci Forum, 2006, 519, 1041–1046.
18.
WilshireB. and ScharningP. J.: Scr. Mater., 2007, 56, 701–704.
19.
WilshireB. and ScharningP. J.: Scr. Mater., 2007, 56, 1023–1026.
20.
Creep DataNIMSSheet No. 9b: Data sheets on the elevated temperature properties of 1Cr-lMo-0•25V steel forgings for turbine rotors and shafts (ASTM A470-8), 1990.
KimuraK.: in ‘Creep deformation and fracture, design and life extension’, (ed.MishraR. S.et al.), 97-106; 2005, Pittsburg, MST.
24.
LarsonF. R. and MillerJ.: Trans. ASME, 1952, 74, 765–775.
25.
MansonS. S. and HaferdA. M.: NASA TN2890, 1953.
26.
OrrR. L., SherbyO. D. and DornJ. E.: Trans. ASM, 1954, 46, 113–128.
27.
WilliamsK. R. and WilshireB.: Metal. Sci. J., 1973, 7, 176–179.
28.
EvansR. W., WillisM. R., WilshireB., HoldsworthS. R., SeniorB., FlemingA., SpindlerM. and WilliamsJ. A.: Proc. 5th Int. Conf. on ‘Creep and fracture of engineering materials and structures’, (ed.WilshireB. and EvansR. W.), 633-640; 1993, London, The Institute of Materials.
29.
MatsuoT., KimuraK., TanakaR. and KikuchiM.: Proc. 4th Int. Conf. on ‘Creep and fracture of engineering materials and structures’, (ed.WilshireB. and EvansR. W.), 477-486; 1990, London, The Institute of Metals.
30.
MatsuoT., KimuraK., OhiH. and KikuchiM.: Proc. 4th Int. Conf. on ‘Creep and fracture of engineering materials and structures’, (ed.WilshireB. and EvansR. W.), 487-496; 1990, London, The Institute of Metals.
31.
MishraR. S., MukherjeeA. K. and MurtyK. L. (eds.): ‘Creep behaviour of advanced materials for the 21st century’, 391–507; 1999, Warrendale, PA, TMS.
32.
AshbyM. F. and DysonB. F.: in ‘Advances in fracture research’, (ed.ValluriS. R.), 3-30; 1984, Oxford, Pergamon Press.
33.
LeckieF. A. and HayhurstD. R.: Acta Metall., 1977, 25, 1059–1070.
34.
WilshireB. and BurtH.: in ‘Creep and fracture in high temperature components - design and life assessment issues’, (ed.ShibliI. A..), 191-200; 2005, London, DEStech Publ. Inc.
35.
‘ASME boiler and pressure vessel code’, Section II, Part D, Appendix I, 789; 2004, New York, ASME.