Effect of electric contact surface treatment on microstructure and wear behaviour of ductile iron

A study of electric contact surface treatment to ductile iron has been carried out. This technology was based on the application of the contact resistance heating between the electrode and workpiece. For comparison, the experiments of induction hardening to ductile iron were studied. The microstructure, microhardness, surface residual stress and wear properties were investigated using optical microscope, scanning electron microscope, X-ray diffraction, Vickers microhardness and rolling contact wear tests. Electric contact surface treatment resulted in the formation of fine ledeburite (white bright layer) and martensite in the ductile iron surface, in which the hardness in these areas was higher than that of induction hardened surface. The wear test results showed that the ductile iron surface after electric contact surface treatment had better wear resistance owing to the fine microstructure, high hardness and residual compressive stress.