Lamellar structures of Ti–46Al–0·5W–0·5Si (at-) alloy solidifying through the primary α phase were successfully aligned parallel to the growth direction using a self-seeding technology in a Bridgman type directional solidification furnace. At the growth rate of 20 μm s−1 and temperature gradient of 12·1 K mm−1, the α phase grows along the
direction. Therefore, the parallel lamellar structures, whose lamellar orientation is
direction, can grow continuously until the end of solidification under these solidification parameters. The original lamellar structures of the unmelted region parallel to the growth direction and suitable solidification parameters are necessary for TiAl alloys solidifying through the primary α phase to control the lamellar orientation. The self-seeding technology gets rid of the cutting and fixing of seeds and simplifies the processing of controlling the lamellar orientation of TiAl alloys. It can promote the engineering applications of the lamellar orientation control of TiAl alloys.
WuX.: ‘Review of alloy and process development of TiAl alloys’, Intermetallics, 2006, 14, 1114–1122.
2.
ClemensH. and KestlerH.: ‘Processing and applications of intermetallic γ-TiAl-based alloys’, Adv. Eng. Mater., 2000, 2, 551–570.
3.
DimidukD. M.: ‘Gamma titanium aluminide alloys – an assessment within the competition of aerospace structural materials’, Mater. Sci. Eng. A, 1999, A263, 281–288.
4.
JohnsonD. R., InuiH. and YamaguchiM.: ‘Directional solidification and microstructural control of the TiAl/Ti3Al lamellar microstructure in TiAl–Si alloys’, Acta Mater., 1996, 44, 2523–2535.
5.
LeeH. N., JohnsonD. R., InuiH., OhM. H., WeeD. M. and YamaguchiM.: ‘A composition window in the TiAl–Mo–Si system suitable for lamellar structure control through seeding and directional solidification’, Mater. Sci. Eng. A, 2002, A329–A331, 19–24.
6.
KimS. E., LeeY. T., OhM. H., InuiH. and YamaguchiM.: ‘Directional solidification of TiAl–Si alloys using a polycrystalline seed’, Intermetallics, 2000, 8, 399–405.
7.
JohnsonD. R., InuiH., MutoS., OmiyaY. and YamanakaT.: ‘Microstructural development during directional solidification of α-seed TiAl alloys’, Acta Mater., 2006, 54, 1077–1085.
8.
FuH., GuoJ., SuY., XuD. and LiJ.: ‘Directional solidification and lamellar orientation control of TiAl intermetallics’, Chin. J. Nonferr. Met., 2003, 13, 797–910.
9.
LeeH. N., JohnsonD. R., InuiH., OhM. H., WeeD. M. and YamaguchiM.: ‘Microstructure control though seeding and directional solidification of TiAl alloys containing Mo and C’, Acta Mater., 2000, 48, 3221–3233.
10.
YamaguchiM., JohnsonD. R., LeeH. N. and InuiH.: ‘Directional solidification of TiAl-based alloys’, Intermetallics, 2000, 8, 511–517.
11.
JohnsonD. R., InuiH. and YamaguchiM.: ‘Directional solidification and microstructural control of the TiAl/Ti3Al lamellar microstructure in TiAl–Si alloys’, Acta Mater., 1996, 44, 2523–2535.
12.
LuoW., ShenJ., MinZ. and FuH.: ‘Lamellar orientation control of TiAl alloys under high temperature gradient with Ti–43Al–3Si seed’, J. Cryst. Growth, 2008, 310, 5441–5446.
13.
JohnsonD. R., MasudaY., InuiH. and YamaguchiM.: ‘Alignment of the TiAl/Ti3Al lamellar microstructure in TiAl alloys by growth from a seed material’, Acta Mater., 1997, 45, 2523–2533.
14.
JohnsonD. R., MasudaY., InuiH. and YamaguchiM.: ‘Alignment of the TiAl/Ti3Al lamellar microstructure in TiAl alloys by directional solidification’, Mater. Sci. Eng. A, 1997, A239–A240, 577–583.
15.
KimJ. H., KimS. W., LeeH. N., OhM. H., InuiH. and WeeD. M.: ‘Effects of Si and C additions on the thermal stability of directionally solidification TiAl–Nb alloys’, Intermetallics, 2005, 13, 1038–1047.
16.
LeeH. N., JohnsonD. R., HnuiH., OhM. H., WeeD. M. and YamaguchiM.: ‘Directional solidification and creep deformation of a Ti–46Al–1·5Mo–0·2C (at) alloy’, Intermetallics, 2002, 10, 841–850.
17.
DingX. F., LinJ. P., ZhangL. Q., SuY. Q., WangH. L. and ChenG. L.: ‘Lamellar orientation control in a Ti–46Al–5Nb alloy by directional solidification’, Scr. Mater., 2011, 65, 61–64.
18.
LapinJ., OndrúšL. and NazmyM.: ‘Directional solidification of intermetallic Ti–46Al–2W–0·5Si alloy in alumina moulds’, Intermetallics, 2002, 10, 1019–1031.
19.
FanJ., LiX., SuY., ChenR., GuoJ. and FuH.: ‘Microstructure evolution of directionally solidified Ti–46Al–0·5W–0·5Si alloy’, J. Cryst. Growth, 2011, 337, 52–59.
20.
FanJ., LiX., SuY., GuoJ. and FuH.: ‘The microstructure parameters and microhardness of directionally solidified Ti–43Al–3Si alloy’, J. Alloys Compd, 2010, 506, 593–599.
21.
FanJ., LiX., SuY., ChenR., GuoJ. and FuH.: ‘Dependency of microstructure parameters and microhardness on the temperature gradient for directionally solidified Ti–49Al alloy’, Mater. Chem. Phys., 2011, 130, 1232–1238.
22.
JungI. S., KimM. C., LeeJ. H., OhM. H. and WeeD. M.: ‘High temperature phase equilibria near Ti–50atAl composition in Ti–Al system studied by directional solidification’, Intermetallics, 1999, 7, 1247–1253.
23.
LiX., FanJ., SuY., LiuD., GuoJ. and FuH.: ‘Lamellar orientation and growth direction of α phase in directionally solidified Ti–46Al–0·5W–0·5Si alloy’, Intermetallics, 2012, 27, 38–45.
direction. Therefore, the parallel lamellar structures, whose lamellar orientation is 
direction, can grow continuously until the end of solidification under these solidification parameters. The original lamellar structures of the unmelted region parallel to the growth direction and suitable solidification parameters are necessary for TiAl alloys solidifying through the primary α phase to control the lamellar orientation. The self-seeding technology gets rid of the cutting and fixing of seeds and simplifies the processing of controlling the lamellar orientation of TiAl alloys. It can promote the engineering applications of the lamellar orientation control of TiAl alloys.