Effects of melt superheat treatment on microstructure and wear behaviours of hypereutectic Al

Abstract

In the present study, the effects of melt superheat treatment on the microstructural evolution and wear behaviours of hypereutectic Al–20Si alloy were investigated. The morphology of primary and eutectic Si phase was analysed by optical microscopy (OM) and scanning electron microscopy (SEM). The results of OM and SEM reveal that increasing the melt superheat temperature can significantly refine the primary and eutectic Si of hypereutectic Al–20Si alloy. The average size of primary Si was reduced from 94 to 47 μm, and its morphology was transformed from coarse and irregular shape to fine blocky shape or particles, while the eutectic Si was modified into fine fibrous structure. The differential scanning calorimeter curves show an exothermic reaction happens when the melt temperature arrives at 940·5°C, and the exothermic peak is at 951°C. Friction and wear tests show that the friction coefficient and specific wear rate of Al–20Si alloy gradually decrease with increasing melt superheat treatment temperature. In addition, the wear mechanism of hypereutectic Al–20Si alloy before and after refining the primary and eutectic Si phase was also discussed.

Keywords

Hypereutectic Al–20Si alloy Melt superheat treatment Primary Si Eutectic Si Wear behaviours

Get full access to this article

View all access options for this article.

References

Q. L.

, Xia

T. D.

, Lan

Y. F.

, Zhao

W. J.

, Fan

and Li

P. F.

: ‘Effect of rare earth cerium addition on the microstructure and tensile properties of hypereutectic Al–20Si alloy’, J. Alloys Compd , 2013, 562, 25–32.

Mohamed

A. M. A.

, Samuel

A. M.

, Samuel

F. H.

and Doty

H. W.

: ‘Influence of additives on the impact toughness of Al–10·8Si near-eutectic cast alloys’, Mater. Des. , 2009, 30, 3943–3957.

Choi

H. S.

and Li

X. C.

: ‘Refinement of primary Si and modification of eutectic Si for enhanced ductility of hypereutectic Al–20Si–4·5Cu alloy with addition of Al₂O₃ nanoparticles’, J. Mater. Sci. , 2012, 47, 3096–3102.

Ardakan

H. A.

, Liu

X. C.

, Ajersch

and Chen

X. G.

: ‘Wear behaviour of hypereutectic Al–Si–Cu–Mg casting alloys with variable Mg contents’, Wear , 2010, 269, 684–692.

Chandrashekharaiah

T. M.

and Kori

S. A.

: ’Effect of grain refinement and modification on the dry sliding wear behaviour of eutectic Al–Si alloys’, Tribol. Int. , 2009, 42, 59–65.

Shi

W. X.

, Gao

, Tu

G. F.

, Li

S. W.

, Hao

and Yu

F. X.

: ‘Effect of neodymium on primary silicon and mechanical properties of hypereutectic Al–15Si alloy’, J. Rare Earths , 2010, 28, 367–370.

Fatih Kilicaslana

, Lee

W. R.

, Lee

T. H.

, Sohn

and Hong

S. J.

: ‘Effect of Sc addition on the microstructure and mechanical properties of as-atomized and extruded Al–20Si alloys’, Mater. Lett. , 2012, 71, 164–167.

Q. L.

, Xia

T. D.

, Lan

Y. F.

, Zhao

W. J.

, Fan

and Li

P. F.

: ‘Effect of in-situ γ-Al₂O₃ particles on the microstructure of hypereutectic Al–20Si alloy’, J. Alloys Compd , 2013, 577, 232–236.

Dahle

A. K.

, Nogita

, McDonald

S. D.

, Dinnis

and Lu

: ‘Eutectic modification and microstructure development in Al–Si alloys’, Mater. Sci. Eng. A , 2005, A413–A414, 243–248.

10.

D. H.

, Jiang

Y. H.

, Guan

G. S.

, Zhou

R. F.

, Li

Z. H.

and Zhou

: ‘Refinement of primary Si in hypereutectic Al–Si alloy by electromagnetic stirring’, J. Mater. Process. Technol. , 2007, 189, 13–18.

11.

Uzun

, Karaaslan

, Gogebakan

and Keskin

: ‘Hardness and microstructural characteristics of rapidly solidified Al–8–16wt-Si alloys’, J. Alloys Compd , 2004, 376, 149–157.

12.

Jung

H. K.

, Seo

P. K.

and Kang

C. G.

: ‘Microstructural characteristics and mechanical properties of hypo-eutectic and hyper-eutectic Al–Si alloys in semi-solid forming process’, J. Mater. Process. Technol. , 2001, 113, 568–573.

13.

Chen

Z. W.

, Jie

W. Q.

and Zhang

R. J.

: ‘Superheat treatment of Al–7Si–0·55Mg alloy melt’, Mater. Lett. , 2005, 59, 2183–2185.

14.

Sun

Y. J.

, Wang

Q. L.

and Geng

H. R.

: ‘Effects of complex modificating technique on microstructure and mechanical properties of hypereutectic Al–Si alloys’, J. Mater. Sci. , 2012, 47, 2104–2109.

15.

Bian

X. F.

and Wang

: ‘Thermal-rate treatment and structure transformation of Al–13Si alloy melt’, Mater. Lett. , 2000, 44, 54–58.

16.

Zha

, Wang

H. Y.

, Liu

, Zhao

, Liang

M. L.

, Li

and Jiang

Q. C.

: ‘Influence of melt superheating on microstructures of Mg–3·5Si–1Al alloys’, Trans. Nonferrous Met. Soc. China , 2008, 18, s107–s112.

17.

Haquea

M. M.

and Ismail

A. F.

: ‘Effect of superheating temperatures on microstructure and properties of strontium modified aluminium–silicon eutectic alloy’, J. Mater. Process. Technol. , 2005, 162–163, 312–316.

18.

Wang

, He

S. X.

, Sun

B. D.

, Guo

Q. X.

and Nishio

: ‘Grain refinement of Al–Si alloy (A356) by melt thermal treatment’, J. Mater. Process. Technol. , 2003, 141, 29–34.

19.

P. J.

, Nikitin

V. I.

, Knadalova

E. G.

and Nikitin

K. V.

: ’Effect of melt overheating, cooling and solidification rates on Al–16wt-Si alloy structure’, Mater. Sci. Eng. A , 2002, A332, 371–374.

20.

Dwivedi

D. K.

: ‘Adhesive wear behaviour of cast aluminium–silicon alloys: overview’, Mater. Des. , 2010, 31, 2517–2531.

21.

Kori

S. A.

and Chandrashekharaiah

T. M.

: ‘Studies on the dry sliding wear behaviour of hypoeutectic and eutectic Al–Si alloys’, Wear , 2007, 263, 745–755.

22.

Xing

P. F.

, Gao

, Zhuang

Y. X.

, Liu

K. H.

and Tu

G. F.

: ‘Effect of erbium on properties and microstructure of Al–Si eutectic alloy’, J. Rare Earths , 2010, 28, (6), 927–930.

23.

Dwivedi

D. K.

, Arjun

T. S.

, Thakur

, Vaidya

and Singh

: ‘Sliding wear and friction behaviour of Al–18Si–0·5Mg alloy’, J. Mater. Process. Technol. , 2004, 152, 323–328.

Effects of melt superheat treatment on microstructure and wear behaviours of hypereutectic Al–20Si alloy

Abstract

Keywords

Get full access to this article

References