Mechanical, electrochemical and magnetic properties of duplex stainless steel were analysed to evaluate its use as biomaterial, comparing the results with those obtained for austenitic stainless steel. Yield and ultimate tensile strengths are almost twice in duplex stainless steel, being the values 870 MPa and 564 MPa, respectively. The electrochemical test revealed that this material has lower susceptibility to localised corrosion because of its greater passive range, 1 V from the open circuit potential, while the austenitic stainless steel exhibited a passive region of 0.370 V. Both steels behave as soft magnetic materials, however, duplex stainless steel has higher magnetic saturation and remanence, while austenitic stainless steel is more prone to heating when exposed to a magnetic field.
FrakerA. C.: ‘Corrosion of metallic implants and prosthetic devices’, in ‘ASM handbook’, (ed. DavisJ. R.., ‘Corrosion’Vol. 13. 9th edn, 1324–1335; 1992, Materials Park, OH, ASM International.
2.
GurappaI.: ‘Characterization of different materials for corrosion resistance under simulated body fluid conditions’, Mater. Character., 2002, 49, 73–79. doi: 10.1016/S1044-5803(02)00320-0
3.
ManivasagamG., DhinasekaranD. and RajamanickamA.: ‘Biomedical implants: corrosion and its prevention – a review’, Recent Pat. Corros. Sci., 2010, 2, 40–54. doi: 10.2174/1877610801002010040
4.
DavisonR. M.: ‘Corrosion of stainless steels’, in ‘ASM handbook’, (ed. DavisJ. R.., ‘Corrosion’Vol. 13. 9th edn, 1327–1381; 2004, Materials Park, OH, ASM International.
5.
Vander VoortG. F.: ‘Service characteristics of carbon and low-steels alloy’, in ‘ASM handbook’, (eds. LampmanS. R. and ZorcT. B.., ‘Properties and selection: irons, steels and high performance alloys’Vol. 1. 10th edn, 1058–1133; 2005, Materials Park, OH, ASM International.
NilssonJ. O. and WilsonA.: ‘Influence of isothermal phase transformation on toughness and pitting corrosion of super duplex stainless steel SAF2507’, Mater. Sci. Technol., 1993, 9, (7), 545–554. doi: 10.1179/mst.1993.9.7.545
8.
NiinomiM.: ‘Recent metallic materials for biomedical applications’, Metall. Mater. Trans. A, 2002, 33A, 477–485. doi: 10.1007/s11661-002-0109-2
9.
ShettlemoreM. G. and BundyK. J.: ‘Examination of in vivo influences on bioluminescent microbial assessment of corrosion product toxicity’, Biomaterials, 2001, 22, 2215–2228. doi: 10.1016/S0142-9612(00)00410-5
10.
TairaM., ToguchiM. S., HamadaY., TakahashiJ., ItouR., ToyosawaS., IjyuinN. and OkazakiM.: ‘Studies on cytotoxic effect of nickel ions on three cultured fibroblast’, J. Mater. Sci.: Mater. Med., 2001, 12, 373–376.
11.
SumitaM., HanawaT. and TeoS. H.: ‘Development of nitrogen-containing nickel-free austenitic stainless steels for metallic biomaterials – review’, Mater. Sci. Eng. C, 2004, C24, 753–760. doi: 10.1016/j.msec.2004.08.030
12.
SargeantA. and GoswamiT.: ‘Hip implants – paper VI – ion concentrations’, Mater. Des., 2007, 28, 155–171. doi: 10.1016/j.matdes.2005.05.018
13.
LüX., BaoX., HuangY., QuY., LuH. and LuZ.: ‘Mechanisms of cytotoxicity of nickel ions based on gene expression profiles’, Biomaterials, 2009, 30, 141–148. doi: 10.1016/j.biomaterials.2008.09.011
14.
YangK. and RenY.: ‘Nickel-free austenitic stainless steels for medical applications’, Sci. Technol. Adv. Mater., 2010, 11, 1–13. doi: 10.1088/1468-6996/11/1/014105
15.
CigadaA., RondelliG., VicentiniB., GiacomazziM. and RoosA.: ‘Dúplex stainless steel for osteosynthesis devices’, J. Biomed. Mater. Res., 1989, 23, 1087–1095. doi: 10.1002/jbm.820230908
16.
CigadaA., De SantisG., GattiM. A., RoosA. and ZaffeD.: ‘In vivo behavior of a high performance dúplex stainless steel’, J. Appl. Biomater., 1993, 4, 39–46. doi: 10.1002/jab.770040105
17.
PanJ., KarlénC. and UlfvinC.: ‘Electrochemical study of resistance to localizad corrosion of stainless steel for biomedical applications’, J. Eletrochem. Soc., 2000, 147, 1021–1025. doi: 10.1149/1.1393307
18.
BelotiM. M., RolloJ. M. D. A., Itman FilhoA. and RosaA. L.: ‘In vitro biocompatibility of dúplex stainless steel with and without 0.2 niobium’, J. Appl. Biomater. Biomech., 2004, 2, 162–168.
19.
OhK., KimY., ParkY. and KimK.: ‘Properties of super stainless steels for orthodontic applications’, J. Biomed. Mater. Res. B, 2004, 69B, 183–194. doi: 10.1002/jbm.b.30002
20.
KocijanA. and ConradiM.: ‘The corrosion behaviour of austenitic and duplex stainless steels in artificial body fluids’, Mater. Technol., 2010, 44, 21–24.
21.
PlattJ. A., GuzmanA., ZuccariA., ThornburgD. W., RhodesB. F., OshidaY. and MooreB. K.: ‘Corrosion behavior of 2205 duplex stainless steel’, Am. J. Orthod. Dentofacial Orthop., 1997, 112, 69–79. doi: 10.1016/S0889-5406(97)70276-2
22.
‘Handbook of materials for medical devices’, (ed. DavisJ. R.., Chap. 3, 21–50; 2003, Materials Park, OH, ASM International.
23.
BrunskiJ. B.: ‘Biomaterials science – an introduction to materials in medicine’, (ed. RatnerB. D., ,). 2nd edn, 137–153; 2004, San Diego, CA, Elsevier Academic Press.
24.
DouthettJ.: ‘Heat treating of stainless steels’, in ‘ASM handbook’, (eds. LampmanS. R. and ZorcT. B.., ‘Heat treating’Vol. 4. 9th edn, 1682–1757; 1991, Materials Park, OH, ASM International.
25.
OkamotoH. and BakerH.: ‘Metals handbook’, ‘Alloy phase diagrams’Vol. 3. 8th edn, 682; 1992, Materials Park, OH, ASM International.
26.
VillanuevaD. M. E., JuniorF. C. P., PlautR. L. and PadillaA. F.: ‘Comparative study on sigma phase precipitation of three types of stainless steels: austenitic, superferritic and duplex’, Mater. Sci. Technol., 2006, 22, (9), 1098–1104. doi: 10.1179/174328406X109230
27.
SudhakarK. V.: ‘Metallurgical investigation of a failure in 316L stainless steel orthopaedic implant’, Eng. Fail. Anal., 2005, 12, 249–256. doi: 10.1016/j.engfailanal.2004.05.004
28.
PohlerO. E. M.: ‘Failures of metallic orthopedic implants’, in ‘Metals handbook’, (eds. BeckerW. T. and ShipleyR. J.., ‘Failure analysis and prevention’Vol. 11, 2746–2749; 2002, Materials Park, OH, ASM International.
29.
TeohS. H.: ‘Fatigue in biomaterials: a review’, Inter. J. Fatigue, 2000, 22, 825–837. doi: 10.1016/S0142-1123(00)00052-9
30.
SieurinH.: ‘Fracture toughnessproperties of duplex stainless steels’, 12–20; PhD thesis, Royal Institute of Technology, Stockholm, Sweden2006.
31.
JohanssonR.: ‘Fatigue and fracture properties of duplex stainless steels’, in ‘ASM handbook’, (ed. LampmanS.., ‘Fatigue and fracture’Vol. 19, 757–768; 1996, Materials Park, OH, ASM International.
32.
EbaraR.: ‘Corrosion fatigue crack initiation behavior of stainless steels’, Proc. Eng., 2010, 2, 1297–1306. doi: 10.1016/j.proeng.2010.03.141
33.
PerrenR. A., SuterT., SolenthalerC., GulloG., UggowitzerP. J., BöhniH. and SpeidelM. O.: ‘Corrosion resistance of super duplex stainless steels in chloride ion containing environments: investigations by means of a new microelectrochemical method. II: influence of precipitates’, Corros. Sci., 2001, 43, 727–745. doi: 10.1016/S0010-938X(00)00088-3
34.
AhnY. S., KimJ. M. and JeongB. H.: ‘Effect of aging treatments and microstructural evolution on corrosion resistance of tungsten substituted 2205 duplex stainless steel’, Mater. Sci. Technol., 2002, 18, (4), 383–388. doi: 10.1179/026708302225001642
35.
Kamachi MudaliU., SridharT. M. and RajB.: ‘Corrosion of bio implants’, Sadhana, 2003, 28, 601–637. doi: 10.1007/BF02706450
36.
RenY., YangK., ZhangB., WangY. and LiangY.: ‘Nickel-free stainless steel for medical applications’, J. Mater. Sci. Technol., 2004, 20, 571–573.
37.
TalhaM., BeheraC. K. and SinhaO. P.: ‘Promising in vitro performances of nickel-free nitrogen containing stainless steels for orthopaedic applications’, Bull. Mater. Sci., 2014, 37, 1321–1330. doi: 10.1007/s12034-014-0078-2
38.
FrankelG. S.: ‘Pitting corrosion’, in ‘Metals handbook’, (ed. DavisJ. R.., ‘Corrosion fundamentals, testing and protection’Vol. 13A. 9th edn, 591–599; 2004, Materials Park, OH, ASM International.
39.
PerrenR. A., SuterT. A., UggowitzerP. J., WeberL., MagdowskiR., BöhniH. and SpeidelM. O.: ‘Corrosion resistance of super duplex stainless steels in chloride ion containing environments: investigations by means of a new microelectrochemical method. I: precipitation-free states’, Corros. Sci., 2001, 43, 707–726. doi: 10.1016/S0010-938X(00)00087-1
40.
DengB., JiangY., GongJ., ZhongC., GaoJ. and LiJ.: ‘Critical pitting and repassivation temperatures for duplex stainless steel in chloride solutions’, Electrochem. Acta, 2008, 53, 5220–5225. doi: 10.1016/j.electacta.2008.02.047
41.
PalmerT. A., ElmerJ. W. and BabuS. S.: ‘Observations of ferrite/austenite transformations in the heat affected zone of 2205 duplex stainless steel spot welds using time resolved X-ray diffraction’, Mater. Sci. Eng. A, 2004, A374, 307–321. doi: 10.1016/j.msea.2004.03.037
42.
Sawyer-GloverM. and ShellockF. G.: ‘Pre-MRI procedure screening: recommendations and safety considerations for biomedical implants and devices’, J. Magn. Reson. Imaging, 2000, 12, 92–106. doi: 10.1002/1522-2586(200007)12:1<92::AID-JMRI11>3.0.CO;2-7
43.
MatsuuraH., InoueT., KonnoH., SasakiM., OgasawaraK. and OgawaA.: ‘Quantification of susceptibility artifacts produced on highfield magnetic resonance images by various biomaterials used for neurosurgical implants’, J. Neurosurg., 2002, 97, 1472–1475. doi: 10.3171/jns.2002.97.6.1472
44.
StradiottiP., CurtiA., CastellazziG. and ZerbiA.: ‘Metal-related artifacts in instrumented spine. Techniques for reducing artifacts in CT and MRI: state of the art’, Eur Spine J., 2009, 18, 102–108. doi: 10.1007/s00586-009-0998-5
45.
WoodsT. O.: ‘MRI safety and compatibility of implants and medical devices’, in ‘Stainless steels for medical and surgical applications’, (eds. WintersG. L. and NuttM. J.., 82–92; 2003, Pittsburgh, PA, ASTM International.