Characterisation of fibre–polymer interactions and transcrystallinity in short keratin fibre

Abstract

Short fibre reinforced composites were made from keratin fibres obtained from poultry feathers. The matrix material was either polypropylene or a blend of polypropylene and maleic anhydride modified polypropylene (MaPP). In general, the addition of MaPP to polypropylene (PP) did not alter the tensile properties of the blend in a significant way. When not using MaPP, composites had lower breaking stresses than samples without fibres. However, MaPP at concentrations of >4 wt-% enhanced the breaking stress of the composites to above the value without fibres. Concurrent thermal analysis using differential scanning calorimetry (DSC) showed a distinct increase in the amount of transcrystallinity in the composites at MaPP concentrations greater than 4 wt-%. Scanning electron microscopy (SEM) revealed increased interactions between the protein fibres and the PP/MaPP matrix. Annealing showed that more large polymer crystals near the fibres were not enough to increase stress transfer across the interface.

Keywords

COMPOSITES POLYPROPYLENE MALEIC ANHYDRIDE DSC PROPERTIES

Get full access to this article

View all access options for this article.

References

Kuan

H. C.

, Huang

J. M.

, Ma

C. C. M.

and Wang

F. Y.

: Plast. Rubber Compos ., 2003, 32, 122–126.

Colom

, Carrasco

, Pages

and Canavate

: Compos. ScL TechnoL , 2003, 63, 161–169.

Wambua

, Ivens

and Verpoest

: Compos. Sci TechnoL , 2003, 63, 1259–1264.

Rana

A. K.

, Mandal

and Bandyopadhyay

: Compos. ScL TechnoL , 2003, 63, 801–806.

Oksman

and Clemons

: J. AppL Polym. Set , 1998, 67, 1503–1513.

Schneider

J. P.

, Myers

G. E.

, Clemons

C. M.

and English

B. W.

: J. Vinyl Addit. Technot , 1995, 1, 103–108.

Joseph

P. V.

, Joseph

, Thomas

, Pillai

C. K. S.

, Prasad

V. S.

and Groeninckx

S. M.

: Compos. A , 2003, 34A, 253–266.

Nunez

A. J.

, Kenny

J. M.

, Reboredo

M. M.

, Aranguren

M. I.

and Marcovich

M. E.

: Polym. Eng. Set , 2002, 42, 733–742.

Karmaker

A. C.

and Youngquist

J. A.

: J. Appl. Polym. Sci ., 1996, 62, 1147–1151.

10.

Bullions

T. A.

, Gillespie

R. A.

, Price-O'Brien

and Loos

A. C.

: J. AppL Polym. ScL , 2004, 92, 3771–3783.

11.

Schuster

: Proc. Conf. AutoPolymers 2005, San Diego, CA, USA, July 2003, National Science Foundation and The Luso-American Foundation (Portugal), Paper 4.

12.

Zafeiropoulos

N. E.

, Baillie

C. A.

and Matthews

F. L.

: Adv. Campos. Lett ., 2001, 10, 293–297.

13.

Chawla

K. K.

: ‘Composite materials’: 1987, New York, Springer-Verlag.

14.

Murayama-Arai

, Takahashi

, Yokote

and Akahane

: Eur. J. Bioehem ., 1983, 132, 501–507.

15.

Barone

J. R.

and Schmidt

W. F.

: Campos. Set Technot , 2005, 65, 173–181.

16.

Wang

and Hwang

L. M.

: J. Polym. Set B , 1996, 34B, 1435–1442.

17.

Gassner

, Schmidt

, Line

M. J.

, Thomas

and Water

R. M.

: US Patent 5705030, 1998.

18.

Dweib

M. A.

, Hu

, O'Donnell

, H.W. Shenton and R. P. Wool: Campos. Struct., 2004, 63, 147–157.

19.

Fraser

R. D. B.

and MacRae

T. P.

: in ‘Symposia of the society for experimental biology number XXXIV: the mechanical properties of biological materials’, (ed. Vincent

J. F. V.

and Currey

J. D.

), 211–246; 1980, Cambridge, Cambridge University Press.

20.

Kuroda

M. M. H.

and Scott

C. E.

: Polym. Campos ., 2002, 23, 395–405.

21.

Fried

J. R.

: ‘Polymer science and technology’: 1995, Englewood Cliffs, NJ, Prentice-Hall.

22.

Liu

Z. Q.

, Cunha

A. M.

, Yi

X. S.

and Bernardo

C.A.

: J. Maeromot Set Phys. B , 2001, 40B, 529–538.

23.

Barone

J. R.

: Campos. A , 2005, 36A, 1518–1524.

Characterisation of fibre–polymer interactions and transcrystallinity in short keratin fibre–polypropylene composites

Abstract

Keywords

Get full access to this article

References