Microstructure and improved hydrogen storage properties of Mg based alloy powders prepared by modified milling method

Abstract

In this study, the modified preparation method of combining planetary and vibratory ball milling was proposed to prepare Mg based hydrogen storage alloy powders. The comparison of micromorphology and hydrogen storage behaviour between Mg₂Ni prepared using the modified and conventional preparation methods were investigated experimentally. The comparison results showed that the combination of first planetary and then vibratory ball milling has more favourable effect on improving both the kinetics and the thermodynamics of ball milled Mg₂Ni alloys. The sample synthesised by first planetary milling for 40 h and then vibratory milling for 30 h has faster hydrogen absorption kinetics and lower dehydriding onset temperature than those prepared by the single method of planetary or vibratory milling and hydriding combustion synthesis owing to its popcorn-like microstructure. Moreover, this kind of modified method reduces the reaction enthalpy and activation energy by up to ∼18 and 22% respectively.

Keywords

Mechanical alloying Magnesium based hydrogen storage alloys Kinetics Thermodynamics

Get full access to this article

View all access options for this article.

References

Zhu

Y. F.

, Yang

, Wei

L. J.

, Zhao

Z. L.

and Li

L. Q.

‘Hydrogen storage properties of Mg–Ni–Fe composites prepared by hydriding combustion synthesis and mechanical milling’, J. Alloys Compd, 2012, 520, 207–212.

Schuth

‘Challenges in hydrogen storage’, Eur. Phys. J. Spec. Top., 2009, 176, 155–166.

Felderhoff

, Weidenthaler

, Von Helmolt

and Eberle

‘Hydrogen storage: the remaining scientific and technological challenges’, Phys. Chem. Chem. Phys., 2007, 9, 2643–2653.

Jain

I. P.

, Lal

and Jain

‘Hydrogen storage in Mg: a most promising material’, Int. J. Hydrogen Energy, 2010, 35, 5133–5144.

Song

M. Y.

, Kwak

Y. J.

, Lee

S. H.

and Park

H. R.

‘Hydriding and dehydriding characteristics of LiBH₄ and transition metals-added magnesium hydride’, Mater. Res. Bull., 2013, 48, 2476–2481.

Wang

Y. Q.

, Yang

F. S.

, Meng

X. Y.

, Guo

Q. F.

, Zhang

Z. X.

, Park

I. S.

, Kim

and Kim

K. J.

‘Simulation study on the reaction process based single stage metal hydride thermal compressor’, Int. J. Hydrogen Energy, 2010, 35, 321–328.

Muthukumar

and Ramana

S. V.

‘Study of heat and mass transfer in MmNi_4·6Al_0·4 during desorption of hydrogen’, Int. J. Hydrogen Energy, 2010, 35, 10811–10818.

Yang

F. S.

, Wang

G. X.

, Zhang

Z. X.

and Rudolph

‘Investigation on the influences of heat transfer enhancement measures in a thermally driven metal hydride heat pump’, Int. J. Hydrogen Energy, 2010, 35, 9725–9735.

Jung

, Ahn

J. P.

, Jung

H. S.

and Park

J. K.

‘Hydrogenation of Ti–12Mg blending powder during mechanical milling in liquid media containing hydrogen’, Powder Metall., 2006, 49, 57–61.

10.

, Yang

F. S.

, Bao

Z. W.

, Nyamsi

S. N.

and Zhang

Z. X.

‘Improvement in hydrogen storage characteristics of Mg-based metal hydrides by doping nonmetals with high electronegativity: a first-principle study’, Comput. Mater. Sci., 2013, 78, 83–90.

11.

Yao

X. D.

, Wu

C. Z.

, Du

A. J.

, Zou

, Zhu

Z. H.

, Wang

, Cheng

H. M.

, Smith

and Lu

G. Q.

‘Metallic and carbon nanotube-catalyzed coupling of hydrogenation in magnesium’, J. Am. Chem. Soc., 2007, 129, 15650–15654.

12.

C. Z.

, Yao

X. D.

and Zhang

‘Hydriding/dehydriding properties of MgH₂/5 wt.%Ni coated CNFs composite’, Int. J. Hydrogen Energy, 2012, 35, 247–252.

13.

C. Y. V.

, Wang

Z. M.

, Liu

and Chan

S. L. I.

‘Electrochemical characteristics of La–Ni–Al thin films’, J. Alloys Compd, 2008, 456, 407–412.

14.

Teresiak

, Uhlemann

, Gebert

, Thomas

, Eckert

and Schultz

‘Formation of nanostructured LaMg₂Ni by rapid quenching and intensive milling and its hydrogen reactivity’, J. Alloys Compd, 2009, 481, 144–151.

15.

Chai

Y. J.

, Liu

Z. Y.

, Gao

H. N.

, Zhao

Z. Y.

, Wang

and Hou

D. L.

‘Microstructure and hydrogen storage properties of porous Ni@Mg’, Int. J. Hydrogen Energy, 2011, 36, 14484–14487.

16.

Huot

, Ravnsbak

D. B.

, Zhang

, Cuevas

, Latroche

and Jensen

T. R.

‘Mechanochemical synthesis of hydrogen storage materials’, Prog. Mater. Sci., 2013, 58, 30–75.

17.

Hakimi

, Kameli

, Salamati

and Mazaheri

‘Evolution of microstructural and mechanical properties of nanocrystalline Co₂FeAl Heusler alloy prepared by mechanical alloying’, Powder Metall., 2013, 56, 111–116.

18.

Polanski

, Bystrzycki

and Plocinski

‘The effect of milling conditions on microstructure and hydrogen absorption/desorption properties of magnesium hydride (MgH₂) without and with Cr₂O₃ nanoparticles’, Int. J. Hydrogen Energy, 2008, 33, 1859–1867.

19.

Huot

, Liang

, Boily

, Van Neste

and Schulz

‘Structural study and hydrogen sorption kinetics of ball-milled magnesium hydride’, J. Alloys Compd, 1999, 293–295, 495–500.

20.

Schimmel

H. G.

, Johnson

M. R.

, Kearley

G. J.

, Ramirez-Cuesta

A. J.

, Huot

and Mulder

F. M.

‘Structural information on ball milled magnesium hydride from vibrational spectroscopy and ab-initio calculations’, J. Alloys Compd, 2005, 393, 1–4.

21.

Doppiu

, Schultz

and Gutfleisch

‘In situ pressure and temperature monitoring during the conversion of Mg into MgH₂ by high-pressure reactive ball milling’, J. Alloys Compd, 2007, 427, 204–208.

22.

Singh

A. K.

, Singh

A. K.

and Srivastava

O. N.

‘On the synthesis of the Mg₂Ni alloy by mechanical alloying’, J. Alloys Compd, 1995, 227, 63–68.

23.

, Cao

X. X.

and Zhang

Z. X.

‘Identifying the influences of external parameters on the kinetics of Mg₂Ni prepared by ball milling’, Proc. 12th China Hydrogen Energy Conf. & 4th Mainland, Taiwan and Hong Kong Symp. on ‘Hydrogen energy’, Wuhan, China, October 2011, China Association for Hydrogen Energy, 172.

24.

Cullity

B. D.

and Cohen

(eds.) ‘The structure of polycrystalline aggregates’, in ‘Elements of X-ray diffraction’, Reading, MA, Addison-Wesley, 1st edn, Chap. 9, 1956, 259–296.

25.

Vijay

, Sundaresan

, Maiya

M. P.

and Murthy

S. S.

‘Comparative evaluation of Mg–Ni hydrogen absorbing materials prepared by mechanical alloying’, Int. J. Hydrogen Energy, 2005, 30, 501–508.

26.

Spassov

, Solsona

, Surinach

and Baro

M. D.

‘Optimisation of the ball-milling and heat treatment parameters for synthesis of amorphous and nanocrystalline Mg₂Ni-based alloys’, J. Alloys Compd, 2003, 349, 242–254.

27.

Bobet

J. L.

, Castro

F. J.

and Chevalier

‘Effects of reactive mechanical milling conditions on the physico-chemical properties of Mg+Cr₂O₃ mixtures’, J. Alloys Compd, 2004, 376, 205–210.

28.

Barabaszová

K. C.

and Valášková

‘Characterization of vermiculite particles after different milling techniques’, Powder Technol., 2013, 239, 277–283.

29.

Zaluska

, Zaluski

and Strom-Olsen

J. O.

‘Nanocrystalline magnesium for hydrogen storage’, J. Alloys Compd, 1999, 288, 217–225.

30.

Vyas

, Jain

, Agarwal

, Jain

and Jain

I. P.

‘Hydrogen storage properties of Mg₂Ni affected by Cr catalyst’, Int. J. Hydrogen Energy, 2012, 37, 16013–16017.

31.

Zhang

D. L.

‘Processing of advanced materials using high-energy mechanical milling’, Prog. Mater. Sci., 2004, 49, 537–560.

32.

Cheng

H. H.

‘Special hydrogen storage materials and the measurement apparatus’, PhD thesis, Institute of Metal Research, Chinese Academic of Sciences, Shenyang, China, 2007, 20–25.

33.

Flanagan

T. B.

and Clewley

J. D.

‘Hysteresis in metal hydrides’, J. Less-Common Met., 1982, 83, 127–141.

34.

Reilly

J. J.

and Wiswall

R. H.

‘The reaction of hydrogen with alloys of magnesium and nickel and the formation of Mg₂NiH₄’, Inorg. Chem., 1968, 7, 2254–2256.

35.

, Liu

and Chou

K. C.

‘Comparative study on the controlled hydriding combustion synthesis and the microwave synthesis to prepare Mg₂Ni from micro-particles’, Int. J. Hydrogen Energy, 2010, 35, 3129–3135.

36.

Jacobs

M. H. G.

and Spencer

P. J.

‘Thermodynamic evaluation of the systems Cu–Si, Mg–Ni, Si–Sn and Si–Zn’, J. Chim. Phys., 1993, 90, 167–173.

37.

Zeng

K. J.

, Klassen

, Oelerich

and Bormann

‘Thermodynamic analysis of the hydriding process of Mg–Ni alloys’, J. Alloys Compd, 1999, 283, 213–224.

38.

Xie

, Liu

, Zhang

X. Z.

, Qu

J. L.

, Wang

Y. T.

and Li

X. G.

‘Catalytic effect of Ni nanoparticles on the desorption kinetics of MgH₂ nanoparticles’, J. Alloys Compd, 2009, 482, 388–392.

39.

Ismail

, Zhao

and Dou

S. X.

‘An investigation on the hydrogen storage properties and reaction mechanism of the destabilized MgH₂–Na₃AlH₆ (4∶1) system’, Int. J. Hydrogen Energy, 2013, 38, 1478–1483.

40.

Kissinger

H. E.

‘Reaction kinetics in differential thermal analysis’, Anal. Chem., 1957, 29, 1702–1706.

41.

Friedlmeier

and Groll

‘Experimental analysis and modeling of the hydriding kinetics of Ni-doped and pure Mg’, J. Alloys Compd, 1997, 253–254, 550–555.

42.

Chung

C. A.

and Lin

C. S.

‘Prediction of hydrogen desorption performance of Mg₂Ni hydride reactors’, Int. J. Hydrogen Energy, 2009, 34, 9409–9423.

43.

Guzman

, Ordonez

, Fernandez

J. F.

, Sanchez

, Serafini

, Rojas

P. A.

, Aguilar

and Tapia

‘Effect of amorphous Mg₅₀Ni₅₀ on hydriding and dehydriding behavior of Mg₂Ni alloy’, Mater. Charact., 2011, 62, 442–450.