Crack initiation and kinking behaviours of spot welded coach peel specimens under cyclic loading

Abstract

The present study is carried out to investigate fatigue crack initiation and kinking behaviours of spot welded coach peel (CP) specimens of low carbon steel sheets subjected to cyclic loading by experimental and finite element analysis methods. Evaluations of fatigue crack growth stages were performed by crack tip plastic strains and J integral analyses and also by microhardness measurements on process zone. According to the experimental and analytical results, fatigue crack initiation and growing stages in the spot welded CP specimens can be divided to three stages. Stage I corresponds to ‘gap sharpening stage’ observed at the beginning steps of cyclic loading with crack growing on the interface plane between the overlapped sheets. Stage II corresponds to kinked crack initiation and propagation through the sheet thickness observed after applying a certain number of loading cycles. Stage III corresponds to crack propagation through the width of the specimens observed at the final step of the fatigue crack propagation. The FE results of the crack paths and crack locations are in good agreement with those of experimental observations.

Keywords

SPOT WELD FATIGUE FE ANALYSIS J INTEGRAL COACH PEEL KINKED CRACK

Get full access to this article

View all access options for this article.

References

Chao

Y. J.

: Sci. Technol. Weld. Join., 2003, 8, 133–137.

Pouranvari

, Asgari

H. R.

, Mosavizadch

S. M.

, Marashi

P. H.

and Goodarzi

: Sci. Technol. Weld. Join., 2007, 12, 218–225.

Henrysson

H. F.

: ‘Fatigue of spot welded joints: experiment and life prediction’, PhD thesis, Chalmers University of Technology, Göteborg, Sweden, 2001.

Pan

: ‘Fatigue life study of spot welds’, PhD thesis, Stanford University, Stanford, CA, USA, 2000.

Newman

J. A.

and Dowling

N. E.

: Fatigue Fract. Eng. Mater. Struct., 1998, 21, 1123–1132.

Sheppard

S. D.

and Strange

: Fatigue Fract. Eng. Mater. Struct., 1992, 15, 531–549.

Conle

F. A.

and Chu

C. C.

: Int. J. Fatigue, 1997, 19, 317–323.

Zhang

and Taylor

: Eng. Fract. Mech., 2000, 67, 55–63.

Wang

D. A.

and Pan

: Int. J. Solids Struct., 2005, 42, 6277–6298.

10.

Pook

L. P.

: Int. J. Fract., 1975, 11, 173–176.

11.

Wang

P. C.

and Ewing

K. W.

: ‘A J-integral approach to fatigue resistance of a tensile-shear spot weld’, SAE paper 880373, UK, 1988.

12.

Wang

P. C.

and Ewing

K. W.

: Fatigue Fract. Eng. Mater. Struct., 1991, 14, 915–930.

13.

Liang

C. P.

, Lin

Z. Q.

, Chen

G. L.

and Li

Y. B.

: Sci. Technol. Weld. Join., 2006, 11, 609–617.

14.

Zuniga

S. T.

: ‘Predicting overload pull-out failure in resistance spot-welded joints’, PhD dissertation, Chapter 2, Stanford University, Stanford, CA, USA, 1994.

15.

Cahoon

J. R.

, Broughton

W. H.

and Kutzak

A. R.

: Metall. Trans., 1971, 2, 1979–1983.