The growth of Mg and Al coatings on copper by pack cementation is examined in this work by investigating the mechanism of the process, the effect of temperature and heating time on the coating structure. The experiments were undertaken at temperatures ranging from 550 to 600°C, while the duration of the process varied from 30 min to 3 h. It was found that the magnesium coatings consist of two phases corresponding to MgCu2 and CuMg2. These phases appeared as distinguished layers or mixed with each other, depending on the deposition temperature and duration. On the other hand, the aluminium coatings consist of a single Al4Cu9 phase whose thickness increases with deposition time and temperature. Finally, the oxidation resistance was also evaluated by thermogravimetric measurements, which revealed that the coated samples have superior resistance to bare copper, while Al coated coupons had the best performance when exposed in high temperature environment.
SozerEB, JiangC, GundersenMA and UmstattdRJ: ‘Quantum efficiency measurements of photocathode candidates for back-lighted thyratrons’, IEEE Trans. Dielectr. Electr. Insul., 2009, 16, (4), 993–998.
2.
KimKH, NortonDP, ChristenDK and BudaiJD: ‘Formation of oxidation-resistant Cu–Mg coatings on (001) Cu for oxide superconducting tapes’, Surf. Coat. Technol., 2008, 202, 5136–5139.
3.
A SchweitzerP: ‘Fundamentals of metallic corrosion: atmospheric and media corrosion of metals’, 2nd edn; 2007, Boca Raton, FL, CRC Press.
4.
ChaliampaliasD, PapazoglouM, TsipasS, PavlidouE, SkolianosS, StergioudisG and VourliasG: ‘Fabrication and examination of oxidation resistance of zinc coated copper and brass components by chemical deposition’, Surf. Eng., 2011, 27, (5), 362–367.
5.
RahmanA, JayaganthanR, PrakashS, ChawlaV and ChandraR: ‘Cyclic high temperature oxidation behaviour of sputtered Cr/Al multilayer coatings on superalloy’, Surf. Eng., 2011, 27, (5), 393–401.
6.
LiuGJ, JiaSS, HongSH, LimJW, ZhuYF, MimuraK and IsshikiM: ‘Corrosion resistance of dilute CuMg alloys at elevated temperature’, Corros. Sci., 2009, 51, (3), 463–468.
7.
ArcotB, MurarkaSP, ClevengerLA, HongQZ and ZieglerW: ‘Intermetallic formation in copper/magnesium thin films – kinetics, nucleation and growth, and effect of interfacial oxygen’, J. Appl. Phys., 1994, 76, 5161.
8.
ChaliampaliasD, AndronisS, StergioudisG, TsipasD, VourliasG and PavlidouE: ‘Deposition of multilayer NiCrBSiFe and Al coatings on low carbon steels’, Microscopy Cong., Kiel, Germany, August–September 2011, Proc., (Copyright) 2011 DGE – German Society for Electron Microscopy e.V. Germany, MC2011.
9.
FelipeTS, MurarkaSP, BedellS and LandfordWA: ‘Capacitance–voltage, current–voltage, and thermal stability of copper alloyed with aluminium or magnesium’, Thin Solid Films, 1998, 35, 49–53.
10.
FrederickMJ and RamanathGJ: ‘Kinetics of interfacial reaction in Cu–Mg alloy films on SiO2’, Appl. Phys., 2004, 95, 363–366.
11.
StathokostopoulosD, ChaliampaliasD, StefanakiEC, PolymerisG, PavlidouE, ChrissafisK, HatzikraniotisE, ParaskevopoulosKM and VourliasG: ‘Structure, morphology and electrical properties of Mg2Si layers deposited by pack cementation’Appl. Surf. Sci., 2013, 285, 417–424.
12.
StathokostopoulosD, ChaliampaliasD, PavlidouE, HatzikraniotisE, StergioudisG, ParaskevopoulosKM and VourliasG: ‘Formation of Mg2Si thick films on Si substrates using pack cementation process’, AIP Conf. Proc., 2012, 1449, 203–206.
13.
VourliasG, ChaliampaliasD, PavlidouE, StergioudisG and ChrissafisK: ‘Examination of zinc coatings on copper substrates by thermal analysis’, J. Therm. Anal. Calorim., 2013, 111, 49–55.
14.
HuG, XuZ, LiuJ and LiY: ‘Microstructure and corrosion resistance of simultaneous Al–Fe coating on copper by pack cementation’, Surf. Coat. Technol., 2009, 203, 3392–3397.
15.
EslamiA, ArabiH and RastegariS: ‘Gas phase aluminizing of a nickel base superalloy by a single step HTHA aluminizing process’, Can. Metall. Q., 2009, 48, (1), 91–98.
16.
XiangZD and DattaPK: ‘Relationship between pack chemistry and aluminide coating formation for low-temperature aluminisation of alloy steels’, Acta Mater., 2006, 54, 4453–4463.
17.
SchmidtD, GaletzM and SchutzeM: ‘Deposition of manganese and cobalt on ferritic–martensitic steels via pack cementation process’Oxid. Met., 2013, 79, 589–599.
18.
VourliasG, PistofidisN, ChrissafisK, PavlidouE and StergioudisG: ‘Mechanism and kinetics of the formation of zinc pack coatings’, J. Therm. Anal. Calorim., 2008, 91, 497–501.
19.
ZhouF, GaoM, TuGF, LiuK and PenguKW: ‘Aluminide coating prepared on Ni-base superalloy by pack cementation’, Adv. Mater. Res., 2014, 848, 11–17.
20.
SakidjaR, PerepezkoJH and CalhounP: ‘Synthesis, thermodynamic stability and diffusion mechanism of Al5Fe2-based coatings’, Oxid. Met., 2014, 81, 167–177.
21.
WangJ, WuDJ, ZhuCY and XiangZD: ‘Low temperature pack aluminising kinetics of nickel electroplated on creep resistant ferritic steel’, Surf. Coat. Technol., 2013, 236, 135–141.
22.
ChiangKT, KallenbornKJ and YuenJL: ‘Aluminization of copper for oxidation protection’, Surf. Coat. Technol., 1992, 52, 135–139.
23.
Abd El-AzimME and SolimanHM: ‘Pack aluminizing of copper’, J. Mater. Sci. Technol., 1997, 13, 127–132.
NordlienJH, OnoS, MasukoN and NisanciogluK: ‘A TEM investigation of naturally formed oxide films on pure magnesium’, Corros. Sci., 1997, 39, (8), 1397–1414.
27.
EliezerD and AlvesH (eds.): ‘Corrosion and oxidation of magnesium alloys’, 267–291; 2002, New York, John Wiley & Sons.
28.
ZhuF, LuHM, JiangQ, MimuraK and IsshikiM: ‘Effect of alloying Mg on corrosion resistance of Cu at high temperature’, J. Electrochem. Soc., 2007, 3, 153–158.