In this study, the effect of conventional plasma nitriding on chromised tool steel was investigated. The samples were chromised at 1100°C for 12 h using thermoreactive diffusion/deposition (TRD). Subsequent tof TRD, specimens were nitrided at 600°C using a DC plasma set-up. Phase composition and surface morphology of the coatings were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) respectively. Corrosion resistance of the samples was investigated by polarisation corrosion test. X-ray diffraction analysis indicated that after chromising, the coating mainly consisted of Cr7C3, Cr23C6 and Fe3C and surface hardness increased from 330 to 1400 HV0.01. However, after plasma nitriding, nanosized Cr2N, CrN, Fe3N and Fe4N phases with particle sizes ranging from 32 to 54 nm were formed. The results of polarisation corrosion tests showed that by applying duplex TRD and plasma nitriding, the corrosion resistance was improved.
KaramısM. B., YıldızlıK. and AydınG. C.: ‘Sliding/rolling wear performance of plasma nitrided H11 hot working steel’, Tribol. Int., 2012, 51, 18–24. doi: 10.1016/j.triboint.2012.02.005
2.
WeiC. Y. and ChenF. S.: ‘Characterization on multi-layer fabricated by TRD and plasma nitriding’, Mater. Chem. Phys., 2005, 90, 178–184. doi: 10.1016/j.matchemphys.2004.10.008
3.
Baggio-ScheidV. H., de VasconcelosG., OliveiraM. A. S. and FerreiraB. C.: ‘Duplex surface treatment of chromium pack diffusion and plasma nitriding of mild steel’, Surf. Coat. Technol., 2003, 163–164, 313–317. doi: 10.1016/S0257-8972(02)00607-2
4.
TaktakS., UlcerS. and GunseI.: ‘High temperature wear and friction properties of duplex surface treated bearing steels’, Surf. Coat. Technol., 2008, 202, 3367–3377. doi: 10.1016/j.surfcoat.2007.12.015
5.
ChangD. Y., LeeS. Y. and KangS. -G.: ‘Effect of plasma nitriding on the surface properties of the chromium diffusion coating layer in iron-base alloys’, Surf. Coat. Technol., 1999a, 116–119, 391–397. doi: 10.1016/S0257-8972(99)00234-0
6.
KingP. C., ReynoldsonR. W., BrownriggA. and LongJ. M.: ‘Cr(N,C) diffusion coating formation on pre-nitrocarburised H13 tool steel’, Surf. Coat. Technol., 2004, 179, 18–26. doi: 10.1016/S0257-8972(03)00791-6
7.
LiuX., WangH., LiD. and WuY.: ‘Study on kinetics of carbide coating growth by thermal diffusion process’, Surf. Coat. Technol., 2006, 201, 2414–2418. doi: 10.1016/j.surfcoat.2006.04.028
8.
DixonG. J.: ‘Heat treatment’, ‘Vol.137’; 1981, Cornell University, New York
, The Metal Society.
9.
OzdemirO., SenS. and SenU.: ‘Formation of chromium nitride layers on AISI 1010 steel by nitro-chromizing treatment’, Vacuum, 2007, 81, 567–570. doi: 10.1016/j.vacuum.2006.07.002
10.
Karimi ZarchiH. R., JalalyM., SoltaniehM. and MehrjooH.: ‘Comparison of the activation energies of the formation of chromium carbide coating on carburized and uncarburized AISI 1020 steel’, Steel Res. Int., 2009, 80.
11.
SenS.: ‘A study on kinetics of CrxC-coated high-chromium steel by thermo-reactive diffusion technique’, Vacuum, 2005, 79, 63–70. doi: 10.1016/j.vacuum.2005.01.009
12.
HakamiF., heydarzadeh SohiM. and Rasizadeh GhaniJ.: ‘Duplex surface treatment of AISI 1045 steel via plasma nitriding of chromized layer’, Thin Solid Films, 2011, 519, 6792–6796. doi: 10.1016/j.tsf.2011.04.054
13.
BassoR. L. O., PastoreH. O., SchmidtV., BaumvolI. J. R., AbarcaS. A. C., de SouzaF. S., SpinelliA., FigueroaC. A. and GiacomelliC.: ‘Microstructure and corrosion behaviour of pulsed plasma-nitrided’, Corros. Sci., 2010, 52, 3133–3139. doi: 10.1016/j.corsci.2010.05.036
14.
TaguchiM. and KoriharaJ.: ‘Effect of surface nitriding on corrosion resistance of chromium in sulfuric acid solution’, Mater. Trans., 1991, 32, 1170–1176. doi: 10.2320/matertrans1989.32.1170
GunesI., ErdoganM. and ÇelikA. G.: ‘Corrosion Behavior and Characterization of Plasma Nitrided and Borided AISI M2 Steel’, Mater. Res., 2014, 17, 612–618. doi: 10.1590/S1516-14392014005000061
17.
BelahssenO., ChalaA. and BenramacheS.: ‘Corrosion behavior of the 42CrMo4 steel nitride by plasma’, Orient. J. Chem., 2013, 29, 1543–1546. doi: 10.13005/ojc/290434
18.
KusmicD. and HrubyV.: ‘Corrosion resistance of plasma nitride structural steel’, ‘23rd International Conference on Metallurgy and Materials METAL 2014, Brno, Czech Republic, EU, May 2014, Hotel Voronez I, Paper 15’; 2014.
19.
SoltaniehM., AghajaniH., MahboubiF. and NekoueeKh. A.: ‘Surface characterization of multiple coated H11 hot work tool steel by plasma nitriding and hard chromium electroplating processes’, Vacuum, 2012, 86, 1470–1476. doi: 10.1016/j.vacuum.2012.01.003
20.
LiC. X., BellT. and DongH.: ‘A study of active screen plasma nitriding’, Surf. Eng., 2002, 18, 174–181. doi: 10.1179/026708401225005250
21.
ChangD. Y., LeeS. Y. and KangS. G.: ‘Effect of plasma nitriding on the surface properties of the chromium diffusion coating layer in iron-base alloys’, Surf. Coat. Technol., 1999, 116–119, 391–397. doi: 10.1016/S0257-8972(99)00234-0
22.
ShahH. N., JayaganthanR. and KaurD.: ‘Effect of sputtering pressure and temperature on DC magnetron sputtered CrN films’, Surf. Eng., 2010, 26, 629–637. doi: 10.1179/174329409X389326
23.
TaktakS., GunesI., UlkerS. and YalcinY.: ‘Effect of N2+H2 gas mixtures in plasma nitriding on tribological properties of duplex surface treated steels’, Mater. Charact., 2008, 59, 1784–1791. doi: 10.1016/j.matchar.2008.04.010
24.
CaoH. L., LuoC. P., LiuJ. W., WuC. L. and ZouG. F.: ‘Formation of a nanostructured CrN layer on nitrided tool steel by low-temperature chromizing’, Scr. Mater., 2008, 58, 786–789. doi: 10.1016/j.scriptamat.2007.12.027
25.
CaoH. L., LuoC. P., LiuJ. W., WubC. L. and ZouaG. F.: ‘Formation of a nanostructured CrN layer on nitrided tool steel by low-temperature chromizing’, Scr. Mater., 2008, 58, 786–789. doi: 10.1016/j.scriptamat.2007.12.027
AhangaraniSh., SabourA. R., MahboubiF. and ShahrabiT.: ‘The influence of active screen plasma nitriding parameters on corrosion behavior of a low-alloy steel’, J. Alloys Compd., 2009, 484, 222–229. doi: 10.1016/j.jallcom.2009.03.161