Electrical and electromechanical characteristics of LTCC embedded piezoelectric bulk actuators

Abstract

Piezoelectric effect is a versatile method to generate force and movement in microsystems as well as electrical feedback in sensors and smart packages. On the other hand, low temperature cofired ceramic (LTCC) has been utilised as a base material for hybrid circuit boards, packages as well as some microfluidic devices; however, new means to introduce integrated functionalities for it are needed. In this paper, a 10×5 mm rectangle and 10 mm in diameter round PZT samples fully embedded and cofired with Heraeus HeraLock LTCC were manufactured and their hysteresis, dielectric, displacement and microstructure properties and coupling factors were characterised. Relative permittivity of the LTCC embedded varied from 1300 for the rectangle sample to 1500 for the round sample at 1 kHz, while_r of 2209-2406 was obtained for corresponding bare bulk samples respectively. Measured piezoelectric d₃₃ coefficient was in the range of 324-441 pm V⁻¹ for embedded structures, while 553-567 pm V⁻¹ was obtained for free bulk samples at 100 Hz. Results show that LTCC has significant impact for electromechanical performance mainly due to constraining of the LTCC layers. In spite of this, feasible figures of merits were obtained for LTCC embedded PZT materials, while further improvements can be obtained by optimising the process and structures for LTCC based microsystems, sensors and actuators.

Keywords

Piezoelectric LTCC Integration Electromechanical

Get full access to this article

View all access options for this article.

References

Achmann

, Hämmerle

, Kita

and Moos

: ‘Miniaturized low temperature co-fired ceramics (LTCC) biosensor for ampero-metric gas sensing’, Sensors Actuators B, 2005 135B, (1), 89–95.

Golonka

L. J.

: ‘New application of LTCC technology’, Proc. 28th Int. Spring Semin. on ‘Electronics technology: ‘Meeting the challenges of electronics technology progress’, Vienna, Austria, May 2005, Technische Universitat, 162–166.

Golonka

L. J.

: ‘Technology and applications of low temperature cofired ceramic (LTCC) based sensors and microsystems’, Pot Acad Sci, 2006, 54, (2), 223–233.

Golonka

L. J.

, Zawada

, Roguszczak

, Malecha

, Chudy

, Stadnik

and Dybko

: ‘Three-dimensional fluidic microsystem fabricated in low temperature cofired ceramic technology’, J. Microelectron. Electron. Packag., 2006, 3, (3), 145–151.

Gongora-Rubio

M. R.

, Espinoza-Vallejos

, Sola-Laguna

and Santiago-Aviles

J. J.

: ‘Overview of low temperature co-fired ceramics tape technology for meso-system technology (MsST)’, Sensors. Actuators A, 2001, 89A, 222–241.

Sobocinski

, Juuti

, Jantunen

and Golonka

: ‘Piezoelectric unimorph valve assembled on an LTCC substrate’, Sensors Actuators A, 2009, 149A, (2), 315–319.

Hrovat

, Holc

, Drnovgek

, Belavie

, Bernard

, Kosec

, Golonka

, Dziedzic

and Kita

: ‘Characterization of PZT thick films fired on LTCC substrates’, J. Mater. Set Lett., 2003, 22, 1193–1195.

Juuti

, Jantunen

, Moilanen

V.-P.

and Leppävuori

: ‘Manufacturing of pre-stressed piezoelectric unimorphs using a post-fired biasing layer’, IEEE Trans. Ultrason. Ferroelectr. Freq. Control, 2006, 53, (5), 838–846.

Heinonen

, Juuti

and Jantunen

: ‘Characteristics of piezoelectric cantilevers embedded in LTCC’, J. Eur. Ceram. Soc., 2007, 27, (13-15), 4135–4138.

10.

Juuti

: Acta Universitatis Ouluensis C 235, 2006. Available at: http://herkules.oululdisbn9514279891/

11.

Moilanen

and Leppävuori

: ‘Laser interferometric measure-ment of displacement-field characteristics of piezoelectric actuators and actuator materials’, Sensors Actuators A, 2001, 92A, 326–334.