A series of plate impact experiments have been conducted on alumina specimens with different thicknesses through the light gas gun in order to further investigate the delayed failure phenomenon under shock loading. With the aid of the velocity interferometer system for any reflector, an evident recompression signal has been observed in the temporal curve of the rear free surface velocity of the specimen, which indicates the generation of the failure wave. According to the experimental results, the failure wave propagation was probed. The results show that the failure wave generates a delayed time of ∼0·105 μs behind the shock wave front and propagates into the stressed body with a velocity of ∼5051 m s−1 under the impact stress of 7·16 GPa. The physical mechanism of the failure wave was further discussed.
RasorenovS, KanelG, FortovV, AbasehovM: ‘The fracture of glass under high-pressure impulsive loading’, High Pressure Res., 1991, 6, 225–232.
2.
KanelGI, RasorenovSV, FortovVE:‘The failure waves and spallations in homogeneous brittle materials’, in ‘Shock compression of condensed matter’(, SchmidtS C, et al..), 451–454; 1991, Williamsburg, VA, Elsevier Science Publishers BV.
3.
BrarNS, RosenbergZ, BlessSJ: ‘Spall strength and failure waves in glass’, J. Phys. IV, 1991, 1, (C3), 639–642.
4.
BrarNS, BlessSJ, RosenbergZ: ‘Impact-induced failure waves in glass bars and plates’, Appl. Phys. Rev., 1993, 46, (12), 540–546.
5.
BlessSJ, BrarNS, KanelG, RosenbergZ: ‘Failure waves in glass’, J. Am. Ceram. Soc., 1992, 75, 1002–1004.
6.
BourneNK, RosenbergZ, FieldJE: ‘High-speed photography of compressive failure in glasses’, J. Appl. Phys., 1995, 78, (6), 3736–3739.
7.
BourneNK, MillettJ, RosenbergZ, MurrayN: ‘On the shock induced failure of brittle solids’, J. Mech. Phys. Solids, 1998, 46, (10), 1887–1908.
8.
ZhangY, DuanZ, ZhangL, OuZ, HuangF: ‘Experimental research on failure wave of brittle materials under shock loading’, Acta Armamentarii, 2010, 31, (4), 486–490.
9.
LiuZ, ChangJ, YaoG, ZhangK, LiJ: ‘Propagation of failure front in shock-loaded polycrystalline alumina’, Acta Mech. Sin., 2006, 38, (5), 626–632.
10.
BourneNK, MillettJ, PickupI: ‘Delayed failure in shocked silicon carbide’, J. Appl. Phys., 1997, 81, (9), 6019–6023.
11.
BourneNK, GrayGT:‘On the failure of boron carbide under shock’, in ‘Shock compression of condensed matter’(, FurnishM D, et al..), 775–779; 2001.
12.
GroteDL, ParkSW, ZhouM: ‘Experimental characterization of the dynamic failure behavior of mortar under impact loading’, J. Appl. Phys., 2001, 89, (4), 2115–2123.
13.
ZhangQM, HuangFL, HanLM: ‘Failure wave motion of 3D-C/SiC composites subjected to shock compression’, Chin. Sci. Bull., 2000, 45, (5), 408–411.
14.
BlessSJ, BrarNS: ‘Failure waves and their effects on penetration mechanics in glass and ceramics’, Shock Wave Science and Technology Reference Library, (Chapter 3), 2007, 105–141.
15.
CliftonRJ: ‘Analysis of failure waves in glasses’, Appl. Mech. Rev., 1993, 46, (12), 540–546.
16.
GradyDE: ‘Shock-waves properties of brittle solids’, in ‘Shock compression of condensed matter’, (ed. , SchmidtS C, TaoW C), 9–20; 1996, Washington, Elsevier Science Publishers BV.
17.
HeH, JingF, JinX, KanelGI: ‘Compressive failure of brittle materials under shock wave loading’, Proc. Sino-Japanese Symp.on ‘Deformation/fracture of solids’, Huangshan, China, 1997, 81–90.
18.
HeH: ‘Dynamic response and microstructure damage of brittle materials under shock wave compression’, PhD thesis, Institute of Fluid Physics of CAEP, Chengdu, China, 1997.
19.
ZhaoJH: ‘Experimental and theoretical investigation on failure waves in glass-like brittle materials under shock wave loading’; 2000, Beijing, Institute of Mechanics, Chinese Academy of Science.
20.
KanelGI, BogatchAA, RazorenovSV, ChenZ: ‘Transformation of shock compression pulse in glass due to the failure wave phenomena’, J. Appl. Phys., 2002, 92, 5045–5052.
21.
KanelGI, RazorenovSV, SavinykhAS, RajendranA, ChenZ: ‘A study of failure wave phenomenon in glasses compressed at different levels’, J. Appl. Phys., 2005, 98, 113523–113527.
22.
KanelGI, SavinykhAS, GarkushinGV, RazorenovSV, RajendranA:‘Phenomenological description of the failure waves in glasses’, in ‘Shock Compres Conden Mat’(, ElertM, et al..), 751–754, AIP CP955; 2008.
23.
EspinosaHD, XuYP: ‘Micromechanics of failure waves in glass: I experiments’, J. Am. Ceram. Soc., 1997, 80, (8), 2061–2073.
24.
ZhangY, DuanZ, OuZ, HuangF: ‘Experimental research on failure waves in soda-lime glass’, Exp. Mech., 2011, 51, 247–253.
25.
EspinosaHD, XuYP: ‘Micromechanics of failure waves in glass: II modeling’, J. Am. Ceram. Soc., 1997, 80, (8), 2074–2085.
26.
PartomY: ‘Modeling failure waves in glass’, Int. J. Impact Eng., 1998, 21, (9), 791–799.
27.
LiuZ, YaoG, ZhanX: ‘A damage accumulating modeling of failure waves in glass under high velocity impact’, J. Appl. Math. Mech., 2001, 22, (9), 1090–1095.
28.
ChenZ, XinX: ‘An analytical numerical study of failure waves’, Int. J. Solids Struct., 1999, 36, 3977–3991.
29.
FengR: ‘Formation and propagation of failure in shocked glasses’, J. Appl. Phys., 2000, 87, (4), 1693–1700.
30.
JingF: ‘Introduction to experimental equation of state’; 1999, Beijing, Science Press.
31.
MorozovN, PetrovY: ‘Dynamics of fracture’; 2000, Berlin, Springer-Verlag.
32.
ChenD, HeH, JingF: ‘Delayed failure of the shock compressed inhomogeneous brittle material’, J. Appl. Phys., 2007, 102, 033519, 1–5.