Abstract
The influence of P on the creep behaviour of Ni, Ni–20Cr (wt-%), and Nimonic 80A was investigated by carrying out creep tests under various loads and at different temperatures. After creep fracture the samples were investigated using optical, scanning electron, and transmission electron microscopy. The grain boundary segregation was examined using Auger electron spectroscopy (AES). It was found that P segregates to the grain boundaries in all the materials investigated. The creep rate of Ni–20Cr and Nimonic 80A is decreased by the addition of P. Grain boundary segregation of P and its influence on strength was also investigated using AES for specimens aged between 600 and 700°C after fracture by a tensile test inside an ultrahigh vacuum chamber. Maxima of tensile strength are observed to be time dependent as a result of carbide precipitation, which is affected by the P segregation.