Phosphide precipitation has been studied in a Ti modified type 316 stainless steel containing a 0·15 wt-%P addition during thermal aging in the temperature range 600–800°C and as a function of initial condition (solution treated or cold worked). Needle shaped M3P precipitates in well defined crystallographic orientations are observed to nucleate on either complex defects or dislocations resulting from the initial thermomechanical condition. The stability of the phosphides decreases with increasing aging temperature and in the presence of prior cold work.
MST/3239
Get full access to this article
View all access options for this article.
References
1.
DUBUISSONP., MAILLARDA., DELALANDEC., GILBOND., and SERANJ. L.: in ‘Effects of radiation on materials’, STP1125, 995; 1992, Philadelphia, PA, ASTM.
2.
WEISSB. and STICKLERR.: Met. Trans.,1972, 3, 851.
3.
GROTA. S. and SPRUIELLJ. E.: Met. Trans. A, 1975, 6A, 2023.
4.
SPRUIELLJ. E., SCOTTJ. A., ARYC. S., and HARDINR. L.: Metall. Trans.,1973, 4, 1533.
KEGGG. R., SILCOCKJ. M., and WESTD. R. F.: Met. Sci.,1974, 8, 337.
7.
FROESF. H., HONEYCOMBER. W. K., and WARRINGTOND. H.: Acta Metall., 1967, 15, 157.
8.
KESTERNICHW.: Philos. Mag.,1985, 52, 533.
9.
KESTERNICHW. and MEERTENSD.: Acta Metall., 1986, 34, 1071.
10.
LEEE. H., MANSURL. K., and ROWCLIFFEE. F.: J. Nucl. Mater., 1984, 122-123, 299.
11.
LEEE. H., MAZIASZP. J., and ROWCLIFFEA. F.: Report of contract W-7405—ENG-26. Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA.
12.
BOULANGERL.: Doctoral thesis, University of Paris Sud, France, 1986.
13.
LAIJ. K. and GALBRAITHI. F.: J. Mater. Sci.,1980, 15, 1297.
14.
BANERJEEB. R., DULISE. J., and HAUSERJ. J.: Trans. ASM, 1968, 61, 103.
15.
FROESF. H., WELLSM. G. H., and BANERJEEB. R.: Met. Sci.,1968, 2, 232.
16.
LEITNAKERJ. M. and BENTLEYJ.: Metall. Trans. A, 1977, 8A, 1605.
17.
BENTLEYJ. and LEITNAKERJ. M.: in ‘The metal science of stainless steels’, (ed. CollingsE. W. and KingH. W.), 70-91; 1978, Warrendale, PA, TMS/AIME.
18.
ROWCLIFFEA. F. and NICHOLSONR. B.: Acta Metall., 1972, 20, 143.