Effect of local induction heat treatment on the induced residual stresses in the web region of a welded rail

Abstract

Rails are often joined by welding and about 80–90 per cent of tracks are welded using the flash-butt welding method. As the result of the welding process, high tensile residual stresses are induced in the web region of the rail, at and near the welded zone. Since the main part of the welded zone is coarse grained and has porosities and inclusions, the web part of the rail is susceptible to failure. The magnitude of the induced stresses may be reduced by stress-relieving heat treatment, but in practice the heat treatment process is not used as it is very time consuming and adds to overall project costs. In this paper, microscopic studies were performed on the welded zone in the head, the web and the base parts of the rail. The effects of local induction heat treatments on the microstructure and on the resultant tensile residual stresses in the web region were studied. To do this, firstly, dilatometery specimens were prepared from the base metal of the rail. These were heat-treated under different induction heat treatment cycles and the resulting phase transformation and the changes in the length of the specimens were obtained. Secondly, the effects of local induction heat treatments on the residual stress field in the welded zone of the rail were investigated using finite element analysis. Finally, a local induction hardening and tempering heat treatment is proposed to reduce the residual stresses in the web region of a welded rail.

Keywords

flash-butt welded rail residual stress dilatometery finite element analysis

Get full access to this article

View all access options for this article.

References

ASM Metals Handbook, Welding, Brazing and Soldering, Vol. 6, 10th edition, 1997, p. 1101 (ASM International, Metals Park, Ohio).

Ezellio

A. N.

Webster

G. A.

Webster

P. J.

Annual Report, The Institute Laue-Langevin, UK, 1996, p. 10.

Krishnaraj

Rao

K. P.

Ramachandran

E. G.

The quality of flash welded-joints in mild-steel: A study on the effects of welding parameters

Weld. J., 1993, 72 (6). 239S.

Webster

P. J.

Mills

Wang

X. D.

Kang

W. P.

Holden

T. M.

Residual stresses in alumino-thermic welded rails

J. Strain Analysis, 1997, 32 (6), 389–400.

Urashima

Nishida

Sugino

The influence of residual stress on durability of rails. In International Conference on

Residual Stresses (ICRS2), Nancy, France, 23–25 November 1988, pp. 912–918.

Steele

R. K.

Joerms

M. W.

Utrata

Carpenter

G. F.

Catastrophic web cracking of railroad rail In Residual Stresses in Rails (Eds Orringer

). Vol. 1, 1992, pp. 1–19 (Kluwer Academic Publications, Dordrecht, The Netherlands).

Wineman

S. J.

McClintock

F. A.

Rail web fracture in the presence of residual stresses

Theoret. Appl. Fracture Mechanics, 1987, 8 (2), 87–99.

Muller

H. H.

Local heat treatment by induction In Stress Relieving Heat Treatments of Welded Steel Constructions, 1987 (Pergamon Press, Oxford).

ASM Metals Handbook, Heat-treating, Vol. 4, 10th edition, 1991, p. 164 (ASM International, Metals Park, Ohio).

10.

Nitschke-Pagel

Th.

Wohlfart

Residual stress distributions after welding as a consequence of the combined effect of physical, metallurgical and mechanical sources In Proceedings of the IUTAM International Symposium on The Mechanical Effects of Welding, Luleå, Sweden, 1992, pp. 123–134.

11.

Avner

S. H.

Introduction to Physical Metallurgy, 1974 (McGraw-Hill, New York).

12.

ABAQUS User's Manual Version 5.8, 1998 (Hibbitt Karlsson and Sorensen Inc., Providence, Rhode Island).