T-stress and mixed-mode stress intensity factors have been determined experimentally using thermoelastic stress analysis and using a finite element method. Pure mode I, strong mixed-mode I and II, and interacting cracks have been used as the case studies. A new technique has been proposed to identify the crack tip from thermoelastic images. It has also been shown that using three terms of Williams's stress field formulation to determine the T-stress, yields a more accurate solution than using only the first two terms of the expansion.
LarssonS. G.CarlssonA. J.Influence of nonsingular stress terms and specimen geometry on small scale yielding at crack tips in elastic-plastic materials. J. Mech. Phys. Solids, 1973, 21, 263–277.
2.
WilliamsM. L.On the stress distribution at the base of a stationary crack. J. Appl. Mech., 1957, 24, 109–114.
3.
AyatollahiM. R.PavierM. J.SmithD. J.Determination of T-stress from finite element analysis for mode I and mixed mode I/II loading. Int. J. Fracture, 1998, 91, 283–298.
4.
LeeversP. S.RadonJ. C.Inherent stress biaxiality in various fracture specimen geometries. Int. J. Fracture, 1982, 19, 311–325.
5.
AyatollahiM. R.PavierM. J.SmithD. J.Mode I cracks subjected to large T-stresses. Int. J. Fracture, 2002, 117, 159–174.
6.
ErdoganF.SihG. C.On the crack extension in plates under plane loading and transverse shear. J. Basic Engng, 1963, 85, 519–527.
7.
CotterellB.Notes on the paths and stability of cracks. Int. J. Fracture, 1966, 2(3), 526–533.
8.
RoychowdhuryS.DoddsR. H.JrEffect of T-stress on fatigue crack closure in 3-D small-scale yielding. Int. J. Solids Struct., 2004, 41, 2581–2606.
9.
SmithD. J.AyatollahiM. R.PavierM. J.The role of T-stress in brittle fracture for linear elastic materials under mixed-mode loading. Fatigue Fract. Engng Mater. Struct., 2001, 24(2), 137–150.
10.
SherryA. H.FranceC. C.GoldthorpeM. R.Compendium of T-stress solutions for two and three dimensional cracked geometries. Fatigue Fract. Engng Mater. Struct., 1995, 18(1), 141–155.
StanleyP.ChanW. K.The determination of stress intensity factors and crack-tip velocities from thermoelastic infra-red emissions. In Proceedings of the International Conference on Fatigue of Engineering Materials and Structures (IMechE), Sheffield, September 1986, pp. 105–114, Vol. 1, paper c262/86.
17.
Dulieu-BartonJ. M.WordenK.Identification of crack-tip parameters using thermoelastic isopachics and differential evolution. Key Engng Mater., 2003, 245–246, 77–86.