Effect of process parameters on microhardness and microstructure of heat affected zone in submerged arc welding

Abstract

The aim of the present work was to study the effect of flux, welding current, arc voltage, and travel speed on changes in microhardness and microstructure of the heat-affected zone (HAZ) and to optimize the process so that minimal changes occur in the material properties after completion of a submerged arc welding (SAW) process following suitable Taguchi experimental design. Micrographs of the welded samples were studied to analyse the changes in the microstructure of the material and the resultant changes in ferrite percentage, pearlite, bainite, and martensite formations. Welding current and type of flux were found to be the most significant factors leading to changes in microhardness and metallurgical properties. The microhardness tended to increase significantly with the increase of welding current from 350 to 450 Amp whereas higher hardness was observed when flux type I (basicity index 0.8) was used. Travel speed and arc voltage were found to be insignificant in relative comparison. Flux with basicity index of 0.8 showed a significantly higher microhardness compared to flux with basicity index of 1.6 (flux II). A higher amount of CaO and MgO present in flux II has a tendency to pick up carbon from steel workpiece, thus lowering the microhardness.

Keywords

SAW HAZ microhardness microstructure experimental design

References

Datta

Sundar

Bandyopadhyay

Nandi

Pal

P. K

Roy

S. C

. Effect of process parameters on mechanical properties of submerged arc butt-welding experiments and statistical modeling. Int. J. Microstrain Mater. Properties, 2007, 2, 339–360.

Tsai

H. L

Tarng

Y. S

Tseng

C. M

. Optimization of submerged arc welding process parameters in hardfacing. Int. J. Adv. Mfg Technol., 1996, 12, 402–406.

Sharma

Arora

Mishra

B. K

. Statistical modeling of deposition rate in twin-wire submerged arc welding. Proc. IMechE, Part B: J. Engineering Manufacture, 2009, 223(7), 851–863.

Tarng

Y. S

Juang

S. C

Chang

C. H

. The use of grey-based Taguchi methods to determine submerged arc welding process parameters in hardfacing. J. Mater. Process. Technol., 2002, 128, 1–6.

Datta

Bandyopadhyay

Pal

P. K

. Solving multi-criteria optimization problem in submerged arc welding consuming a mixture of fresh flux and fused slag. Int. J. Adv. Mfg Technol., 2008, 33, 935–942.

Datta

Bandyopadhyay

Pal

P. K

. Application of Taguchi philosophy for parametric optimization of bead geometry and HAZ width in submerged arc welding using a mixture of fresh flux and fused flux. Int. J. Adv. Mfg Technol., 2008, 36, 689–698.

Datta

Bandyopadhyay

Pal

P. K

. Modeling and optimization of features of bead geometry including percentage dilution in submerged arc welding using mixture of fresh flux and fused slag. Int. J. Adv. Mfg Technol., 2008, 36, 1080–1090.

Lee

J. I

Rhee

. Prediction of process parameters for gas metal arc welding by multiple regression analysis. Proc.IMechE, Part B: J. Engineering Manufacture, 2000, 214(6), 443–449.

Patnaik

Biswas

Mahapatra

S. S

. An evolutionary approach to parameter optimisation of submerged arc welding in the hardfacing process. Int. J. Mfg Res., 2007, 2, 462–483.

10.

Eroglu

Aksoy

Orhan

. Effect of coarse initial grain size on microstructure and mechanical properties of weld metal and HAZ of low carbon steel. Mater. Sci. Engng, 1999, 269, 59–66.

11.

Lee

C. S

Chandel

R. S

Seow

H. P

. Effect of welding parameters on the size of heat affected zone of submerged arc welding. Mater. Mfg Process, 2000, 15(5), 649–666.

12.

Pathak

A. K

Datta

G. L

. Three-dimensional finite element analysis to predict the different zones of microstructure in submerged arc welding. Proc. IMechE, Part B: J. Engineering Manufacture, 2004, 218(3), 269–280.

13.

Biswas

Mahapatra

M. M

Mandal

N. R

. Numerical and experimental study on prediction of thermal history and residual deformation of double-sided fillet welding. Proc. IMechE, Part B: J. Engineering Manufacture, 2010, 224(1), 125–134.

14.

. A finite element analysis of welding-induced distortion control for large box beam structures. Proc. IMechE, Part B: J. Engineering Manufacture, 2007, 221(2), 289–301.

15.

Lee

C. H

Chang

K. H

. Effect of the welding sequence in the circumferential direction on residual stress distribution in a thin-walled pipe weld. Proc. IMechE, Part B: J. Engineering Manufacture, 2009, 223(6), 723–735.

16.

Biswas

Mandal

N. R

. Thermomechanical finite element analysis and experimental investigation of single-pass single-sided submerged arc welding of C–Mn steel plates. Proc. IMechE, Part B: J. Engineering Manufacture, 2010, 224(4), 627–639.

17.

Sharma

Arora

Mishra

B. K

. Statistical modeling of deposition rate in twin-wire submerged arc welding. Proc. IMechE, Part B: J. Engineering Manufacture, 2009, 223(7), 851–863.

18.

Lucia

Voorwald

Neves

Bott

. Effects of a post weld heat treatment on a submerged arc welded ASTM A537 pressure vessel steel. J. Mater. Engng Performance, 2001, 10, 249–257.

19.

Prasad

Dwivedi

D. K

20.

Pandey

N. D

Bharti

. Effect of submerged arc welding parameters and fluxes on element transfer behaviour and weld-metal chemistry. J. Mater. Process Technol., 1994, 40, 195–211.

21.

Devis

M. L. E

. How submerged arc flux composition influence element transfer. Weld Pool Chem. Metallurgy, 1980, 8, 289–310.

22.

Mcpherson

N. A

Baker

T. N

Millar

D. W

. A study of the structure of dissimilar submerged arc welds. Metall. Mater. Trans., 1998, 29, 823–832.

23.

Kanjilal

Pal

T. K

Majumdar

S. K

. Combined effect of flux and welding parameters on chemical composition and mechanical properties of submerged arc weld metal. J. Mater. Process. Technol., 2006, 171, 223–231.

24.

Mercado

Víctor

López

Arturo

Sanchezand

Maribel

Saucedo

. Effect of active and non active fluxes on the mechanical properties and microstructure in submerged arc welds of A-36 steel plates. Mater. Mfg Process, 2007, 22, 295–297.

25.

Ross

P. J

. Taguchi technique for quality engineering, (McGraw Hill, New York).