Determining the Low-Temperature Fracture Toughness of Asphalt Mixtures

Abstract

There has been a sustained effort in applying fracture mechanics concepts to crack formation and propagation in bituminous pavement materials. Adequate fracture resistance is an essential requirement for asphalt pavements built in the northern part of the United States and Canada, for which the prevailing failure mode is cracking due to low-temperature shrinkage stresses. The current Superpave^® specifications address this issue mainly through the use of strength tests on unnotched (smooth boundary) specimens. However, recent studies have shown the limitations of this approach and have suggested that fracture mechanics concepts, based on tests performed on notched samples, should be used instead. Research in progress at the University of Minnesota investigates the use of fracture mechanics principles to determine the low-temperature fracture properties of asphalt mixtures. A testing protocol is presented that makes it possible to obtain multiple measurements of fracture toughness as a function of crack propagation based on the compliance method to measure crack length. An increase in fracture toughness with crack length is observed, which is consistent with the behavior displayed by other brittle materials. The plateau of the curves may be representative of the asphalt concrete resistance to fracture, because the initial values can be significantly influenced by the presence of the inelastic zone at the crack tip.

Get full access to this article

View all access options for this article.

References

Dongre

, Sharma

M. G.

, and Anderson

D. A.

. Development of Fracture Criterion for Asphalt Mixes at Low Temperatures. In Transportation Research Record 1228, TRB, National Research Council, Washington, D.C., 1989. pp. 94–105.

Lee

N. K.

, and Hesp

S. A. M.

. Low-Temperature Fracture Toughness of Polyethylene-Modified Asphalt Binders. In Transportation Research Record 1436, TRB, National Research Council, Washington, D.C., 1994. pp. 54–59.

Lee

N. K.

, Morrison

G. R.

, and Hesp

S. A.

. Low Temperature Fracture of Polyethylene-Modified Asphalt Binders and Asphalt Concrete Mixes. Journal of the Association of Asphalt Paving Technologists, Vol. 64, 1995. pp. 534–574.

Champion

, Gerard

J. F.

, Planche

J.-P.

, Martin

, and Anderson

D. A.

. Low-Temperature Rheological and Fracture Properties of Polymer-Modified Bitumens. Proc., 2nd Eurasphalt and Eurobitume Congress, Barcelona, Spain, 2000.

Anderson

D. A.

, Lapalu

, Le Hir

Y. M.

, Marasteanu

M. O.

, Martin

, and Planche

J. P.

. Low-Temperature Thermal Cracking of Asphalt Binders as Ranked by Strength and Fracture Properties. In Transportation Research Record: Journal of the Transportation Research Board, No. 1766, TRB, National Research Council, Washington, D.C., 2001. pp. 1–6.

Roy

S. D.

, and Hesp

S. A. M.

. Fracture Energy and Critical Crack Tip Opening Displacement: Fracture Mechanics Based Failure Criteria for Low-Temperature Grading of Asphalt Binders. Journal of the Canadian Association of Asphalt Paving Technologists (in press), 2002.

Wells

A. A.

Unstable Crack Propagation in Metals. Proceedings of the Crack Propagation Symposium, The College of Aeronautics, Cranfield, England, 1962.

Ewalds

H. L.

, and Wanhill

R. J. H.

. Fracture Mechanics. Delft University Press, Delft, Netherlands, 1985.

Roque

, Zhang

, and Sankar

. Determination of Crack Growth Rate Parameters of Asphalt Mixtures Using the Superpave IDT. Journal of the Association of Asphalt Paving Technologists, Vol. 68, 1999. pp. 404–433.

10.

Zhang

, Roque

, and Birgisson

. Evaluation of Laboratory-Measured Crack Growth Rate for Asphalt Mixtures. In Transportation Research Record: Journal of the Transportation Research Board, No. 1767, TRB, National Research Council, Washington, D.C., 2001. pp. 67–75.

11.

Labuz

F. J.

, and Dai

. Cracking of Asphalt Concrete at Low Temperatures. Final Report. Minnesota Department of Transportation, St. Paul, Oct. 1994.

12.

Mobasher

, Mamlouk

M. S.

, and Lin

H.-M.

. Evaluation of Crack Propagation Properties of Asphalt Mixtures. Journal of Transportation Engineering, Vol. 123, No. 5, 1997. pp. 405–413.

13.

Schmidt

R. A.

Fracture Toughness Testing of Limestone. Experimental Mechanics, Vol. 16, 1976. pp. 161–167.

14.

Schmidt

R. A.

, and Lutz

T. J.

. _K and _J of Westerly Granite—Effects of Thickness and In-Plane Dimensions. Fracture Mechanics Applied to Brittle Materials. ASTM STP 678. ASTM, Philadelphia, 1979. pp. 166–182.

15.

Irwin

G. R.

, and Kies

J. A.

. Critical Energy Rate Analysis of Fracture Strength. Welding Research Supplement, Vol. 19, 1954. pp. 193–198.

16.

Sokolnikoff

I. S.

Theory of Elasticity. McGraw-Hill, New York, 1956.

17.

Molenaar

J. M. M.

, and Molenaar

A. A. A.

. Fracture Toughness of Asphalt in the Semi-Circular Bend Test. 2000 Eurasphalt and Eurobitume Congress, Barcelona, Spain, 2000.

18.

Labuz

J. F.

, Shah

S. P.

, and Dowding

C. H.

. Experimental Analysis of Crack Propagation in Granite. International Journal of Rock Mechanics and Mining Sciences, Vol. 22, No. 2, 1985. pp. 85–98.