Basaltic Crushed Rock Stabilized with Cementitious Additives: Compressive Strength and Stiffness,Drying Shrinkage,and Capillary Flow Characteristics

Abstract

Research was undertaken to increase knowledge of the properties of local stabilized pavement materials to facilitate their wider use in road construction and rehabilitation. Laboratory tests involved testing for the unconfined compressive strength (UCS), shrinkage, and capillary behavior of crushed basaltic rocks stabilized with two conventional cementitious binders—general purpose cement and lime—and two cementitious binders comprising industrial waste products—blended cement and alkali-activated slag. The alkali-activated slag and blended cement significantly increased UCS of untreated material and performed as well as or better than such traditional binders as general purpose cement. Overall, lime performed poorly as a stabilizer of crushed basaltic rocks, primarily because the fine content containing clay minerals was not significant in the crushed basaltic rock composition. UCS of stabilized materials increased significantly as binder content increased; UCS could be described as a function of binder quantity. Ultimate shrinkage increased with binder content for general purpose cement and alkali-activated slag, but for blended cement, behavior was different. The rate of drying shrinkage was relatively high at the early stage of shrinkage. Generally, alkali-activated slag produced less shrinkage compared with general purpose and blended cements. Capillary rise and water absorption were also measured. Test results indicated that the rate of capillary rise and amount of water absorbed by the material matrix decreased with the increase of binder content. The research indicated that the use of binders with industrial by-products could be a viable option in stabilization of crushed basaltic rock materials.

Get full access to this article

View all access options for this article.

References

A Guide to the Structural Design of Road Pavements. Austroads Inc., Haymarket, New South Wales, Australia, 1992.

Chakrabarti

, Kodikara

, and Pardo

. An Overview of Stabilization Methods and Performance of Local Government Roads in Australia. Proc., First International Symposium on Subgrade Stabilisation and In Situ Pavement Recycling Using Cement, Salamanca, Spain, Oct. 2001.

Colombier

Cracking in Pavements: Nature and Origin of Cracks. Prevention of Reflective Cracking in Pavements, E&FN Spon, London, 1997.

Nakayama

, and Handy

R. L.

. Factors Influencing Shrinkage of Soil-Cement. In Highway Research Record 86, HRB, National Research Council, Washington, D.C., 1965, pp. 15–27.

Guide to Stabilization in Roadworks. Austroads Inc., Haymarket, New South Wales, Australia, 1998.

Neville

A. M.

Cementitious Materials—A Different Viewpoint. American Concrete International, July 1994.

Serruto

, and Pardo

. Evaluation of Stabilized Marginal Pavement Materials Using Established and Newly Developed Cementitious Binders. Proc., 20th Conference Australian Road Research Board, Melbourne, March 2001.

Standards Australia. Determination of the Dry Density/Moisture Content Relation of a Soil Using Standard Compactive Effort. AS 1289.5.1.1. Sydney, Australia, 1993.

Standards Australia. Determination of the Soil Particle Density of Combined Soil Fraction–Vacuum Pycnometer Method. AS 1289.3.5.2. Sydney, Australia, 1995.

10.

Standards Australia. Determination of the Linear Shrinkage of a Soil-Standard Method. AS 1289.3.4.1. Sydney, Australia, 1995.

11.

Standards Australia. Determination of the Cone Liquid Limit of a Soil. AS 1289.3.9. Sydney, Australia, 1991.

12.

Standards Australia. Determination of the Plastic Limit of a Soil-Standard Method. AS 1289.3.2.1. Sydney, Australia, 1995.

13.

Standards Australia. Unconfined Compressive Strength of Compacted Materials. AS 1141.51. Sydney, Australia, 1996.

14.

George

K. P.

Shrinkage Characteristics of Soil-Cement Mixtures. Highway Research Record 255, HRB, National Research Council, Washington, D.C., 1968, pp. 42–58.

15.

Rawlings

R. E.

, Williams

D. J.

, and Gordon

R. G.

. Laboratory and Field Comparisons of Cement-Treated Paving Materials. Proc., 14th Australian Road Research Board (ARRB) Conference, Canberra, Vol. 14, Part 7, 1988.

16.

Standards Australia. Determination of the Drying Shrinkage of Concrete for Samples. AS 1012.13. Sydney, Australia, 1992.

17.

Standards Australia. Absorption, Swell and Capillary Rise of Compacted Materials. AS 1141.53. Sydney, Australia, 1996.

18.

Mohammad

L. N.

, Raghavandra

, and Huang

. Laboratory Performance Evaluation of Cement-Stabilized Soil Base Mixtures. In Transportation Research Record: Journal of the Transportation Research Board, No. 1721, TRB, National Research Council, Washington, D.C., 2000, pp. 19–28.

19.

Wilmot

, and Vorobieff

. Australian Experience on Subgrade Stabilization and Pavement Recycling. Proc., First International Symposium on Subgrade Stabilisation and In Situ Pavement Recycling Using Cement, Salamanca, Spain, Oct. 2001.

20.

Little

D. N.

Handbook for Stabilization of Pavement Subgrades and Base Courses with Lime. Kendall/Hunt Publishing Company, Dubuque, Iowa, 1995.

21.

Developments in Road Stabilization. Proc., Joint VicRoads and AusStab Technology Transfer Seminar for Austroads NT&E Project 01. Australian Stabilisation Industry Association. Melbourne, Victoria, Aug. 2001.