Fatigue Behavior of Prestressed Tubular Bridge Deck of Fiber-Reinforced Polymer

Abstract

An experimental study was undertaken to assess the flexural fatigue performance of a new deck system of fiber-reinforced polymer (FRP) that has been installed on a bridge in Delaware County, Ohio. The deck consists of a series of 4-in. (102-mm) square pultruded FRP tubes with a thickness of 1/4 in. (6.4 mm), laid side by side on existing stringers, perpendicular to the direction of traffic. The tubes are posttensioned up to 20 kips (90 kN) with 0.6-in. (15-mm) diameter seven-wire strands at midpoints between the stringers in the direction of traffic. Four double-span FRP deck specimens with two different tube sizes and three different span lengths were tested in flexural fatigue under AASHTO-prescribed footprint of wheel loads for an HS20 truck. Panel action in the deck system was inadequate for the most part, as only the tubes that were directly under the load carried the majority of the load. Subsequent slippage between these tubes and their adjacent tubes can cause cracking in the asphalt overlay. However, no such crack has been observed on the actual bridge after 1 year in service. Panel action is generally improved at higher prestress levels. Prestressing also offers additional redundancy and reserve strength for the system. While longer span decks fail in bending, shorter span decks generally suffer from local shear failure as a result of stress concentrations at the corner of the tubes under the applied load or at the support. The fatigue problem is less critical for longer span decks and smaller tube sizes.

Get full access to this article

View all access options for this article.

References

Standard Specifications for Highway Bridges, 17th ed. American Association of Highway and Transportation Officials, Washington, D.C., 2003.

Brinson

H. F.

A Nonlinear Visco-elastic Approach to Durability Predictions for Polymer Based Composite Structures. Durability of Polymer Based Composite Systems for Structural Applications ( Cardon

A. H.

and Verchery

, eds.). Kluwer Academic Publishers, Dordrecht, Netherlands, 1991, pp. 46–64.

Product Selection Guide: FRP Composite Product for Bridge Applications (CD-ROM). Market Development Alliance of the FRP Composites Industry, Harrison, N.Y., 2000.

Technical Data for TechDeck System. Fiber Reinforced Systems, Columbus, Ohio, 2000.

Karbhari

V. M.

, Chin

J. W.

, and Reynaud

. Critical Gaps in Durability Data for FRP Composites in Civil Infrastructure. Proceedings of the International SAMPE Symposium and Exhibition, Vol. 45, No. 1, 2000, pp. 549–563.

Shekar

, Petro

S. H.

, and GangaRao

H. V. S.

. Construction of Fiber-Reinforced Plastic Modular Decks for Highway Bridges. In Transportation Research Record: Journal of the Transportation Research Board, No. 1813, TRB, National Research Council, Washington, D.C., 2002, pp. 203–209.

Kumar

S. V.

, and GangaRao

H. V. S.

. Fatigue Response of Concrete Decks Reinforced with FRP Rebars. Journal of Structural Engineering, ASCE, Vol. 124, No. 1, Jan. 1998, pp. 11–16.

Senne

J. L.

, Lesko

J. J.

, Case

S. W.

, and Cousins

. Development of a Life Prediction Methodology for Hybrid FRP Beams for Deck/Girder Bridges. Proceedings of the International SAMPE Symposium and Exhibition, Vol. 45, No. I, 2000, pp. 916–927.

Dutta

, Kwon

S.-C.

, and Lopez-Anido

. Fatigue Performance Evaluation of Fiber-Reinforced Plastics Composite Bridge Deck Prototypes Under High and Low Temperatures. Presented at 82nd Annual Meeting of the Transportation Research Board, Washington, D.C., 2003.

10.

Prestressed FRP Tubular Deck System. M.S. thesis. North Carolina State University, Raleigh, 2003.