Polymer porous scaffolds and hydrogels have been separately employed and explored for a wide range of applications including cell encapsulation, drug delivery, and tissue engineering.
Methods
In this study, a three-dimensional poly (L-lactic acid) (PLLA) scaffold with interconnected and homogeneously distributed pores was fabricated to support the alginate hydrogel (Alg). The gels were filled into the porous scaffold, which acted as an analogue of native extracellular matrix (ECM) for entrapment of cells within a support of predefined shape. The mechanical strength of the composite scaffold was characterized by compression testing. The chondrocyte behavior in the scaffold was determined by inverted microscopy, scanning electron microscopy (SEM) and MTT viability assay. The repair efficiency of such a composite scaffold was further investigated in dog spinal defects by histological evaluation after implantation for 4 weeks.
Results
Results showed that the composite scaffold possessed superior mechanical properties and hierarchical porous structure in comparison to pure Alg. Cell culture revealed that the cells presented a specific cartilage status in the composite scaffold in line with higher adherence and proliferation ratio. The histological analyses suggested that the composite scaffold substantially promotes its integration in the host tissue accompanied with a low inflammatory reaction and new tissue formation.
Conclusions
The method thus provides a useful pathway for scaffold preparation that can simultaneously achieve suitable mechanical properties and good biocompatibility.
AstiA., GioglioL.Natural and synthetic biodegradable polymers: different scaffolds for cell expansion and tissue formation.Int J Artif Organs.2014; 37(3): 187–205.
2.
RezwanK., ChenQ.Z., BlakerJ.J., BoccacciniA.R.Biodegradable and bioactive porous polymer/inorganic composite scaffolds for bone tissue engineering.Biomaterials.2006; 27(18): 3413–3431.
3.
ManoJ.F., SousaR.A., BoeselL.F., NevesN.M., ReisR.L.Bioinert, biodegradable and injectable polymeric matrix composites for hard tissue replacement: State of the art and recent developments.Compos Sci Technol.2004; 64(6): 789–817.
4.
CuiN., QianJ., LiuT., ZhaoN., WangH.Hyaluronic acid hydrogel scaffolds with a triple degradation behavior for bone tissue engineering.Carbohydr Polym.2015; 126: 192–198.
5.
MöllerL., KrauseA., DahlmannJ., GruhI., KirschningA., DrägerG.Preparation and evaluation of hydrogel-composites from methacrylated hyaluronic acid, alginate, and gelatin for tissue engineering.Int J Artif Organs.2011; 34(2): 93–102.
6.
GüntherM.I., WeidnerN., MüllerR., BleschA.Cell-seeded alginate hydrogel scaffolds promote directed linear axonal regeneration in the injured rat spinal cord.Acta Biomater.2015; 27: 140–150.
7.
LindenhaynK., PerkaC., SpitzerR.. Retention of hyaluronic acid in alginate beads: aspects for in vitro cartilage engineering.J Biomed Mater Res., Part A.1999; 44(2): 149–155.
8.
GrigoloB., LisignoliG., PiacentiniA.. Evidence for redifferentiation of human chondrocytes grown on a hyaluronan-based biomaterial (HYAff 11): molecular, immunohistochemical and ultrastructural analysis.Biomaterials.2002; 23(4): 1187–1195.
9.
DruryJ.L., MooneyD.J.Hydrogels for tissue engineering: scaffold design variables and applications.Biomaterials.2003; 24(24): 4337–4351.
10.
WuL.Q., BentleyW.E., PayneG.F.Biofabrication with biopolymers and enzymes: potential for constructing scaffolds from soft matter.Int J Artif Organs.2011; 34(2): 215–224.
11.
JensenB.E., EdlundK., ZelikinA.N.Micro-structured, spontaneously eroding hydrogels accelerate endothelialization through presentation of conjugated growth factors.Biomaterials.2015; 49: 113–124.
12.
HashimotoT., SuzukiY., TaniharaM., KakimaruY., SuzukiK.Development of alginate wound dressings linked with hybrid peptides derived from laminin and elastin.Biomaterials.2004; 25(7-8): 1407–1414.
13.
FragonasE., ValenteM., Pozzi-MucelliM.. Articular cartilage repair in rabbits by using suspensions of allogenic chondrocytes in alginate.Biomaterials.2000; 21(8): 795–801.
14.
UeyamaY., IshikawaK., ManoT.. Usefulness as guided bone regeneration membrane of the alginate membrane.Biomaterials.2002; 23(9): 2027–2033.
15.
DarA., ShacharM., LeorJ., CohenS.Optimization of cardiac cell seeding and distribution in 3D porous alginate scaffolds.Biotechnol Bioeng.2002; 80(3): 305–312.
16.
BidarraS.J., BarriasC.C., GranjaP.L.Injectable alginate hydrogels for cell delivery in tissue engineering.Acta Biomater.2014; 10(4): 1646–1662.
17.
WangL., SheltonR.M., CooperP.R., LawsonM., TriffittJ.T., BarraletJ.E.Evaluation of sodium alginate for bone marrow cell tissue engineering.Biomaterials.2003; 24(20): 3475–3481.
18.
GüntherMl, WeidnerN., MüllerR., BleschA.Cell-seeded alginate hydrogel scaffolds promote directed linear axonal regeneration in the injured rat spinal cord.Acta Biomater.2015; 27: 140–150.
19.
ParkH., LeeK.Y.Facile control of RGD-alginate/hyaluronate hydrogel formation for cartilage regeneration.Carbohydr Polym.2011; 86(30): 1107–1112.
20.
ZhaoL., WeirM.D., XuH.H.An injectable calcium phosphate-alginate hydrogel-umbilical cord mesenchymal stem cell paste for bone tissue engineering.Biomaterials.2010; 31(25): 6502–6510.
RajkumarM., MeenakshisundaramN., RajendranV.Development of nanocomposites based on hydroxyapatite/sodium alginate: Synthesis and characterization.Mater Charact.2011; 62(5): 469–479.
23.
LohmannC.H., SchwartzZ., NiederauerG.G., CarnesD.L.Jr., DeanD.D., BoyanB.D.Pretreatment with platelet derived growth factor-BB modulates the ability of costochondral resting zone chondrocytes incorporated into PLA/PGA scaffolds to form new cartilage in vivo.Biomaterials.2000; 21(1): 49–61.
ZhaoM., LiL., LiX., ZhouC., LiB.Three-dimensional honeycomb-patterned chitosan/poly(L-lactic acid) scaffolds with improved mechanical and cell compatibility.J Biomed Mater Res., Part A.2011; 98A(3): 434–441.
26.
ZhaoM., LiL., LiB., WuD., ZhouC., TianY.A Comparative Study of Fibroblast Behaviors under Cyclic Stress Stimulus and Static Culture on 3D Patterned Matrix.J Bionic Eng.2013; 10(2): 148–155.
27.
CoreyJ.M., GertzC.C., WangB.S.. The design of electrospun PLLA nanofiber scaffolds compatible with serum-free growth of primary motor and sensory neurons.Acta Biomater.2008; 4(4): 863–875.
28.
LouT., WangX., SongG., GuZ., YangZ.Fabrication of PLLA/β-TCP nanocomposite scaffolds with hierarchical porosity for bone tissue engineering.Int J Biol Macromol.2014; 69: 464–470.
29.
BaldinoL., NaddeoF., CardeaS., NaddeoA., ReverchonE.FEM modeling of the reinforcement mechanism of Hydroxyapatite in PLLA scaffolds produced by supercritical drying, for Tissue Engineering applications.J Mech Behav Biomed Mater.2015; 51: 225–236.
30.
LiuZ-M, LeeS-Y, SarunS., PeschelD., GrothT.Immobilization of poly (ethylene imine) on poly (L-lactide) promotes MG63 cell proliferation and function.J Mater Sci Mater Med.2009; 20(11): 2317–2326.
31.
HäuselmannH.J., FernandesR.J., MokS.S.. Phenotypic stability of bovine articular chondrocytes after long-term culture in alginate beads.J Cell Sci.1994; 107(Pt 1): 17–27.
32.
van SusanteJ.L., BumaP., van OschG.J.. Culture of chondrocytes in alginate and collagen carrier gels.Acta Orthop Scand.1995; 66(6): 549–556.
33.
ZhaoM., LiL., ZhouC., LuL.Preparation and characterization of calcium alginate hydrogels as injectable cartilage scaffolds.Gongneng Cailiao/Journal of Functional Materials.2010; 8: 1353–1356. [Article in Chinese].
34.
HildebrandT., LaibA., MüllerR., DequekerJ., RüegseggerP.Direct three-dimensional morphometric analysis of human cancellous bone: microstructural data from spine, femur, iliac crest, and calcaneus.J Bone Miner Res.1999; 14(7): 1167–1174.
35.
IgnjatovićN., SavićV., NajmanS., PlavgićM., UskokovićD.A study of HAp/PLLA composite as a substitute for bone powder, using FT-IR spectroscopy.Biomaterials.2001; 22(6): 571–575.
36.
RescignanoN., González-AlfaroY., FantechiE.. Design, development and characterization of a nanomagnetic system based on iron oxide nanoparticles encapsulated in PLLA-nanospheres.Eur Polym J.2015; 62: 145–154.
37.
ShuT., LuP., HeN.Mercury adsorption of modified mulberry twig chars in a simulated flue gas.Bioresour Technol.2013; 136: 182–187.
38.
XuS., WangZ., GaoY., ZhangS., WuK.Adsorption of Rare Earths(III) Using an Efficient Sodium Alginate Hydrogel Cross-Linked with Poly-γ-Glutamate.PLoS One.2015; 10(5): e0124826.
39.
OseniA.O., CrowleyC., BolandM.Z., ButlerP.E., SeifalianA.M.Cartilage Tissue Engineering: the Application of Nanomaterials and Stem Cell Technology. In: EberliD., ed. Tissue Engineering for Tissue and Organ Regeneration.Intech, 2011; 233–266.