Conductive ceramic composite was prepared by sintering the mixture of clay and printer toner at 1050°C and in the N2 atmosphere. The microstructure and mineral phases of the ceramic composite were characterised by SEM, EDX, TG and XRD, and its electrical conductivity and mechanical properties were also investigated. The results show that, in the sintering process, a series of physical and chemical reactions take place, and mineral phases with excellent electrical conductivity, such as metal iron, carbon and Fe–Al solid solution material, are formed. The electrical conductivity mechanism can be explained by the percolation theory. The threshold value for electrical conductive percolation is between 3.5 and 7.0 wt-%. At the content of printer toner 10 wt-%, the volume electrical resistance of the ceramic composite is as low as 8.5 Ω cm, and the composite exhibits excellent flexural strength higher than 14 MPa.
GuoZ, BluganG, GrauleT, The effect of different sintering additives on the electrical and oxidation properties of Si3N4–MoSi2 composites. J Eur Ceram Soc. 2007;27(5):2153–2161. doi: 10.1016/j.jeurceramsoc.2006.07.009
PatankarSN, McAllisterSD, ChengIF, Conductive ceramic coating on polyacrylonitrile–vinyl chloride (modacrylic) discontinuous fibers via electroless deposition. J Power Sour. 2010;195(1):362–366. doi: 10.1016/j.jpowsour.2009.07.010
4.
KishimotoA, MoritaM, AsaokaH, Using ion exchange to control the mechanical strength of Naβ-alumina ceramics. Solid State Ionics. 2006;177(9–10):949–953. doi: 10.1016/j.ssi.2005.12.033
5.
MehrotraAK, MaitiHS, SubbaraoEC. Electrical conductivity of pure and CaO-doped ThO2 ceramics. Mater Res Bull. 1973;8(8):899–907. doi: 10.1016/0025-5408(73)90074-3
6.
MonteverdeF, BellosiA, ScatteiaL. Processing and properties of ultra-high temperature ceramics for space applications. Mater Sci Eng A. 2008;485(1):415–421. doi: 10.1016/j.msea.2007.08.054
ParkCO, AkbarSA. Ceramics for chemical sensing. J Mater Sci. 2003;38(23):4611–4637.
9.
FangG, LiD, YaoB. Fabrication and characterization of transparent conductive ZnO:Al thin films prepared by direct current magnetron sputtering with highly conductive ZnO(ZnAl2O4) ceramic target. J Cryst Growth. 2003;247(3–4):393–400. doi: 10.1016/S0022-0248(02)02012-2
10.
FaridET. New double negative and positive temperature coefficients of conductive EPDM rubber TiC ceramic composites. Eur Polym J. 2002;38(3):567–577. doi: 10.1016/S0014-3057(01)00208-7
11.
PumeraM, MerkociA, AlegretS. Carbon nanotube-epoxy composites for electrochemical sensing. Sens Actuators B. 2006;113(2):617–622. doi: 10.1016/j.snb.2005.07.010
12.
MastragostinoM, ArbizzaniC, SoaviF. Conducting polymers as electrode materials in supercapacitors. Solid State Ionics. 2002;148(3):493–498. doi: 10.1016/S0167-2738(02)00093-0
13.
BadiniC, FinoP, OrtonaA, High temperature oxidation of multilayered SiC processed by tape casting and sintering. J Eur Ceram Soc. 2002;22(12):2071–2079. doi: 10.1016/S0955-2219(01)00520-9
14.
BaudS, ThevenotF, ChatillonC. High temperature sintering of SiC with oxide additives: IV. Powder beds and the influence of vaporization on the behaviour of SiC compacts. J Eur Ceram Soc. 2003;23(1):29–36. doi: 10.1016/S0955-2219(02)00070-5
15.
LiJ, PengJ, GuoS, Application of response surface methodology (RSM) for optimization of sintering process for the preparation of magnesia partially stabilized zirconia (Mg-PSZ) using natural baddeleyite as starting material. Ceram Int. 2013;39(1):197–202. doi: 10.1016/j.ceramint.2012.06.009
MoriM, HieiY and SammesNM. Sintering behavior of Ca- or Sr-doped LaCrO3 perovskites including second phase of AECrO4 (AE=Sr, Ca) in air. Solid State Ion. 2000;135(1–4):743–748. doi: 10.1016/S0167-2738(00)00372-6
18.
WangZ, KongY, YaoC, A sensitive o-aminophenol sensor based on a modified montmorillonite-modified expanded graphite electrode. Appl Clay Sci. 2012;55(1):173–176. doi: 10.1016/j.clay.2011.11.017
19.
InamF, YanH, ReeceMJ, Structural and chemical stability of multiwall carbon nanotubes in sintered ceramic nanocomposite. Adv Appl Ceram. 2010;109(4):240–247. doi: 10.1179/174367509X12595778633336
ZhouY, PervinF, RangariVK, Influence of montmorillonite clay on the thermal and mechanical properties of conventional carbon fiber reinforced composites. J Mater Process Technol. 2007;191(1–3):347–351. doi: 10.1016/j.jmatprotec.2007.03.059
22.
Alcaniz-MoengeJA, Cazorla-AmorosD, Linares-SolanoA, Preparation of conductive carbon-ceramic composites from coal tar pitch and ceramic monoliths. Carbon. 1998;36(7–8):1003–1009. doi: 10.1016/S0008-6223(97)00233-9
23.
AlvarezED, LaffitaYM, RuizER, High conducting sepiolite–graphenelike carbon nanocomposite from sugar residual as carbon source. Adv Appl Ceram. 2012;111(8):508–511. doi: 10.1179/1743676112Y.0000000036
24.
KanbaraT, YamamotoT. Preparation and characterization of porous and electrically conducting carbon-clay composites. J Mater Sci. 1989;24(5):1552–1558. doi: 10.1007/BF01105670
25.
BondarAM, IordacheI. Carbon/ceramic composites designed for electrical application. J Optoelectron Adv Mater. 2006;8(2):631–637.
26.
BluganG, MichalkovaM, HnatkoM, Processing and properties of alumina–carbon nano fibre ceramic composites using standard ceramic technology. Ceram Int. 2011;37(8):3371–3379. doi: 10.1016/j.ceramint.2011.05.139
27.
TangQ, GongJ. Effect of porosity on the microhardness testing of brittle ceramics: a case study on the system of NiO–ZrO2. Ceram Int. 2013;39(8):8751–8759. doi: 10.1016/j.ceramint.2013.04.061