Graphite fiber composites interlayered with single-walled carbon nanotubes

Abstract

A scalable processing method was used to fabricate graphite fiber composites with single-walled carbon nanotubes (SWCNTs) and the microstructures and properties of the fabricated laminates were investigated. SWCNTs were sprayed onto the surface of graphite/epoxy prepreg using an air spray. Interlaminar shear strength (ILSS) tests showed that the air spray processing had minimal effect on the quality of the laminates. Scanning electron microscopy (SEM) studies showed that SWCNTs are distributed uniformly in the plane of the laminate but not in the thickness direction due to low resin flow during cure. At high concentrations (>1.0 wt%), combination of a rather thick band of SWCNTs and low resin flow caused lack of resin inside of SWCNT bundles. The properties positively affected are in-plane shear strength, interlaminar fracture toughness (mode I), compressive strength, and electrical conductivity. Those properties showed improvement particularly when a lower concentration of SWCNTs was used. Fractography study using SEM showed altered crack propagation and crack bridging due to the presence of SWCNTs. The out-of-plane electrical conductivity was improved by 144% for 2 wt% SWCNT samples compared to samples without SWCNTs.

Keywords

nanocomposites carbon nanotubes carbon fibers mechanical properties electrical properties

Get full access to this article

View all access options for this article.

References

Ajayan PM , Schadler LS and Braunet PV Nanocomposite science and technology. Weinheim : Wiley-VCH, 2003.

Nalwa HS Polymeric nanostructure and their applications. Vol. 1, Stevenson Ranch, CA: American Scientific Publishers, 2007.

Coleman JN , Khan U. and Gun’ko YK Mechanical reinforcement of polymers using carbon nanotubes. Adv Mater 2006; 18(6): 689-706.

Hu Y. , Shenderova OA , Hu Z. , Padgett CW and Brenner DW Carbon nanostructures for advanced composites. Rep Prog Phys 2006; 69(6): 1847-1895.

Tjong SC Structural and mechanical properties of polymer nanocomposites. Mater Sci Eng R 2006; 53(3-4): 73-197.

Coleman JN , Khana U. , Blaua WJ and Gun’ko YK Small but strong: a review of the mechanical properties of carbon nanotube-polymer composites. Carbon 2006; 44(9): 1624-1652.

Esawi AMK and Farag MM Carbon nanotube reinforced composites: potential and current challenges. Mater Des 2007; 28(9): 2394-2401.

Gojny FH , Wichmann MHG , Fiedler B. , Bauhofer W. and Schulte K. Influence of nano-modification on the mechanical and electrical properties of conventional fibre-reinforced composites. Composites: Part A 2005; 36(11): 1525-1535.

Wichmann MHG , Sumfleth J. , Gojny FH , Quaresimin M. , Fiedler B. and Schulte K. Glass-fibre-reinforced composites with enhanced mechanical and electrical properties - benefits and limitations of a nanoparticle modified matrix. Eng Fract Mech 2006; 73(16): 2346-2359.

10.

Zhu J. , Imam A. , Crane R. , Lozano K. , Khabashesku VN and Barrera EV Processing a glass fiber reinforced vinyl ester composite with nanotube enhancement of interlaminar shear strength. Comp Sci Tech 2007; 67(7-8): 1509-1517.

11.

Adhikari K. , Hubert P. , Simard B. and Johnston A. Effect of the localized application of SWNT modified epoxy on the interlaminar shear strength of carbon fibre laminates. In: Proceedings of the 47th AIAA/ASME/ASCE/AHS/ ASC Structures, Structural Dynamics, and Materials Conference, Newport, Rhode Island, 2006.

12.

Veedu VP , Cao A. , Li X. , Ma K. , Soldano C. , Kar S. , et al. Multifunctional composites using reinforced laminae with carbon-nanotube forests. Nature Mater 2006; 5: 457-462.

13.

Garcia EJ , Wardle BL , Hart AJ and Yamamoto N. Fabrication and multifunctional properties of a hybrid laminate with aligned carbon nanotubes grown In Situ. Comp Sci Tech 2008; 68(9): 2034-2041.

14.

Bekyarova E. , Thostenson ET , Yu A. , Kim H. , Gao J. , Tang J. , et al. Multiscale carbon nanotube-carbon fiber reinforcement for advanced epoxy composites. Langmuir 2007; 23(7): 3970-3974.

15.

Qiu J. , Zhang C. , Wang B. and Liang R. Carbon nanotube integrated multifunctional multiscale composites. Nanotechnology 2007; 18(27): 275708(11pp).

16.

Chen W. , Shen H. , Auad ML , Huang C. and Nutt S. Basalt fiber-epoxy laminates with functionalized multi-walled carbon nanotubes . Composites: Part A 2009; 40: 1082-1089.

17.

Zhao B. , Hu H. , Yu A. , Perea D. and Haddon R. Synthesis and characterization of water soluble single-walled carbon nanotube graft copolymers. J Am Chem Soc 2005 ; 127: 8197-8203.

18.

Daniel IM and Ishai O. Engineering mechanics of composite materials. New York : Oxford University Press, 1994.

19.

Khare R. and Bose S. Carbon nanotube based composites - a review. J Miner Mater Charact Eng 2005; 4(1): 31-46.

20.

Boeing Specification Support Standard BSS 7260. Advanced Composite Compression Tests. Seattle, Washington: The Boeing Company, 1988.

21.

Stellbrink KKU. Micromechanics of composites: composite properties of fibre and matrix constituents . Munich: Hanser Publishers , 1996.

22.

Piggott MR Load-bearing fibre composites. Oxford: Pergamon Press, 1980.

23.

Rosen BW Fiber composite materials. Materials Park, OH: American Society of Metals, 1965.

24.

Ajayan PM , Schadler LS , Giannaris C. and Rubio A. Single-walled carbon nanotube - polymer composites: strength and weakness . Adv Mater 2000; 12(10): 750-753.

25.

Ezquerra TA , Connor MT , Roy S. , Kulescza M. , Fernandes-Nascimento J. and Baltá-Calleja FJ Alternating-current electrical properties of graphite, carbon-black and carbon fiber polymering composites. Compos Sci Technol 2001; 61(6): 903-909.

26.

Kim H. and Hahn HT Graphite nanoplatelets interlayered carbon/epoxy composites. AIAA Journal 2009; 47(11): 2779-2784.