The effects of glass weave on the low temperature flexure properties of composite laminates

Abstract

A variety of glass fiber weaves are being considered for use in insulation materials in the International Thermonuclear Experimental Reactor central solenoid. In this study, three candidate glass weaves (1581, 7781, and 38050) were used with a Di-Glycidyl Ether of Bisphenol F (DGEBF) anhydride epoxy matrix to produce composite laminates of constant thickness. These laminates were compared at room temperature (295 K) and liquid nitrogen temperature (77 K) via three-point flexure tests. The material variables among these glass products were type of weave pattern (eight-harness satin versus plain), fiber surface treatment (epoxy compatible surface treatment versus no treatment), and cloth areal density. Based on the flexural elastic modulus and strength data at both 77 K and 295 K, the 7781/epoxy composites showed the highest values followed closely by 1581/epoxy. The 38050/epoxy performed quite poorly. The correlations of the laminate density with modulus and strength at both temperatures were almost linear. It was also found that the failure modes of samples having fibers with epoxy compatible surface treatment differed from those having no surface treatment.

Keywords

Composite laminates insulation materials flexure tests glass/epoxy fusion energy International Thermonuclear Experimental Reactor

Get full access to this article

View all access options for this article.

References

Scultz JL, Antaya T, Feng J, et al. The ITER central solenoid, In: 21^st IEE/NPS Symposium on Fusion Engineering, Knoxville, TN, September, 2005.

Madhukar

Drzal

. Fiber-matrix adhesion and its effect of composite mechanical properties: II. Longitudinal (0°) and transverse (90°) tensile and flexure behavior of graphite/epoxy composites. J Composite Materials 1991; 25: 958–991.

Thomason

Schoolenberg

. An investigation of glass fiber/polypropylene interface strength and its effect of composite properties. Composites 1993; 25: 197–203.

Keusch

Haessler

. Influence of surface treatment of glass fibers on dynamic mechanical properties of epoxy resin composites. Composites Part A 2008; 30: 997–1002.

Gao

Jensen

. Effect of fiber surface texture created from silane blends on the strength and energy absorption of the glass fiber/epoxy interphase. J of Composite Materials 2008; 42: 513–534.

Mittal

. Influence of fiber length, fiber orientation, and interfacial adhesion on poly (butylene terephthalate)/polyethylene alloys reinforced with short glass fibers. Polymer Compos 2004; 26: 1–11.

Singh

Gupta

Verma

. Influence of fiber surface treatment on the properties of sisal-polyester composites. Polymer Compos 1996; 17: 910–918.

Nayak

Mohanty

Samal

. Influence of interfacial adhesion on the structural and mechanical behavior of PP-banana/glass hybrid composites. Polymer Compos 2010; 31: 1247–1257.

Blakley

Grady

O'Rear

. Effects of styrene-isoprene copolymer glass fiber coatings on woven glass cloth epoxy composite performance. Polymer Compos 2004; 25: 82–93.

10.

Cecen

Sarikanat

Yildiz

. Comparison of mechanical properties of epoxy composites reinforced with stitched glass and carbon fabrics: characterization of mechanical anisotropy in composites and investigation on the interaction between fiber and epoxy matrix. Polymer Compos 2008(29): 840–853.

11.

Suppakul

Bandyopadhyay

. The effect of weave pattern on the mode-I interlaminar fracture energy of E-glass/vinyl ester composites. Compos Sci Technol 2002; 62: 709–717.

12.

Reed

Darr

Schutz

. Shot-beam shear testing of candidate magnet insulators. Cryogenics 1992; 32(ICMC Suppl): 9–13.

13.

Reed

Evans

Fabian

. Development of a new resin system for the US ITER central solenoid modal coil. Adv Cryogenic Eng-Mater 2000; 46A: 227–234.

14.

Reed RP and McColskey JD. Composite struts for SMES plants, NISTIR 5024, National Institute of Standards and Technology, Boulder, Colorado, October, 1994.